1. Biblioteca Digital de Teses e Dissertações da UFCG
  2. Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
  3. PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
  4. Doutorado em Ciência e Engenharia de Materiais.
Please use this identifier to cite or link to this item: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35601
Full metadata record
DC FieldValueLanguage
dc.contributor.advisor1CASTRO, Walman Benício de.-
dc.contributor.advisor1IDBenicio DE CASTRO, Walman.pt_BR
dc.contributor.advisor1IDCASTRO, W. B.pt_BR
dc.contributor.advisor1IDde Castro, W. B.pt_BR
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/3592569966434979pt_BR
dc.contributor.referee1ARAÚJO, Carlos José de.-
dc.contributor.referee1IDDE ARAÚJO, C. J.pt_BR
dc.contributor.referee1IDDe Araujo, Cpt_BR
dc.contributor.referee1IDDEARAUJO, Cpt_BR
dc.contributor.referee1Latteshttp://lattes.cnpq.br/9466801408291152pt_BR
dc.contributor.referee2MACIEL, Theophilo Moura.-
dc.contributor.referee2IDMACIEL, T. M.pt_BR
dc.contributor.referee2IDMACIEL, THEOPHILO MOURA.pt_BR
dc.contributor.referee2IDDiego D. S. Diniz.pt_BR
dc.contributor.referee2Latteshttp://lattes.cnpq.br/9476858938351846pt_BR
dc.description.resumoEste trabalho teve como finalidade estudar uma série de cinco composições de ligas Ti50Ni50-xZrx (x = 0, 2, 5, 10 e 15 %at.) e avaliar a interferência da substituição do níquel pelo zircônio e a influência do percentual de zircônio nas propriedades térmicas, mecânicas e corrosivas. As ligas foram produzidas empregando o processo de fundição Plasma Skull Push-Pull (PSPP) e estudadas por diversas técnicas e ensaios para averiguação das características térmicas, mecânicas e corrosivas. As ligas foram obtidas com sucesso pelo processo PSPP. Verificou-se que a partir de 15% de zircônio a liga apresentou alta fragilidade devido a solubilidade parcial do percentual de zircônio no níquel. De forma geral podemos afirmar que a adição e aumento do percentual de zircônio favoreceram a formação de fases secundárias que interferiram diretamente nas temperaturas de transformação, na microdureza e na resistência a corrosão. A transformação da fase B2 em fase B19' ocorre em uma única etapa e as temperaturas Mi e Ai aumentam de 2oC para 48oC e de -20oC para 93oC para as ligas TiNi50 e TiNi40Zr10, respectivamente. A adição de zircônio ocasionou o aparecimento de partículas de segunda fase nos limites de grão da matriz das ligas com 5,10 e 15% de zircônio e estas fases possuem microdureza mais elevada que a fase matriz. A resistência à corrosão aumentou de η20,23KΩ para 1007,30KΩ e a microdureza da fase matriz 346HV para 805HV para as ligas TiNi50 e TiNi40Zr10 respectivamente.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro de Ciências e Tecnologia - CCTpt_BR
dc.publisher.programPÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAISpt_BR
dc.publisher.initialsUFCGpt_BR
dc.subject.cnpqEngenharia de Materiaispt_BR
dc.titleInfluência do percentual de zircônio nas propriedades térmicas, mecânicas e corrosivas de ligas Ti50Ni50-xZrx com memória de forma.pt_BR
dc.date.issued2019-07-12-
dc.description.abstractThe objective of this work was to study a series of five Ti50Ni50-x Zrx alloy compositions (x = 0, 2, 5, 10 and 15% at.) And to evaluate the interference of nickel substitution by zirconium and the influence of zirconium percentage on thermal, mechanical and corrosive properties. The alloys were produced using the Plasma Skull Push-Pull (PSPP) casting process and studied by various techniques and tests to verify the thermal, mechanical and corrosive characteristics. The alloys were successfully obtained by the PSPP process. It was found that from 15% of zirconium the alloy showed high brittleness due to partial solubility of nickel zirconium percentage. In general we can state that the addition and increase of zirconium percentage favored the formation of secondary phases that directly affected the transformation temperatures, microhardness