Please use this identifier to cite or link to this item: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10923
Full metadata record
DC FieldValueLanguage
dc.creator.IDVIEIRA SEGUNDO, J. E. D.pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/1388540284365683pt_BR
dc.contributor.advisor1VILAR, Eudésio Oliveira.-
dc.contributor.advisor1IDVILAR, E. O.pt_BR
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/6363257813968241pt_BR
dc.contributor.referee1FARIAS NETO, Severino Rodrigues de.-
dc.contributor.referee2OLIVEIRA, Laércio Gomes de.-
dc.contributor.referee3TONHOLO, Josealdo.-
dc.description.resumoNeste trabalho aplicou-se a técnica de permeação eletroquímica à liga API 5L X80 com deposito de níquel ou paládio na superfície de detecção das amostras, em três espessuras diferentes: 0,04; 0,08 e 0,12 um. Para isso, utilizou-se uma célula com dois compartimentos, ambos preenchidos com NaOH 0,1M, separados apenas pela membrana metálica, que serviu como eletrodo de trabalho. A caracterização dos depósitos metálicos foi realizada através da técnica de voltametria cíclica antes e apos a etapa de permeação. Os resultados obtidos mostraram que a superfície da liga com camadas de Ni e Pd tornaram-se mais ativas depois da permeação por hidrogênio. Os resultados da permeação foram expressos através das seguintes propriedades: coeficiente de difusão, permeabilidade e solubilidade. O coeficiente médio de difusão para as amostras com deposito de níquel foi de (2,92 ± 1,06) m2/s, enquanto que para as amostras com deposito de paládio foi de (2,46 ± 0,61) m2/s. Observou-se que o paládio apresenta uma melhor ação eletrocatalítica, alem de medições mais reprodutíveis e menor desvio padrão. As propriedades de interação mostraram-se independentes da espessura do deposito. No caso do níquel, essas propriedades apresentaram uma maior variação e indicaram certa dependência em relação a espessura da camada do metal eletrodepositado.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro de Ciências e Tecnologia - CCTpt_BR
dc.publisher.programPÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICApt_BR
dc.publisher.initialsUFCGpt_BR
dc.subject.cnpqEngenharia Química-
dc.titleEstudo da influência dos depósitos de níquel e paládio sobre a densidade de corrente de oxidação do hidrogênio na liga API 5L X80.pt_BR
dc.date.issued2010-09-27-
dc.description.abstractIn this work, electrochemical permeation technique was applied to alloy API 5L X80 coated with nickel or palladium on the sample detection surface in three different thickness: 0,04; 0,08 and 0,12 um. For this, a two-compartment cell was used, both filled with 0,1 M NaOH, separated only by the metallic membrane, acting as working electrode. The metallic coating characterization was performed by cyclic voltammetry technique before and after the permeation step. Results obtained showed that alloy surface with Ni and Pd layers became more active after hydrogen permeation. Permeation results were expressed by following properties: diffusion coefficient, permeability and solubility. The average diffusion coefficient for samples with nickel deposit was (2,92 ± 1,06) m2/s, while for the samples with palladium deposit was (2,46 ± 0,61) m2/s. It was noticed that palladium shows a better electro catalytic performance besides more reproducible measurements and minor standard deviation. Interaction properties showed no dependence of coating thickness. Regarding nickel, these properties presented larger fluctuation and denoted some dependence for layer metallic coating.pt_BR
dc.identifier.urihttp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10923-
dc.date.accessioned2020-01-14T12:59:43Z-
dc.date.available2020-01-14-
dc.date.available2020-01-14T12:59:43Z-
dc.typeDissertaçãopt_BR
dc.subjectNíquel e Paládio - Depósitos - Influência-
dc.subjectDensidade de Corrente-
dc.subjectOxidação do Hidrogênio-
dc.subjectLiga API 5L X80-
dc.subjectPermeação Eletroquímica-
dc.subjectSólidos Cristalinos - Difusão-
dc.subjectFragilização por Hidrogênio-
dc.subjectNickel and Palladium - Deposits - Influence-
dc.subjectCurrent Density-
dc.subjectHydrogen Oxidation-
dc.subjectAPI 5L X80 Alloy-
dc.subjectElectrochemical Permeation-
dc.subjectCrystalline Solids - Diffusion-
dc.subjectHydrogen Embrittlement-
dc.rightsAcesso Abertopt_BR
dc.creatorVIEIRA SEGUNDO, José Etimógenes Duarte.-
dc.publisherUniversidade Federal de Campina Grandept_BR
dc.languageporpt_BR
dc.title.alternativeStudy of the influence of nickel and palladium deposits on the oxidation current density of hydrogen in the API 5L X80 alloy.pt_BR
dc.identifier.citationVIEIRA SEGUNDO, José Etimógenes Duarte. Estudo da influência dos depósitos de níquel e paládio sobre a densidade de corrente de oxidação do hidrogênio na liga API 5L X80. 2010. 82f. (Dissertação de Mestrado em Engenharia Química), Programa de Pós-graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2010. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10923pt_BR
Appears in Collections:Mestrado em Engenharia Química

Files in This Item:
File Description SizeFormat 
JOSÉ ETIMÓGENES DUARTE VIEIRA SEGUNDO - DISSERTAÇÃO PPGEQ CCT 2010.pdfJosé Etimógenes Duarte Vieira Segundo - Dissertação PPGEQ CCT 2010.6.83 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.