http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11413| Title: | Efeito da direção e da espessura na taxa de propagação de trinca por fadiga de alto ciclo nos aços da classe API 5L-X70 e ASTM A516-GR65. |
| Other Titles: | Effect of direction and thickness on the crack propagation rate by high cycle fatigue in API 5L-X70 and ASTM A516-GR65 class steels. |
| ???metadata.dc.creator???: | FARIAS, Marconi Andrade. |
| ???metadata.dc.contributor.advisor1???: | SANTOS, Marco Antônio dos. |
| ???metadata.dc.contributor.referee1???: | STROHAECKER, Telmo Roberto. |
| ???metadata.dc.contributor.referee2???: | MACIEL, Theóphilo Moura. |
| Keywords: | Defeito-trinca-fadiga;Defecto-crack-fatiga;Defect-crack-fatigue;Aço API5L-X70;API5L-X70 steel;Acero API5L-X70;Aço ASTM A516-GR65;Acero ASTM A516-GR65;ASTM A516-GR65 steel;Propagação de trinca;Crack propagation;Propagación de grietas |
| Issue Date: | 15-Sep-1994 |
| Publisher: | Universidade Federal de Campina Grande |
| Citation: | FARIAS, Marconi Andrade. Efeito da direção e da espessura na taxa de propagação de trinca por fadiga de alto ciclo nos aços da classe API 5L-X70 e ASTM A516-GR65. 201f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 1994. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11413 |
| ???metadata.dc.description.resumo???: | Neste trabalho foi estudada a influência da espessura e da direção de orientação da trinca ( "TL" e "SL" ), no comportamento a fadiga dos aços das classes API 5L-X70 e ASTM A516-GR65. Os ensaios foram realizados a temperatura ambiente em corpos de prova do tipo Tração Compacta ("Compact Tension"). A propagação da trinca de fadiga foi acompanhada pelo método visual com um microscópio de deslocamento ("Travel Microscope"). Para os dois aços estudados, quando a trinca se propaga na direção longitudinal em um piano paralelo ao de laminação da chapa ("SL"), a espessura do corpo de prova tende a afetar a taxa de propagação da trinca de fadiga. O comportamento a fadiga do dois aços foi comparado e as diferenças discutidas. |
| Abstract: | In This work the effect of thickness and crack orientation ("TL" and "SL") on fatigue behaviour of steels class API 5L-X70 and ASTM A516-GR65 was investigated. The tests were conducted at ambient temperature and compact tension tests specimens was used. Fatigue crack propagation was attended with a travell microscope. When the crack propagate in the longitudinal direction in a parallel plane to lamination plane of the plate ("SL"), the test specimen thickness tend to effect the fatigue crack propagation. Fatigue behaviour of the steels was confronted and the differences discussed. |
| Keywords: | Defeito-trinca-fadiga Defecto-crack-fatiga Defect-crack-fatigue Aço API5L-X70 API5L-X70 steel Acero API5L-X70 Aço ASTM A516-GR65 Acero ASTM A516-GR65 ASTM A516-GR65 steel Propagação de trinca Crack propagation Propagación de grietas |
| ???metadata.dc.subject.cnpq???: | Engenharia Mecânica |
| URI: | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11413 |
| Appears in Collections: | Mestrado em Engenharia Mecânica. |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| MARCONI ANDRADE FARIAS - DISSERTAÇÃO PPGEM 1994.pdf | Marconi Andrade Farias - Dissertação PPGEM 1994 | 7.14 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.