DC Field | Value | Language |
---|---|---|
dc.creator.ID | ARAÚJO, E. B. | pt_BR |
dc.creator.Lattes | http://lattes.cnpq.br/3772694813623764 | pt_BR |
dc.contributor.advisor1 | NARDOU, Françoise. | - |
dc.contributor.advisor1ID | NARDOU, F. | pt_BR |
dc.contributor.advisor-co1 | PONTES, Luiz Renato de Araújo. | - |
dc.contributor.advisor-co1ID | PONTES, L. R. A. | pt_BR |
dc.contributor.advisor-co1Lattes | http://lattes.cnpq.br/4820371851760936 | pt_BR |
dc.contributor.referee1 | CARVALHO, Laura Hecker de. | - |
dc.contributor.referee2 | GUEDES, Severino Jackson. | - |
dc.description.resumo | Este trabalho apresenta o estudo sobre a oxidação do ferro puro em temperaturas elevadas e sua correlação com as tensões decorrentes. As amostras em forma de plaquetas retangulares de 15 x 5 mm e com espessuras de 1 e 2 mm foram oxidadas sob atmosferas de argônio ou oxigênio e vapor d'água. As temperaturas das experiências variaram entre 850 e 950°C numa faixa de tempo entre 20 e 50 minutos. Os produtos obtidos foram caracterizados por difração de raios-X, microscopia óptica e por microscopia eletrônica de varredura. Os resultados mostraram que em todos os casos a camada era composta de três óxidos: wustita (FeO), magnetita (Fe304) e hematita (Fe203). Para efetuar o cálculo de tensão, foi escolhida a amostra oxidada a 950°C (Ar/H20) por apresentar uma camada mais aderente e ao mesmo tempo uma granulometria mais fina. Os resultados revelaram que a camada de óxido era submetida a uma tensão compressiva. | pt_BR |
dc.publisher.country | Brasil | pt_BR |
dc.publisher.department | Centro de Ciências e Tecnologia - CCT | pt_BR |
dc.publisher.program | PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA | pt_BR |
dc.publisher.initials | UFCG | pt_BR |
dc.subject.cnpq | Engenharia Mecânica. | pt_BR |
dc.title | Interação tensão-oxidação: caso da oxidação do ferro pelo vapor d'água. | pt_BR |
dc.date.issued | 1994-01 | - |
dc.description.abstract | This work presents the study on the oxidation of pure iron at temperatures their correlation with the resulting tensions. The samples in the form of rectangular platelets of 15 x 5 mm and with thicknesses of 1 and 2 mm were oxidized under atmospheres of argon or oxygen and water vapor. Experiment temperatures ranged from 850 to 950øC in a time range of 20 to 50 minutes. The obtained products were characterized by X-ray diffraction, optical microscopy and scanning electron microscopy. The results showed that in all cases the layer was composed of three oxides: wustita (FeO), magnetite (Fe304) and hematite (Fe203). To perform the voltage calculation, the oxidized sample was chosen at 950 ° C (Ar / H2O) because it has a more adherent layer and at the same time a finer granulometry. The results revealed that the oxide layer was subjected to a compressive stress. | pt_BR |
dc.identifier.uri | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3512 | - |
dc.date.accessioned | 2019-04-18T15:43:47Z | - |
dc.date.available | 2019-04-18 | - |
dc.date.available | 2019-04-18T15:43:47Z | - |
dc.type | Dissertação | pt_BR |
dc.subject | Oxidação de ferro | pt_BR |
dc.subject | Ferro - oxidação | pt_BR |
dc.subject | Interação tensão-oxidação | pt_BR |
dc.subject | oxidação pelo vapor d'água | pt_BR |
dc.subject | Cinética da oxidação de ferro | pt_BR |
dc.subject | Iron Oxidation | pt_BR |
dc.subject | Oxydation du fer | pt_BR |
dc.subject | Cinétique de l'oxydation du fer | pt_BR |
dc.subject | Kinetics of iron oxidation | pt_BR |
dc.rights | Acesso Aberto | pt_BR |
dc.creator | ARAÚJO, Edjânio Barbosa. | - |
dc.publisher | Universidade Federal de Campina Grande | pt_BR |
dc.language | por | pt_BR |
dc.title.alternative | Tension-oxidation interaction: case of iron oxidation by water vapor. | pt_BR |
dc.identifier.citation | ARAÚJO, Edjânio Barbosa. Interação tensão-oxidação: caso da oxidação do ferro pelo vapor d'água. 1994. 102f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 1994. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/3512 | pt_BR |
Appears in Collections: | Mestrado em Engenharia Mecânica. |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
EDJÂNIO BARBOSA ARAÚJO - DISSERTAÇÃO PPGEM 1994.pdf | Edjânio Barbosa Araújo - Dissertação PPGEM 1994 | 13.82 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.