http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/29231| Title: | Deposição de revestimento AISI 317L contra corrosão por processo GTAW mecanizado com adição de arame frio. |
| Other Titles: | AISI 317L coating deposition against process corrosion Mechanized GTAW with addition of cold wire. Deposición de recubrimiento AISI 317L contra la corrosión del proceso GTAW mecanizado con adición de hilo frío. |
| ???metadata.dc.creator???: | SANTOS, Rafael Barbosa Carneiro dos. |
| ???metadata.dc.contributor.advisor1???: | SANTANA, Renato Alexandre Costa de. |
| ???metadata.dc.contributor.advisor-co1???: | SILVA, Marcos Mesquita da. |
| ???metadata.dc.contributor.referee1???: | MACIEL, Theophilo Moura. |
| ???metadata.dc.contributor.referee2???: | MELO, Raphael Henrique Falcão de. |
| Keywords: | Soldagem de revestimento;AISI 317L;Corrosão;GTAW- MAF;Aço Inoxidável austenítico;Overlay welding;Corrosion;Austenitic stainless steel;Soldadura de superposición;Acero inoxidable austenitico |
| Issue Date: | 23-Dec-2021 |
| Publisher: | Universidade Federal de Campina Grande |
| Citation: | SANTOS, Rafael Barbosa Carneiro dos. Deposição de revestimento AISI 317L contra corrosão por processo GTAW mecanizado com adição de arame frio. 2022. 114fl. (Dissertação de Mestrado), Programa de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2019. Disponível em:http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/29231 |
| ???metadata.dc.description.resumo???: | O presente trabalho tem como objetivo investigar a resistência à corrosão de revestimentos de aço inoxidável austenítico aplicados em substrato de aço carbono via processo GTAW mecanizado com adição de arame frio (GTAW-MAF). As soldagens foram realizadas utilizando como o metal de adição arames do aço AISI 317L, com diâmetro de 1,2mm. Inicialmente, foi realizado um estudo sistemático de cordões de solda isolados a fim de investigar o efeito dos parâmetros de soldagem na geometria e diluição desses cordões. Para isso, foi traçado um planejamento de experimentos fatorial linear com três variáveis independentes (corrente, velocidade de alimentação e distância eletrodo/peça) além da adição de pontos centrais e axiais (23+6+3), totalizando 17 ensaios. As variáveis respostas analisadas foram diluição (%), molhabilidade (°), altura e largura dos cordões (mm), selecionando três experimentos com a melhor viabilidade operacional para serem utilizados no processo de revestimento. No processo de soldagem de revestimentos utilizou-se duas técnicas: com e sem preaquecimento do substrato. A temperatura de preaquecimento utilizada foi de 150oC. Para os cordões isolados, obteve- se alturas entre 1,87 e 5,03mm, larguras entre 6,79 e 13,03mm, molhabilidades entre 51,60 e 133,65o e diluições entre 5,65 e 47,82%. O preaquecimento mostrou-se eficaz na diminuição de descontinuidades entre cordões e conseguiu-se desenvolver uma técnica satisfatória e replicável para a deposição de revestimento AISI 317L via processo GTAW- MAF. Verificou-se que o processo de deposição utilizado conferiu revestimentos com composição química semelhantes às do material de adição utilizado e que os melhores resultados de resistência à corrosão e diluição se deram ao utilizar correntes de soldagem acima de 220A, velocidade de alimentação entre 4m/min e 5m/min e distância do eletrodo para a peça de 10mm. O revestimento R2T2 apresentou bons resultados de diluição (10,38%), resistência à polarização 2,8x maior em relação ao substrato, pouca presença de inclusões e boa regularidade operacional na deposição dos cordões com baixa presença de descontinuidades. |
