Title: Estudo do comportamento da eletrodeposição da liga ni-p-w utilizando glicina como complexante.
Other Titles: Study of the behavior of Ni-P-W alloy electrolytes using glycine as a complemente.
Estudio del comportamiento de la electrodeposición de la aleación ni-p-w utilizando glicina como agente complejante.
???metadata.dc.creator???: LINS, Mislene Pereira.
???metadata.dc.contributor.advisor1???: PRASAD, Shiva.
???metadata.dc.contributor.advisor2???: SANTANA, Renato Alexandre Costa de.
???metadata.dc.contributor.referee1???: CAMPOS, Ana Regina Nascimento.
???metadata.dc.contributor.referee2???: ALVES, José Jailson Nicacio.
Keywords: Eletrodeposição;Ligas metálicas;Ni-P-W;Glicina;Electrodeposición;Aleaciones metálicas;Ni-p-w;Glicina
Issue Date: 16-Apr-2015
Publisher: Universidade Federal de Campina Grande
Citation: LINS, Mislene Pereira. .Estudo do comportamento da eletrodeposição da liga ni-p-w utilizando glicina como complexante 2015. 71f. Dissertação (Mestrado em Ciências Naturais e Biotecnologia) – Programa de Pós-Graduação em Ciências Naturais e Biotecnologia PPGCNBiotec, Centro de Educação e Saúde, Universidade Federal Campina Grande - Cuité - Paraíba - Brasil, 2015.
???metadata.dc.description.resumo???: A eletrodeposição de um simples metal ou de suas ligas é atualmente de grande importância nas diversas áreas de engenharia e tecnologia. Dessa forma, as técnicas eletroquímicas para obtenção de revestimentos pelo processo de eletrodeposição são amplamente estudadas. Pelo processo de eletrodeposição podem ser obtidos filmes finos de óxidos metálicos com propriedades bem específicas para determinado uso. Através da utilização de métodos eletroquímicos é possível avaliar o comportamento relacionado a corrosão de um metal ou sua liga. Neste trabalho investigou-se os parâmetros operacionais para eletrodeposição da liga Ni-PW utilizando-se glicina como agente complexante. Para este estudo realizou-se um planejamento experimental 23, com composto central. As variáveis estudadas foram densidade de corrente, pH do banho eletrolítico e temperatura do banho. A liga Ni-P-W foi depositada sobre substrato de cobre de área superficial total de 8 cm2. A composição da liga foi obtida por meio da utilização de energia dispersiva de raios-X. A morfologia foi obtida por meio de microscopia eletronica de varredura. Foi feito medidas de difratometria de raios-X e de microdureza Vickers. No estudo de corrosão foram utilizadas as medidas de polarização potenciodinâmico linear realizados em NaCl 3,5%. As análise de composição química mostraram que as ligas obtidas apresentaram elevadas porcentagens de Ni e P e traços de W. As análises de morfologia das ligas obtidas mostram revestimentos com superfície homogênea e morfologia nodular bem definida para depósitos com maior porcentagem de P. Ligas com uma menor porcentagem de P apresentaram nódulos de tamanhos variados, e uma elevada quantidade de trincas. Os depósitos obtidos apresentaram comportamento amorfo. Os ensaios de corrosão mostraram que os revestimento obtido com densidade de corrente de 70 mA/cm2, pH 6,5 e temperatura de 63,5 oC apresentou os melhores resultados para resistência a polarização e corrente de corrosão.
Abstract: The electrodeposition of a simple metal or alloy is currently of great importance in many areas of engineering and technology. Thus, electrochemical techniques to obtain coatings by electrodeposition process are widely studied. By electrodeposition process there can be obtained thin films of metal oxides with very specific properties for specific use. Through the use of electrochemical methods it is possible to evaluate the corrosion related behavior of a metal or its alloy. In this study we investigated the operating parameters of Ni-P-W alloy plating using glycine as a complexing agent. For this study was made an experimental design 23 with central composite variables studied were current density, the electrolytic bath pH and bath temperature. The Ni-P-W alloy was deposited on copper substrate of total surface area 8 cm2. The composition of the alloy was obtained by using energy dispersive X-ray (EDX). The morphology of the Ni-PW electroplated alloy was obtained by Scanning Electronic Microscopy (SEM). Measurements of X-ray diffraction and Vickers microhardness were made. The linear potentiodynamic polarization (LPP) corrosion measurements were carried out in NaCl 3.5% in the study of corrosion. Chemical composition analysis showed that the obtained alloys showed high percentages of Ni and P and low of W. The analysis of the obtained alloys shows coatings with homogeneous surface and well defined nodular morphology for deposits with the highest percentage of P. Alloys with a lower percentage of P showed varying sizes of nodules, and a high percentage of cracks. The deposits obtained showed amorphous behavior. The corrosion tests showed that the coating obtained with current density 70 m/cm2, pH 6.5 and temperature of 63.5 °C showed the best results for the polarization resistance and corrosion current.
???metadata.dc.description.resumen???: La electrodeposición de un solo metal o sus aleaciones es de gran importancia en la actualidad en diversas áreas de la ingeniería y la tecnología. Así, las técnicas electroquímicas para la obtención de recubrimientos por el proceso de electrodeposición son ampliamente estudiadas. Mediante el proceso de electrodeposición se pueden obtener películas delgadas de óxidos metálicos con propiedades muy específicas para un uso determinado. Mediante el uso de métodos electroquímicos es posible evaluar el comportamiento relacionado con la corrosión de un metal o su aleación. En este trabajo investigamos los parámetros operativos para la electrodeposición de aleación Ni-PW utilizando glicina como agente complejante. Para este estudio se realizó un diseño experimental 23, con un compuesto central. Las variables estudiadas fueron densidad de corriente, pH del baño electrolítico y temperatura del baño. La aleación Ni-P-W se depositó sobre un sustrato de cobre con una superficie total de 8 cm2. La composición de la aleación se obtuvo utilizando rayos X de energía dispersiva. La morfología se obtuvo mediante microscopía electrónica de barrido. Se realizaron mediciones de difractometría de rayos X y microdureza Vickers. En el estudio de corrosión se utilizaron medidas de polarización potenciodinámica lineal realizadas en NaCl al 3,5%. El análisis de composición química mostró que las aleaciones obtenidas presentaban altos porcentajes de Ni y P y trazas de W. Los análisis morfológicos de las aleaciones obtenidas muestran recubrimientos con superficie homogénea y morfología nodular bien definida para depósitos con mayor porcentaje de P. Aleaciones con un menor porcentaje de P mostró nódulos de diferentes tamaños y una gran cantidad de grietas. Los depósitos obtenidos mostraron un comportamiento amorfo. Las pruebas de corrosión mostraron que el recubrimiento obtenido con densidad de corriente de 70 mA/cm2, pH 6,5 y temperatura de 63,5 oC presentó los mejores resultados para la resistencia a la corriente de polarización y corrosión.
Keywords: Eletrodeposição
Ligas metálicas
Ni-P-W
Glicina
Electrodeposición
Aleaciones metálicas
Ni-p-w
Glicina
???metadata.dc.subject.cnpq???: Engenharia e tecnologia
URI: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/1273
Appears in Collections:Mestrado em Ciências Naturais e Biotecnologia - Dissertações 001

Files in This Item:
File Description SizeFormat 
MISLENE PEREIRA LINS - DISSERTAÇÃO PPGCNBio CES 2015.pdfMislene Pereira Lins - Dissertação PPGCNBio CES 20155.62 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.