Please use this identifier to cite or link to this item: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/16038
Full metadata record
DC FieldValueLanguage
dc.creator.IDRAMOS, S. O.pt_BR
dc.creator.IDRAMOS, SILEIDE DE OLIVEIRApt_BR
dc.creator.Latteshttp://lattes.cnpq.br/2948315992571892pt_BR
dc.contributor.advisor1LIRA, Hélio de Lucena.-
dc.contributor.advisor1IDLIRA, Hélio de Lucenapt_BR
dc.contributor.advisor1IDLira, Hélio L.pt_BR
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/5548799845411781pt_BR
dc.contributor.referee1MACEDO, Reginaldo Severo de.-
dc.contributor.referee2SOUZA, Josilene de.-
dc.contributor.referee3BEZERRA, Danielle Cibele.-
dc.contributor.referee4BONIFÁCIO, Maria Aparecida Ribeiro.-
dc.description.resumoCerâmicas porosas são materiais sólidos que tem uma combinação de uma estrutura continua e uma rede de poros abertos interligados que podem ou não serem permeados por um líquido ou gás. Embora diversas pesquisas sobre cerâmica porosa tenham sido realizadas, verifica-se que os resultados ainda são escassos para a aplicação desses materiais na construção civil com o intuito de melhorar propriedades acústicas e térmicas ao mesmo tempo. Dentre as pesquisas realizadas, várias utilizaram cerâmicas porosas, tais como: alumina, zircônia, mulita e cordierita e biocerâmicas. O objetivo deste estudo foi produzir massas cerâmicas a partir da mistura argilas, água, amido ou gelatina, destinada à produção de blocos cerâmicos porosos, utilizando secagem por congelamento. As matérias-primas foram beneficiadas e, em seguida, caracterizadas por fluorescência de raios X (análise química), difração de raios-X (análise mineralógica), análise granulométrica e análise termogravimértica (TG/ATD). Posteriormente, foram preparadas massas cerâmicas com os diferentes tipos de argilas, e as respectivas quantidades de aditivos (água, amido ou gelatina), nas quantidades pré-determinadas. A partir destas massas, foram confeccionados corpos de prova, os quais foram submetidos a tratamento térmico na temperatura de 1100°C com taxa de aquecimento de 5°C/min. Após este procedimento, os produtos obtidos foram caracterizados por Difração de Raios-X, microscopia eletrônica de varredura (MEV) e análise das propriedades físicomecânicas. A partir dos resultados de difração de raios-X foi possível observar nas amostras após tratamento térmico a presença de picos de hematita, cristobalita, espinélio e os primeiros picos de mulita. Pelas imagens de MEV foi revelado que a adição de amido e a gelatina em maiores proporções geram maiores quantidades de poros, cujos dados corroboraram com os obtidos pelas análises físico-mecânicas (porosidade aparente e absorção de água) sendo o melhor resultado obtido para a amostra contendo gelatina (A1GEL15) cuja resistência a compressão simples foi maior do que 2MPa.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro de Ciências e Tecnologia - CCTpt_BR
dc.publisher.programPÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAISpt_BR
dc.publisher.initialsUFCGpt_BR
dc.subject.cnpqCiência e Engenharia de Materiaispt_BR
dc.titleCerâmica porosa obtida a partir de argilas utilizando secagem por congelamento.pt_BR
dc.date.issued2016-09-30-
dc.description.abstractPorous ceramics are solid materials which have a combination of a continue structure and a network of open pores interconnected that may or not be permeated by a liquid or gas. Although several researches on porous ceramics have been carried out, the results are still scarce for the application of these materials in construction to improve acoustic and thermal properties at the same time. Among the research conducted, several have used porous ceramics, such as alumina, zirconia, mullite and cordierite and bioceramics. The aim of this study was to produce ceramic masses from clays, water, starch or gelatin for the production of porous ceramic blocks, using freeze drying. The raw materials were processed and then characterized by X-ray fluorescence (chemical analysis), X-ray diffraction (mineralogical analysis), particle size analysis and thermogravimetric analysis (TG / DTA). Subsequently, ceramic bodies were prepared with different types of clays, and the respective amounts of additives (water, starch and gelatin), in predetermined amounts. From these masses, specimens were made, which were subjected to heat treatment at a temperature of 1100°C with a heating rate of 5°C/min. After this procedure, the samples were characterized by X-ray diffraction, scanning electron microscopy (SEM) and analysis of physical and mechanical properties. From the results of X-ray diffraction it was observed in the samples, after heat treatment, the presence of hematite peaks, cristobalite, spinel and the first peaks of mullite. From SEM images it was revealed that the addition of starch and gelatin in larger proportions generate increased amounts of pores, whose data corroborate with those obtained from physical-mechanical analysis (apparent porosity and water absorption) being the best result obtained for the sample containing gelatin (A1GEL15) whosesimple compression resistance was greater than 2MPa.pt_BR
dc.identifier.urihttp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/16038-
dc.date.accessioned2020-10-08T19:58:54Z-
dc.date.available2020-10-08-
dc.date.available2020-10-08T19:58:54Z-
dc.typeTesept_BR
dc.subjectCerâmica Porosapt_BR
dc.subjectArgilapt_BR
dc.subjectAmidopt_BR
dc.subjectGelatinapt_BR
dc.subjectPorous Ceramicpt_BR
dc.subjectClaypt_BR
dc.subjectStarchpt_BR
dc.subjectGelatinpt_BR
dc.rightsAcesso Abertopt_BR
dc.creatorRAMOS, Sileide de Oliveira.-
dc.publisherUniversidade Federal de Campina Grandept_BR
dc.languageporpt_BR
dc.title.alternativePorous ceramics obtained from clays using drying by freezing.pt_BR
dc.identifier.citationRAMOS, S. O. Cerâmica porosa obtida a partir de argilas utilizando secagem por congelamento. 2016. 71 f. Tese (Doutorado em Ciência e Engenharia de Materiais) – Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2016.pt_BR
Appears in Collections:Doutorado em Ciência e Engenharia de Materiais.

Files in This Item:
File Description SizeFormat 
SILEIDE DE OLIVEIRA RAMOS TESE (PPG-CEMAT) 2016.pdf3.23 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.