http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/18984| Title: | Estudo dos parâmetros operacionais e de composição para o enriquecimento de tungstênio na liga Ni-W. |
| Other Titles: | Study of the operational and composition parameters for tungsten enrichment in Ni-W alloy. Estudio de parámetros operativos y de composición para el enriquecimiento de tungsteno en aleación Ni-W. |
| ???metadata.dc.creator???: | OLIVEIRA, José Anderson Machado. |
| ???metadata.dc.contributor.advisor1???: | SILVA, Paulo Sérgio Gomes da. |
| ???metadata.dc.contributor.referee1???: | FREITAS, Juliano Carlo Rufino de. |
| ???metadata.dc.contributor.referee2???: | SANTANA, Renato Alexandre Costa de. |
| Keywords: | Eletrodeposição;Liga Ni-W;Voltametria cíclica;Eletroquímica;Corrosão;Electroplating;Ni-W alloy;Cyclic voltammetry;Electrochemistry;Corrosion;Aleación de Ni-W;Voltametría cíclica;Galvanoplastia;Electroquímica;Corrosión |
| Issue Date: | 22-Jul-2014 |
| Publisher: | Universidade Federal de Campina Grande |
| Citation: | OLIVEIRA, José Anderson Machado. Estudo dos parâmetros operacionais e de composição para o enriquecimento de tungstênio na liga Ni-W. 2014. 47 fl. (Trabalho de Conclusão de Curso – Monografia), Curso de Licenciatura em química, Centro de Educação e Saúde, Universidade Federal de Campina Grande, Cuité – Paraíba – Brasil, 2014. |
| ???metadata.dc.description.resumo???: | A eletrodeposição de ligas metálicas e um processo mais sofisticado do que a de metais puros, pois, requer um maior refinamento dos parâmetros operacionais para sua obtenção. Na codeposição de ligas unem-se as características dos constituintes metálicos para obter depósitos de melhor qualidade. As excelentes propriedades físicas e químicas do tungstênio agregadas às do níquel contribuem para o aumento na nobreza das ligas Ni-W. As soluções utilizadas para a obtenção dos depósitos foram preparadas com água destilada e deionizada, utilizando-se reagentes de alta pureza analítica. Como agentes complexantes utilizaram—se o tartarato e o oxalato de sódio associados. Avaliaram-se os parâmetros operacionais e de composição para o enriquecimento de tungstênio na liga Ni-W. O pH da solução foi ajustado para três valores estudados neste trabalho: 7, 5 e 3. Adicionou-se ácido sulfúrico para promover a solubilização dos reagentes e para avaliar a influência do pH na composição química da liga. Observou-se que a proporção entre os metais Ni e W variam de acordo com a diminuição no valor do pH da solução eletrolítica. Sendo o pH a única variável no processo de eletrodeposição, nota-se que a diminuição do mesmo favorece o aumento na proporção percentual em massa de tungstênio no depósito obtido. A liga tratada termicamente na temperatura de 600 aC apresentou uma inversão na proporção percentual em massa entre Ni e W, tal fato pode ser explicado pela possível migração do níquel para o substrato de cobre nesta temperatura. Notou-se um aumento considerável na dureza da liga quando submetida ao tratamento de 600 aC. Os resultados obtidos das curvas de polarização, obtidas em meio de NaCl 0,1 M, demonstram as características de resistência a corrosão das ligas estudadas. Observa—se uma elevação do potencial de corrosão com o decréscimo do pH, e consequentemente um aumento da resistência de polarização. Este comportamento está associado ao maior teor de W na liga obtida no menor valor de pH estudado. |
| Abstract: | The electroplating of metal alloys is a more sophisticated process than that of pure metals, therefore, requires a further refinement of the operational parameters to obtaining it. In the codeposition of alloys, the characteristics of the constituents are united to obtain better quality deposits. The excellent properties physical and chemical properties of tungsten added to nickel contribute to the increase in the nobility of Ni-W alloys. The solutions used to obtain deposits were prepared with distilled and deionized water, using high-quality reagents analytical purity. As complexing agents, tartrate and oxalate were used associated sodium The operational and composition parameters were evaluated for the enrichment of tungsten in