http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/14210| Title: | Estudo da liga Ni-Co-Fe na presença do complexante citrato de sódio. |
| Other Titles: | Study of the Ni-Co-Fe alloy in the presence of the sodium citrate complexing agent. Estudo da liga Ni-Co-Fe na presença do complexante citrato de sódio. |
| ???metadata.dc.creator???: | RAULINO, José Leonardo Costa. |
| ???metadata.dc.contributor.advisor1???: | SANTANA, Renato Alexandre Costa de. |
| ???metadata.dc.contributor.referee1???: | BARBOSA, Wellington Antonio. |
| ???metadata.dc.contributor.referee2???: | SILVA, Paulo Sergio Gomes da. |
| Keywords: | Ligas Ni-Co-Fe;Eletrodeposição;Corrosão;Metodologia de superfície de resposta;Ni-Co-Fe alloys;Electrodeposition;Corrosion;And Response Surface Methodology;Electrodeposición;Corrosión;Metodología de superfície de respuesta |
| Issue Date: | 23-Jul-2014 |
| Publisher: | Universidade Federal de Campina Grande |
| Citation: | RAULINO, José Leonardo Costa. Estudo da liga Ni-Co-Fe na presença do complexante citrato de sódio. 2014. 46 fl. (Trabalho de Conclusão de Curso – Monografia), Curso de Licenciatura em química, Centro de Educação e Saúde, Universidade Federal de Campina Grande, Cuité – Paraíba – Brasil, 2014. |
| ???metadata.dc.description.resumo???: | A liga ternaria de Ni-Co-Fe foi eletrodepositada e otimizada em parâmetros operacionais de composição do banho em relação a sua resistência a corrosão. O desenvolvimento de banhos estáveis com níveis de pH relativamente elevados e a utilização de agentes complexantes para estabilizar e crucial para obtenção de filmes de boa qualidade e para aumentar o tempo de vida do banho eletrolítico. O efeito da densidade de corrente e agitação mecânica para se obter Ni-Co-Fe, na presença de um agente complexante citrato de sódio em diferentes pH tem sido estudada no presente trabalho. A metodologia de superfície de resposta foi usada como ferramenta de otimização. Os banhos utilizados para a obtenção destas ligas sem agentes complexantes eram instáveis. Películas ou revestimentos de boa qualidade das ligas de Ni- Co-Fe foram obtidas utilizando um banho eletroquímico com o agente complexante. Os revestimentos obtidos tiveram adesão e bom brilho. As ótimas condições de operação para a obtenção deste filme foram densidade de corrente de 30 mA/cm2 e pH 8,5. Foi observada a presença de micro nódulos na superfície das ligas estudadas, a composição química do melhor revestimento foi Ni73,9Coio,2Fei59, e apresentou ainda um comportamento cristalino e uma eficiência catódica de 85%. |
| Abstract: | A ternary alloy Ni-Co-Fe was electrodeposited and operational and bath composition parameters in relation to its corrosion resistance were optimized. The development of stable baths with relatively high pH levels and the use of complexing agent to stabilize it is crucial for getting good quality films and for increasing the lifetime of the electrolytic bath. The effect of current density and mechanical agitation to obtain Ni-Co-Fe in the presence of a complexing agent and at a controlled high pH has been studied in this work. The response surface methodology was used as optimization tool. The baths used to obtain these alloys without complexing agents were unstable. Good quality films of Ni-Co-Fe alloys were obtained by using an electrochemical bath with the complexing agent. The coatings obtained had good adhesion and gloss. The excelent operating conditions for obtaining this film were current density of 30 mA / cm2 and pH 8.5. It was observed the presence of micro-nodules on the surface of the alloys studied, the chemical composition of the coating was better Ni739Coio,2Fei5;9 and also showed a crystalline behavior and a cathodic efficiency of 85%. |
| ???metadata.dc.description.resumen???: | La aleación ternaria de Ni-Co-Fe fue electrodepositada y optimizada en parámetros operativos de composición del baño en relación a su resistencia a la corrosión. El desarrollo de baños estables con niveles de pH relativamente altos y el uso de agentes complejantes para estabilizarlos es crucial para obtener películas de buena calidad y aumentar la vida útil del baño electrolítico. En el presente trabajo se ha estudiado el efecto de la densidad de corriente y la agitación mecánica para obtener Ni-Co-Fe en presencia de un agente complejante citrato de sodio a diferentes pH. Se utilizó la metodología de superficie de respuesta como herramienta de optimización. Los baños utilizados para obtener estas aleaciones sin agentes complejantes eran inestables. Se obtuvieron películas o recubrimientos de aleaciones de Ni-Co-Fe de buena calidad utilizando un baño electroquímico con el agente complejante. Los recubrimientos obtenidos tenían adherencia y buen brillo. Las condiciones óptimas de operación para la obtención de esta película fueron una densidad de corriente de 30 mA/cm2 y un pH de 8,5. Se observó la presencia de micronódulos en la superficie de las aleaciones estudiadas, la composición química del mejor recubrimiento fue Ni73,9Coio,2Fei59, además presentó un comportamiento cristalino y una eficiencia catódica del 85%. |
| Keywords: | Ligas Ni-Co-Fe Eletrodeposição Corrosão Metodologia de superfície de resposta Ni-Co-Fe alloys Electrodeposition Corrosion And Response Surface Methodology Electrodeposición Corrosión Metodología de superfície de respuesta |
| ???metadata.dc.subject.cnpq???: | Química |
| URI: | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/14210 |
| Appears in Collections: | Curso de Licenciatura em Química - CES - Monografias |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| JOSÉ LEONARDO COSTA RAULINO - TCC LICENCIATURA EM QUÍMICA 2014.pdf | José Leonardo Costa Raulino - TCC Licenciatura em Química CES 2014 | 6.51 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.