| Abstract: | The present work aims to investigate the corrosion resistance of austenitic stainless steel coatings applied on carbon steel substrate via mechanized GTAW process with the addition of cold wire (GTAW-MAF). The welds were carried out using AISI 317L steel wires with a diameter of 1.2mm as the filler metal. For the isolated welding beads, a linear factorial design experiment was designed with three independent variables (current, feed speed and electrode/part distance) and with the addition of central and axial points (23+6+3), totaling 17 tests . The response variables analyzed were dilution (%), wettability (°), height and width of beads (mm), selecting the three parameters with the best operational feasibility to be used in the coating process. In the welding coatings process, two techniques were used: with and without substrate preheating. Preheating proved to be effective in reducing discontinuities between weld beads and it was possible to develop a viable and replicable technique for the deposition of AISI 317L coating via the GTAW-MAF process. It was found that the deposition process used provided coatings with chemical composition similar to those of the addition material used and that the best results in corrosion resistance and dilution were given when using welding currents above 220A, feed speed between 4m/min and 5m/min and electrode-to-part distance of 10mm. The R2T2 coating showed good dilution results (10.38%), resistance to polarization 2.8x greater in relation to the substrate, little presence of inclusions and good operational regularity in the deposition of beads with low presence of discontinuities. |
| ???metadata.dc.description.resumen???: | El presente trabajo tiene como objetivo investigar la resistencia a la corrosión de Recubrimientos de acero inoxidable austenítico aplicados al sustrato de acero al carbono a través de Proceso GTAW mecanizado con adición de hilo frío (GTAW-MAF). las soldaduras se realizaron utilizando alambres de acero AISI 317L como metal de aporte, con 1,2 mm de diámetro. Inicialmente, se llevó a cabo un estudio sistemático de los cordones de soldadura. aislado para investigar el efecto de los parámetros de soldadura en la geometría y la dilución de estos cordones. Para ello se diseñó un diseño factorial lineal de experimentos con tres variables independientes (corriente, velocidad de avance y distancia electrodo/pieza) además de la suma de puntos centrales y axiales (23+6+3), totalizando 17 ensayo. Las variables de respuesta analizadas fueron dilución (%), humectabilidad (°), altura y ancho del cordón (mm), seleccionando tres experimentos con la mejor viabilidad operativo para ser utilizado en el proceso de recubrimiento. En el proceso de soldadura de recubrimientos se utilizaron dos técnicas: con y sin precalentamiento del sustrato. A La temperatura de precalentamiento utilizada fue de 150oC. Para los hilos aislados se obtuvo si alturas entre 1,87 y 5,03 mm, anchos entre 6,79 y 13,03 mm, humectabilidad entre 51,60 y 133,65o y diluciones entre 5,65 y 47,82%. El precalentamiento demostró ser efectivo en reducción de discontinuidades entre cuerdas y fue posible desarrollar una técnica satisfactorio y replicable para la deposición de recubrimiento AISI 317L a través del proceso GTAW MAF. Se encontró que el proceso de deposición utilizado proporcionó recubrimientos con composición química similar a la del material de relleno utilizado y que la mejor Se obtuvieron resultados de resistencia a la corrosión y dilución al usar corrientes de soldadura por encima de 220A, velocidad de avance entre 4m/min y 5m/min y distancia de electrodos para la pieza de 10 mm. El recubrimiento R2T2 mostró buenos resultados de dilución. (10,38%), resistencia a la polarización 2,8x mayor respecto al sustrato, poca presencia de inclusiones y buena regularidad operativa en la deposición de cordones con baja presencia de discontinuidades. |
| Keywords: | Soldagem de revestimento AISI 317L Corrosão GTAW- MAF Aço Inoxidável austenítico Overlay welding Corrosion Austenitic stainless steel Soldadura de superposición Acero inoxidable austenitico |
| ???metadata.dc.subject.cnpq???: | Engenharia Mecânica |
| URI: | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/29231 |
| Appears in Collections: | Mestrado em Engenharia Mecânica. |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| RAFAEL BARBOSA CARNEIRO DOS SANTOS - DISSERTAÇÃO PPGEM 2022.pdf | Rafael Barbosa Carneiro dos Santos - Dissertação PPGEM 2022 | 7.87 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.