1. Biblioteca Digital de Teses e Dissertações da UFCG
  2. Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
  3. PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA
  4. Mestrado em Engenharia Mecânica.
Please use this identifier to cite or link to this item: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/2818
Full metadata record
DC FieldValueLanguage
dc.creator.IDSANTOS, A. X.pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/0810494477757052pt_BR
dc.contributor.advisor1MACIEL, Theophilo Moura.-
dc.contributor.advisor1IDMACIEL, T. M.pt_BR
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/9476858938351846pt_BR
dc.contributor.referee1SANTOS, Marco Antonio dos.-
dc.contributor.referee1IDSANTOS, M. Apt_BR
dc.contributor.referee1Latteshttp://lattes.cnpq.br/4825985900425353pt_BR
dc.contributor.referee2SANTANA, Renato Alexandre Costa de.-
dc.contributor.referee2IDSANTANA, R. A. C.pt_BR
dc.contributor.referee2Latteshttp://lattes.cnpq.br/1438381290031148pt_BR
dc.description.resumoAs falhas por corrosão são as principais causadoras de vazamento na indústria do petróleo. Por esta razão tem sido muito estudada a utilização de novos materiais com melhores resistências a este fenômeno. Uma das alternativas mais utilizadas, devido ao menor custo envolvido, é a aplicação de revestimentos com estes materiais através de processos de soldagem. Este trabalho teve como objetivo inicialmente encontrar os melhores parâmetros de soldagem para se obter o perfil geométrico dos cordões de solda mais adequado para este fim, principalmente a diluição, utilizando planejamento experimental estatístico fatorial em dois níveis e determinar em seguida a resistência à corrosão dos cordões depositados utilizando dois processos de soldagem. Foram utilizados o processo Plasma Pó (PTA-P) e o processo MIG (Metal Inert Gás) ambos automatizados, e como metal de adição, a liga AWS ER NiCrMo-3, à base de Ni , conhecida comercialmente como Inconel 625, na forma de pó com granulometria de 63 µm no processo PTA-P e na forma de arame com diâmetro de 1,2 mm no processo MIG. Como metal de base utilizou-se chapas do aço API 5L X70 utilizado na fabricação de dutos para transporte de petróleo. A resistência à corrosão dos revestimentos foi avaliada por polarização potenciodinâmica linear e espectroscopia de impedância eletroquímica. Foram avaliados também o percentual de Fe e os valores de microdureza na superfície dos revestimentos, Os resultados mostraram que o reforço, a penetração e a diluição dos revestimentos depositados pelo processo PTA-P assim como os seus valores de microdureza foram menores do que aqueles obtidos pelo processo GMAW. Os revestimentos obtidos pelo processo PTA-P também apresentaram melhores resultados de resistência à corrosão.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro de Ciências e Tecnologia - CCTpt_BR
dc.publisher.programPÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICApt_BR
dc.publisher.initialsUFCGpt_BR
dc.titleAvaliação da resistência à corrosão de revestimento à base de inconel 625 utilizando os processos de soldagem MIG e plasma pó.pt_BR
dc.date.issued2014-02-28-
dc.description.abstractThe corrosion failures are the main cause of leakage in oil industry. Because of this new materials with higher corrosion resistance have been researched. One of the alternatives more used, for its low cost, is the application of coating by welding process. This work aimed first to find the better welding parameters to obtain the more adequate weld bead geometry, mainly the dilution, using a factorial statistical experimental design on two levels, and following to determinate its corrosion resistance using two welding process. Automatized Plasma Transferred Arc- Powder (PTA-P) and Metal Inert Gas (MIG) were used. The AWS ER NiCrMo-3Ni alloy, knowing as Inconel 625, in powder form with grain size 63 µm and in wire with 1,2 mm diameter were used as filler metals. API 5L X70 steel plate, used in pipeline for oil and gas transportation was used as base metal. The corrosion resistance was evaluated using linear potentiodynamic polarization and electrochemical impedance spectroscopy analysis. The Fe percents and microhardness test in weld bead surface were also done. The results showed that the weld bead hardness and its penetration and dilution obtained by PTA-P process were lower than those obtained by GMAW process. The coating obtained by PTA-P process also presented better corrosion resistance.pt_BR
dc.identifier.urihttp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/2818-
dc.date.accessioned2019-02-18T17:39:17Z-
dc.date.available2019-02-18-
dc.date.available2019-02-18T17:39:17Z-
dc.typeDissertaçãopt_BR
dc.subjectRevestimentopt_BR
dc.subjectResistência à Corrosãopt_BR
dc.subjectProcesso PTA-Ppt_BR
dc.subjectProcesso MIGpt_BR
dc.subjectInconel 625pt_BR
dc.subjectCoatingpt_BR
dc.subjectCorrosion Resistancept_BR
dc.subjectPTA-P processpt_BR
dc.subjectMIG processpt_BR
dc.rightsAcesso Abertopt_BR
dc.creatorSANTOS, Aureliano Xavier dos.-
dc.publisherUniversidade Federal de Campina Grandept_BR
dc.languageporpt_BR
dc.title.alternativeEvaluation of corrosion resistance of 625 inconel-based coating using the MIG and plasma plasma welding processes.pt_BR
dc.identifier.citationSANTOS, Aureliano Xavier dos. Avaliação da resistência à corrosão de revestimento à base de inconel 625 utilizando os processos de soldagem MIG e plasma pó. 2014. 150f. Dissertação (Mestrado em Engenharia Mecânica) – Programa de Pós-Graduação em Engenharia Mecânica, Centro de Ciência e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2014. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/2818pt_BR
Appears in Collections:Mestrado em Engenharia Mecânica.

Files in This Item:
File Description SizeFormat 
AURELIANO XAVIER DOS SANTOS - DISSERTAÇÃO PPGEM 2014.pdfAureliano Xavier dos Santos - Dissertação PPGEM 20143.43 MBAdobe PDFView/Open
Show simple item record


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.