Title: Resistência à propagação de trinca de fadiga em ferros fundidos nodulares austemperados.
Other Titles: Resistance to fatigue crack propagation in austempered nodular cast iron.
???metadata.dc.creator???: BARBOZA, José do Nascimento.
???metadata.dc.contributor.advisor1???: SANTOS, Marco Antônio dos.
???metadata.dc.contributor.referee1???: BASTIAN, Fernando Luiz.
???metadata.dc.contributor.referee2???: LIMA, Aarão Andrade de.
???metadata.dc.contributor.referee3???: MACIEL, Theóphilo Moura.
Keywords: Ferro Fundido;Ferros Fundidos Nodulares Austemperados;Ferros Fundidos - Trinca de Fadiga;Propagação da Trinca de Fadiga;Características Microestruturais;Ferro Fundido Nodular Ligado e Não Ligado;Cast Iron;Austempered Nodular Cast Irons;Cast Irons - Trinca de Fadiga;Propagation of Fatigue Crack;Microstructural Characteristics;Bonded and Unalloyed Nodular Cast Iron
Issue Date: 13-Oct-1999
Publisher: Universidade Federal de Campina Grande
Citation: BARBOZA, José do Nascimento. Resistência à propagação de trinca de fadiga em ferros fundidos nodulares austemperados. 189f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 1999.
???metadata.dc.description.resumo???: Os ferros fundidos austemperados tem despertado um grande interesse. A possibilidade de uma excelente combinação de dureza e resistência a fadiga torna este material muito atrativo. Neste trabalho determinou-se a resistência a propagação da trinca de fadiga de dois ferros fundidos austemperados: um ferro nodular ligado ao molibdênio (0,2% Mo) e outro não ligado. Ambos os ferros fundidos austemperados foram inoculados com 0,5; 0,7 e 0,9% de FeSi75A. Os ensaios de fadiga foram realizados a temperatura ambiente e em uma máquina de ensaios servo-hidráulica MTS 810, sob controle de carga. A razão de carga, R, foi mantida constante e igual a 0,10. Os resultados obtidos mostraram que o ferro fundido nao ligado austemperado, em geral e independente do teor de FeSi75A, apresentou sempre maior resistência ao crescimento de trinca de fadiga. Este comportamento foi explicado com base no efeito do silício, presente no inoculante, sobre as características da microestrutura da matriz ausferrítica. As superfícies de fratura apresentaram um mecanismo de fratura misto, com facetas planas de fratura, semelhante a clivagem, dentro das quais foram observadas linhas paralelas e regulares.
Abstract: Austempered ductile cast irons have waked to a great interest. The possibility of an excellent combination of toughness and fatigue strength .makes this material very attractive. In this work the fatigue crack growth resistance of two austempered ductile cast irons was determined: molybdenum alloyed nodular cast iron (0.2% Mo) and another unalloyed iron. Both austempered ductile cast irons were inoculate with 0.5, 0.7 and 0.9% FeSi75A. The fatigue tests were carried in room temperature, ambient atmosphere and in a servohydraulic Material Test System (MTS 810) test machine under load control mode. The load ratio, R, was kept constant at 0.10. The results obtained showed that the unalloyed austempered ductile cast iron, for all situations and independent of FeSi75A content, always presented the most fatigue crack growth resistance. This behavior was explained with basis in the silicon effect, present within inoculante, on the microstructure characteristics to the ausferritic matrix. The fracture surfaces presented a mixed mechanism fracture with a flat fracture, cleavage-like regions within which regular parallel arrest lines were observed.
Keywords: Ferro Fundido
Ferros Fundidos Nodulares Austemperados
Ferros Fundidos - Trinca de Fadiga
Propagação da Trinca de Fadiga
Características Microestruturais
Ferro Fundido Nodular Ligado e Não Ligado
Cast Iron
Austempered Nodular Cast Irons
Cast Irons - Trinca de Fadiga
Propagation of Fatigue Crack
Microstructural Characteristics
Bonded and Unalloyed Nodular Cast Iron
URI: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11466
Appears in Collections:Mestrado em Engenharia Mecânica.

Files in This Item:
File Description SizeFormat 
JOSÉ DO NASCIMENTO BARBOZA - DISSERTAÇÃO PPGEM 1999.pdfJosé do Nascimento Barboza - Dissertação PPGEM 1999.28.74 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.