http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/254| Title: | Obtenção de sistemas de PCL com subproduto da cultura algodoeira. |
| Other Titles: | Obtaining PCL systems with a by-product of the cotton crop. |
| ???metadata.dc.creator???: | BEZERRA, Elieber Barros. |
| ???metadata.dc.contributor.advisor1???: | ARAÚJO, Edcleide Maria. |
| ???metadata.dc.contributor.advisor2???: | ROSA, Morsyleide de Freitas. |
| ???metadata.dc.contributor.referee1???: | CAVALCANTI, Wilma Sales. |
| ???metadata.dc.contributor.referee2???: | PAZ, Rene Anisio da. |
| Keywords: | Poli(ε-caprolactona).;Línter de Algodão.;Nanolínter.;Poly(ε-caprolactone).;Cotton Linter. |
| Issue Date: | 19-Aug-2014 |
| Publisher: | Universidade Federal de Campina Grande |
| Citation: | BEZERRA, Elieber Barros. Obtenção de sistemas de PCL com subproduto da cultura algodoeira. 2014. 96 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) – Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande, Campina Grande, Paraíba, Brasil, 2014. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/254 |
| ???metadata.dc.description.resumo???: | Estudos têm sido realizados com o intuito de criar processos que utilizem matérias-primas renováveis, gerando assim produtos não agressivos ao meio ambiente, sem perder em qualidade ou desempenho. Este trabalho teve como objetivo a obtenção de sistemas de poli(ε-caprolactona) (PCL) com subproduto da cultura algodoeira, a fim de avaliar a influência dos componentes línter e nanolínter de algodão nas propriedades finais dos compósitos poliméricos. Os sistemas de PCL com 1, 3 e 5% de cargas foram obtidos em extrusora e, processados em injetora, caracterizados quanto à composição lignocelulósica, tamanho de partícula e potencial zeta, difração de raios-X (DRX), termogravimetria (TG), calorimetria exploratória diferencial (DSC), microscopia eletrônica de varredura (MEV), propriedades mecânicas e temperatura de deflexão térmica (HDT). Por meio da caracterização lignocelulósica foi observado um alto teor de celulose para a fibra vegetal e, por medida do tamanho de partícula e potencial zeta, foram observadas partículas com diâmetro médio na faixa nanométrica. Por DRX, foi vista a presença dos picos característicos da PCL pura, do línter e da nanocelulose. Para os sistemas PCL/Línter e PCL/Nano não foram visualizadas alterações nos picos característicos da matriz. Por TG, foi verificada que a presença da carga não influenciou no comportamento térmico dos sistemas. Por DSC, não foram observadas alterações na cristalinidade dos sistemas com a presença do línter e do nanolínter. Por meio das fotomicrografias de MEV, foi observada a má adesão da matriz polimérica ao línter e ao nanolínter. Por meio dos ensaios de tração e flexão, foi observado que os sistemas com línter apresentaram um pequeno aumento no módulo e na resistência. Para os sistemas contendo nanolínter, os valores de módulo e de resistência foram similares aos da matriz. Por meio do ensaio de resistência ao impacto, foi observado que as cargas utilizadas diminuíram a resistência dos compósitos. Um aumento na temperatura de deflexão térmica (HDT) dos sistemas foi visto com a presença das cargas. |
| Abstract: | Studies have been carried out with the aim of creating processes that use renewable raw materials, thus generating products that are not environmentally aggressive, without losing quality or performance. The aim of this work was to obtain poly (ε-caprolactone) (PCL) systems with a by-product of the cotton crop in order to evaluate the influence of cotton liner and nanolinter components on the final properties of the polymer composites. The PCL systems with 1, 3 and 5% of loading were obtained in an extruder and processed in injectors, characterized by lignocellulosic composition, particle size and zeta potential, X-ray diffraction (XRD), thermogravimetry (TG), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), mechanical properties and thermal deflection temperature (HDT). By means of the lignocellulosic characterization, a high cellulose content was observed for the vegetable fiber and, due to the particle size and zeta potential, particles with a mean diameter in the nano range were observed. By DRX, the peaks characteristic of pure PCL, linter and nanocellulose were observed. For PCL / Línter and PCL / Nano systems, no changes were seen in the characteristic peaks of the array. By TG, it was verified that the presence of the load did not influence the thermal behavior of the systems. By DSC, no changes were observed in the crystallinity of the systems with the presence of linter and nanolinter. By SEM photomicrographs, the poor adhesion of the polymer matrix to the linter and the nanolinter was observed. By means of the tensile and flexure tests, it was observed that the systems with linter presented a small increase in the modulus and the resistance. For systems containing nanolinter, the modulus and resistance values were similar to those of the matrix. By means of the impact strength test, it was observed that the loads used decreased the resistance of the composites. An increase in the thermal deflection temperature (HDT) of the systems was seen with the presence of the charges. |
| Keywords: | Poli(ε-caprolactona). Línter de Algodão. Nanolínter. Poly(ε-caprolactone). Cotton Linter. |
| ???metadata.dc.subject.cnpq???: | Ciência e Engenharia de Materiais. |
| URI: | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/254 |
| Appears in Collections: | Mestrado em Ciência e Engenharia de Materiais. |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| ELIEBER BARROS BEZERRA - DISSERTAÇÃO PPGCEMAT 2014.pdf | Elieber Barros Bezerra - DISSERTAÇÃO PPGCEMAT 2014 | 16.7 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.