the Ni-W alloy. The pH of the solution was adjusted to three values studied in this work: 7, 5 and 3. Sulfuric acid was added to promote the solubilization of reagents and to evaluate the influence of pH on chemical composition of the alloy. It was observed that the proportion between the metals Ni and W vary according to the decrease in the pH value of the electrolyte solution. Being the pH the only variable in the electrodeposition process, it is noted that the decrease in even favors the increase in the mass percentage proportion of tungsten in the obtained deposit. The heat-treated alloy at a temperature of 600 BC an inversion in the mass percentage ratio between Ni and W, this fact can be explained by the possible migration of nickel to the copper substrate in this temperature. A considerable increase in alloy hardness was noted when subjected to the treatment of 600 BC. The results obtained from the polarization, obtained in 0.1 M NaCl medium, demonstrate the characteristics of corrosion resistance of the studied alloys. An increase in the potential is observed corrosion with decreasing pH, and consequently an increase in polarization resistance. This behavior is associated with a higher content of W in the alloy obtained in the lowest studied pH value. |
| ???metadata.dc.description.resumen???: | La galvanoplastia de aleaciones metálicas es un proceso más sofisticado que el de metales puros, por lo tanto, requiere un mayor refinamiento de los parámetros operativos para su obtención. En la codeposición de aleaciones, las características de los constituyentes están unidas para obtener depósitos de mejor calidad. Las excelentes propiedades Las propiedades físicas y químicas del tungsteno agregado al níquel contribuyen al aumento en la nobleza de las aleaciones Ni-W. Las soluciones utilizadas para obtener depósitos se prepararon con agua destilada y desionizada, utilizando reactivos de alta calidad pureza analítica. Como agentes complejantes se utilizaron tartrato y oxalato. sodio asociado Se evaluaron los parámetros operativos y de composición para el enriquecimiento de tungsteno en la aleación Ni-W. El pH de la solución se ajustó a tres valores estudiados en este trabajo: 7, 5 y 3. Se añadió ácido sulfúrico a promover la solubilización de los reactivos y evaluar la influencia del pH en composición química de la aleación. Se observó que la proporción entre los metales Ni y W varían según la disminución del valor de pH de la solución de electrolito. Siendo el pH la única variable en el proceso de electrodeposición, se observa que la disminución en incluso favorece el aumento de la proporción porcentual de masa de tungsteno en el deposito obtenido. La aleación tratada térmicamente a una temperatura de 600 AC. una inversión en la relación porcentual de masa entre Ni y W, este hecho puede ser explicado por la posible migración de níquel al sustrato de cobre en este temperatura. Se notó un aumento considerable en la dureza de la aleación cuando sometido al tratamiento del 600 a. C. Los resultados obtenidos de la polarización, obtenida en medio NaCl 0,1 M, demuestran las características de resistencia a la corrosión de las aleaciones estudiadas. Se observa un aumento en el potencial corrosión con la disminución del pH y, en consecuencia, un aumento en la Resistencia a la polarización. Este comportamiento está asociado a un mayor contenido de W en la aleación obtenida en el valor de pH más bajo estudiado. |
| Keywords: | Eletrodeposição Liga Ni-W Voltametria cíclica Eletroquímica Corrosão Electroplating Ni-W alloy Cyclic voltammetry Electrochemistry Corrosion Aleación de Ni-W Voltametría cíclica Galvanoplastia Electroquímica Corrosión |
| ???metadata.dc.subject.cnpq???: | Espectroscopia |
| URI: | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/18984 |
| Appears in Collections: | Curso de Licenciatura em Química - CES - Monografias |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| JOSÉ ANDERSON MACHADO OLIVEIRA - TCC LICENCIATURA EM QUÍMICA CES 2014.pdf | José Anderson Machado Oliveira - TCC Licenciatura em Química CES 2014.pdf | 7.83 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.