Please use this identifier to cite or link to this item: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/15168
Full metadata record
DC FieldValueLanguage
dc.creator.IDSANTOS, K. C. V.pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/7784021431972104pt_BR
dc.contributor.advisor1SANTANA, Lisiane Navarro de Lima.-
dc.contributor.advisor1IDSANTANA, L. N. L.pt_BR
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/4057799848801141pt_BR
dc.contributor.advisor2LIRA, Hélio de Lucena.-
dc.contributor.advisor2IDLIRA, H. L.pt_BR
dc.contributor.advisor2Latteshttp://lattes.cnpq.br/5548799845411781pt_BR
dc.contributor.referee1MACEDO, Reginaldo Severo de.-
dc.contributor.referee2SILVA, Valmir José da.-
dc.description.resumoA mulita é um mineral extremamente importante para aplicações no campo da cerâmica devido as suas excelentes propriedades físicas, químicas, térmicas e mecânicas. Como este material é raro na natureza, diversos estudos enfocam a síntese do mesmo através de processos que sejam economicamente viáveis. Um dos métodos mais utilizados para obtenção de mulita consiste no aquecimento em altas temperaturas de composições contendo sílica e alumina, alguns aluminossilicatos são muito utilizados para este fim. O caulim é um dos materiais mais importantes na industria cerâmica tradicional, devido seu custo relativamente baixo, facil obtenção além de ser relativamente puro. Quando o caulim é submetido a tratamentos térmicos ocorrem transformações microestruturais, dentre estas a formação de mulita. Este estudo tem por objetivo obter mulita a partir de composições contendo caulim e alumina e avaliar a influência de diferentes tamanhos de partículas da alumina sobre os cristais de mulita. Inicialmente, os precursores foram submetidos à caracterização química, granulométrica e mineralógica. A alumina passou por um processo de moagem durante 15, 45 e 60 minutos. A partir das composições formuladas, as massas cerâmicas foram prensadas e os corpos de prova sinterizados nas temperaturas de 1200, 1300 e 1400°C, com taxa de aquecimento de 5°C/min e tempo de permanência na temperatura máxima durante 60 minutos. Posteriormente, os corpos de prova foram submetidos às caracterizações físico-mecânicas como: retração linear, resistência mecânica a flexão, absorção de água, porosidade e densidade aparentes. Os melhores resultados foram observados para a massa cerâmica contendo caulim e a alumina submetida a moagem durante 45 minutos. Os resultados comprovaram a influência da área superficial sobre a cinética das reações, enfatizando também, a distribuição granulométrica mais larga das partículas.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro de Ciências e Tecnologia - CCTpt_BR
dc.publisher.programPÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAISpt_BR
dc.publisher.initialsUFCGpt_BR
dc.subject.cnpqEngenharia de Materiais e Metalúrgicapt_BR
dc.titleSíntese de mulita a partir de caulim e alumina.pt_BR
dc.date.issued2016-08-31-
dc.description.abstractThe mullite is an extremely important mineral for the field of ceramic applications due to its excellent physical, chemical, thermal and mechanical. As this material is rare in nature, many studies focus on the synthesis of the same through processes that are economically viable. One of the methods used for obtaining mullite consists in heating at high temperatures mixing sources of silica with alumina, some aluminosilicates are often used for this purpose. Kaolin is one of the most important materials in the traditional ceramic industry because of its relatively low cost, easy to obtain as well as being relatively pure. When kaolin is subjected to heat treatment occur microstructural changes, among them the formation of mullite. This study aims to obtain mullite from compositions containing kaolin and alumina and evaluate the influence of different particle sizes of alumina on the mullite crystals. Initially the precursors were subjected to chemical characterization, particle size and mineralogical. The alumina passed through a milling process for 15, 45 and 60 minutes. After formulation of the masses, these were pressed and sintered at temperatures of 1200, 1300 and 1400 ° C with a heating rate of 5 ° C / min time 60 minutes residence. Subsequently, the samples were subjected to physical and mechanical characterizations: linear shrinkage, apparent porosity, water absorption and apparent density. The best results were observed for the composition containing kaolin and alumina subjected to milling for 45 minutes. The results show the influence of surface area on the kinetics of reactions, also emphasizing the granulometric distribution of the larger particles.pt_BR
dc.identifier.urihttp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/15168-
dc.date.accessioned2020-09-11T16:48:44Z-
dc.date.available2020-09-11-
dc.date.available2020-09-11T16:48:44Z-
dc.typeDissertaçãopt_BR
dc.subjectCaulimpt_BR
dc.subjectKaolinpt_BR
dc.subjectCaolínpt_BR
dc.subjectAluminapt_BR
dc.subjectGranulometriapt_BR
dc.subjectGranulometrypt_BR
dc.subjectMulitapt_BR
dc.subjectMullitapt_BR
dc.subjectMullitept_BR
dc.subjectTaxa de aquecimentopt_BR
dc.subjectHeating ratept_BR
dc.subjectVelocidad de calentamientopt_BR
dc.rightsAcesso Abertopt_BR
dc.creatorSANTOS, Kirlyanne Christinne Vital.-
dc.publisherUniversidade Federal de Campina Grandept_BR
dc.languageporpt_BR
dc.title.alternativeSynthesis of mullite from kaolin and alumina.pt_BR
dc.description.sponsorshipCapespt_BR
dc.identifier.citationSANTOS, K. C. V. Síntese de mulita a partir de caulim e alumina. 2016. 54 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2016. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/15168pt_BR
Appears in Collections:Mestrado em Ciência e Engenharia de Materiais.

Files in This Item:
File Description SizeFormat 
KIRLYANNE CHRISTINNE VITAL SANTOS - DISSERTAÇÃO PPG-CEMat CCT 2016.pdfKirlyanne Christinne Vital Santos - Dissertação PPG-CEMat CCT 20161.09 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.