Title: Estudo do fissuramento do vidrado de azulejos em serviço.
Other Titles: Study of cracking of glazed tiles in service.
???metadata.dc.creator???: CAVALCANTI, Maria do Socorro Lopes.
???metadata.dc.contributor.advisor1???: FERREIRA, Heber Carlos.
???metadata.dc.contributor.referee1???: KIYOHARA, Pedro Kunihiko.
???metadata.dc.contributor.referee2???: MACHADO, Edna Célie da Cunha.
Keywords: Fissuramento;Vidrado de Azulejos;Azulejos Cerâmicos - Problemas;Azulejos em Serviço;Argamassa;Tempo de Fixação;Cracking;Glazed Tiles;Ceramic Tiles - Problems;Tiles in Service;Grout;Fixture Time
Issue Date: May-1993
Publisher: Universidade Federal de Campina Grande
Citation: CAVALCANTI, Maria do Socorro Lopes. Estudo do fissuramento do vidrado de azulejos em serviço. 1993. 241f. (Dissertação de Mestrado em Engenharia Química), Curso de Mestrado em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba - Campus II Campina Grande - Brasil, 1993.
???metadata.dc.description.resumo???: Os azulejos cerâmicos, frequentemente apresentam a superfície vidrada fendilhada.Tentando evitar o problema, os azulejos apos sua fabricação são submetidos a ensaios de controle de qualidade pelas normas da ABNT (Associação Brasileira de Normas Técnicas). Tem-se observado que azulejos recém fabricados tem comportamento adequado durante o controle de qualidade , porem, quando em serviço, apresentam seu vidrado fendilhado. Objetivando adquirir maior conhecimento sobre esse problema, vem sendo estudados desde 1974 azulejos nacionais de diversos fabricantes. Em 1977 foram selecionadas amostras de azulejos pertinentes a dois fabricantes, fixados em forma de painéis com argamassa e argamassa mais adesivo, usando tracos e espessuras variadas; durante este período inúmeros dados de fissuramento , curvatura e falha na adesão foram coletados , sendo efetuado nesta etapa final da pesquisa um estudo global dos resultados obtidos ate o presente. Os estudos mostraram que o uso de adesivo orgânico reduziu o fissuramento no vidrado de azulejos em serviço; que o fissuramento no vidrado de azulejos apresentou certa interdependência entre curvatura, falha na adesão e evolução do tempo de fixação; que os painéis com argamassas de espessuras mais finas e tracos mais pobres, foram os que apresentaram melhor comportamento apos 14 anos em serviço.
Abstract: Frequently the ceramic tiles show a crazing glazed surface. Trying to avoid this problem, after fabrication, the tiles are submitted to some tests of quality control specified by ABNT. However, it has been observed that these tiles have a suitable behaviour during the quality control, but after to be fixed on the wall exhibit the development of crazing. Objecting to acquire a great knowledge over this problem, since 1974 have being studied national tiles from different manufactois. The tiles were fixed on the wall in form of panels with mortar and mortar with organic adhesive at various ratio and thickness. At 1977 were selected samples of fixed tiles and from then on several data of crazing, bending and adhesion failure have being collected. So, this research presents a general study based on the results obtained till now. The results show that the use of organic adhesive reduces crazing on the glazed surface of the tiles when in service, that the crazing of the glazed surface has a certain interdependence between bending, adhesion failure and evolution of time fixing, that the panels with less thickness mortar and weaker traces are the ones with best behaviour after 14 years fixing.
Keywords: Fissuramento
Vidrado de Azulejos
Azulejos Cerâmicos - Problemas
Azulejos em Serviço
Argamassa
Tempo de Fixação
Cracking
Glazed Tiles
Ceramic Tiles - Problems
Tiles in Service
Grout
Fixture Time
???metadata.dc.subject.cnpq???: Engenharia Química
URI: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10430
Appears in Collections:Mestrado em Engenharia Química

Files in This Item:
File Description SizeFormat 
MARIA DO SOCORRO LOPES CAVALCANTI -DISSERTAÇÃO PPGEQ 1993.pdf Maria do Socorro Lopes Cavalcanti - Dissertação PPGEQ 1993. 8.59 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.