and corrosion resistance. The transformation from phase B2 to phase B19 'occurs in a single step and temperatures Mi and Ai increase from 2oC to 48oC and from -20oC to 93oC for TiNi50 and TiNi40Zr10 alloys, respectively. The addition of zirconium caused the appearance of second phase particles in the matrix grain boundaries of the alloys with 5.10 and 15% zirconium and these phases have higher microhardness than the matrix phase. The corrosion resistance increased from η20.23KΩ to 1007.30KΩ and the microhardness of the 346HV matrix phase to 805HV for TiNi50 and TiNi40Zr10 alloys respectively.pt_BR
dc.identifier.urihttp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35601-
dc.date.accessioned2024-05-10T11:44:22Z-
dc.date.available2024-05-10-
dc.date.available2024-05-10T11:44:22Z-
dc.typeTesept_BR
dc.subjectEngenharia de materiaispt_BR
dc.subjectLigas de TiNiZrpt_BR
dc.subjectEfeito de memória de formapt_BR
dc.subjectCorrosãopt_BR
dc.subjectMicrodurezapt_BR
dc.subjectMaterials engineeringpt_BR
dc.subjectTiNiZr alloyspt_BR
dc.subjectEffect of shape memorypt_BR
dc.subjectCorrosionpt_BR
dc.subjectMicrohardnesspt_BR
dc.subjectIngenieria de materialespt_BR
dc.subjectAleaciones de TiNiZrpt_BR
dc.subjectEfecto de Memoria de formapt_BR
dc.rightsAcesso Abertopt_BR
dc.creatorRAMOS, Alana Pereira.-
dc.publisherUniversidade Federal de Campina Grandept_BR
dc.languageporpt_BR
dc.title.alternativeInfluence of zirconium percentage on thermal properties, mechanical and corrosive properties of Ti50Ni50-xZrx shape memory alloys.pt_BR
dc.title.alternativeInfluencia del porcentaje de circonio en las propiedades térmicas. Propiedades mecánicas y corrosivas de las aleaciones con memoria de forma Ti50Ni50-xZrx.pt_BR
dc.identifier.citationRAMOS, Alana Pereira. Influência do percentual de zircônio nas propriedades térmicas, mecânicas e corrosivas de ligas Ti50Ni50-xZrx com memória de forma. 2019. 83 fl. Tese (Doutorado em Engenharia de Materiais) - Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2019. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35601pt_BR
dc.description.resumenEste trabajo tuvo como objetivo estudiar una serie de cinco composiciones. de aleaciones Ti50Ni50-xZrx (x = 0, 2, 5, 10 y 15 % at.) y evaluar la interferencia de sustitución del níquel por circonio y la influencia del porcentaje de circonio en Propiedades térmicas, mecánicas y corrosivas. Las aleaciones fueron producidas utilizando el proceso de fundición Plasma Skull Push-Pull (PSPP) y estudiado mediante diversas técnicas y pruebas para investigar las características térmicas, mecánico y corrosivo. Las aleaciones se obtuvieron con éxito mediante el proceso PSPP. Se encontró que a partir del 15% de circonio la aleación presentaba alta fragilidad debido a la solubilidad parcial del porcentaje de circonio en níquel. En general podemos afirman que la adición y aumento del porcentaje de circonio favoreció la formación de fases secundarias que interfirieron directamente en las temperaturas de transformación, microdureza y resistencia a la corrosión. La transformación de fase B2 en la fase B19' ocurre en un solo paso y las temperaturas Mi y Ai aumentan en 2oC a 48oC y de -20oC a 93oC para las aleaciones TiNi50 y TiNi40Zr10, respectivamente. La adición de circonio provocó la aparición de partículas de segunda fase en los límites de grano de la matriz de aleación con 5,10 y 15% de circonio y Estas fases tienen una microdureza mayor que la fase matriz. la resistencia a la corrosión aumentó de η20,23 KΩ a 1007,30 KΩ y la microdureza de la fase de la matriz 346HV a 805HV para aleaciones TiNi50 y TiNi40Zr10 respectivamente.pt_BR
Appears in Collections:Doutorado em Ciência e Engenharia de Materiais.

Files in This Item:
File Description SizeFormat 
ALANA PEREIRA RAMOS - TESE PPG-CEMat 2019.pdfAlana Pereira Ramos - Tese PPG-CEMat 20192.05 MBAdobe PDFView/Open
Show simple item record


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.