1. Biblioteca Digital de Teses e Dissertações da UFCG
  2. Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
  3. PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
  4. Mestrado em Ciência e Engenharia de Materiais.
Please use this identifier to cite or link to this item: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11430
Full metadata record
DC FieldValueLanguage
dc.creator.IDMARQUES, L. N.pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/3754473953019217pt_BR
dc.contributor.advisor1MACIEL, Theophilo Moura.-
dc.contributor.advisor1IDMACIEL, T. M.pt_BR
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/9476858938351846pt_BR
dc.contributor.referee1SANTOS, Marco Antonio dos.-
dc.contributor.referee2ALMEIDA, Daisy Martins de.-
dc.contributor.referee3CASTRO, Walman Benicio de.-
dc.description.resumoNeste trabalho foi avaliada a influencia dos parâmetros, processos e procedimentos de soldagem sobre a susceptibilidade a trincas a frio induzidas pelo hidrogênio (TIH) em juntas soldadas do ago API 5L X80. Para isto foram realizados ensaios de implante em soldagens executadas pelos processos SMAW e FCAW com diferentes parâmetros e procedimentos de soldagem. Os consumíveis utilizados foram o arame autoprotegido AWS E 91T8-K8 com 1,60 mm de diâmetro e com proteção gasosa (75% Ar -25%CO-,) AWS E 91T1-G com diâmetro de 1,20 mm. E os eletrodos AWS E 8010 e AWS E 8018-G, com diâmetro de 4,00 mm. Apos as soldagens os corpos de prova foram cortados transversalmente e as trincas e microtrincas, quando existentes, foram identificadas, para cada condição de soldagem sendo os resultados associados a microestrutura e ao valor de microdureza na região onde ocorreu trincamento. A microestrutura predominante foi composta por Bainita e Ferrita Primaria e todas as trincas encontradas foram de característica intergranular, entretanto não representaram um numero significativo, os como os valores de microdureza, foram todos abaixo de 238,1 HV, tanto no metal de solda como na ZTA e possível dizer que o ago estudado apresenta boa soldabilidade e não e susceptível ao TIH para as condições analisadas.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro de Ciências e Tecnologia - CCTpt_BR
dc.publisher.programPÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAISpt_BR
dc.publisher.initialsUFCGpt_BR
dc.subject.cnpqCiência e Engenharia de Materiais.-
dc.titleAvaliação da susceptibilidade a trincas a frio induzidas por hidrogênio em juntas soldadas dos aços API 5L X-80 por meio do teste de implante.pt_BR
dc.date.issued2013-02-27-
dc.description.abstractIn this study, the influence of the parameters, process and welding procedures on susceptibility to hydrogen induced cold cracking in API 5L X80 steel welded joints . Were evaluated for this Implant Test using SMAW and FCAW process with different parameters and welding procedures. Were used AWS E 91T8-K8 with 1,60 mm diameter self protected and AWS E 91T1-G with 1,20 mm diameter gas protected . And AWS E 8010 e AWS E 8018-G, with diameter 4,00 mm. After welding the specimens were cut and cracks and microcracks were identified for each welding condition and the results associated with the microstructure and microhardness value in the region where cracking occurred. It was verified that all cracks occurred were predominantly composed of Bainite and Primary Ferrite All cracks were intergranular but do not represented a significant size, as all the microhardness values were less than 238,1 HV it is possible to say that the steel studied has a good weldability and it is not likely to be susceptible to hydrogen induced cold cracking for the analyzed conditionspt_BR
dc.identifier.urihttp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11430-
dc.date.accessioned2020-02-03T11:50:33Z-
dc.date.available2020-02-03-
dc.date.available2020-02-03T11:50:33Z-
dc.typeDissertaçãopt_BR
dc.subjectSoldagem-
dc.subjectAço API 5L X80-
dc.subjectTrincamento Induzido por Hidrogênio-
dc.subjectTeste de Implante-
dc.subjectProcessos SMAW e FCAW-
dc.subjectTrincas-
dc.subjectWelding-
dc.subjectAPI 5L X80 Steel-
dc.subjectHydrogen-Induced Cracking-
dc.subjectImplant Test-
dc.subjectSMAW and FCAW Processes-
dc.subjectCracks-
dc.rightsAcesso Abertopt_BR
dc.creatorMARQUES, Lívia Neves.-
dc.publisherUniversidade Federal de Campina Grandept_BR
dc.languageporpt_BR
dc.title.alternativeEvaluation of susceptibility to cold cracks induced by hydrogen in welded joints of API 5L X-80 steels using the implant test.pt_BR
dc.identifier.citationMARQUES, Lívia Neves. Avaliação da susceptibilidade a trincas a frio induzidas por hidrogênio em juntas soldadas dos aços API 5L X-80 por meio do teste de implante. 2013. 97 f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11430pt_BR
Appears in Collections:Mestrado em Ciência e Engenharia de Materiais.

Files in This Item:
File Description SizeFormat 
LÍVIA NEVES MARQUES - DISSERTAÇÃO PPG-CEMat CCT 2013.pdfLívia Neves Marques - Dissertação PPG-CEMat CCT 2013. 10.06 MBAdobe PDFView/Open
Show simple item record


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.