1. Biblioteca Digital de Teses e Dissertações da UFCG
  2. Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
  3. PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
  4. Doutorado em Ciência e Engenharia de Materiais.
Please use this identifier to cite or link to this item: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35747
Full metadata record
DC FieldValueLanguage
dc.creator.IDFARIAS, G. M. G.pt_BR
dc.creator.IDGiselly M. G. Farias.pt_BR
dc.creator.IDFARIAS, GISELLY M.G.pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/5374756102252621pt_BR
dc.contributor.advisor1MÉLO, Tomás Jeferson Alves de.-
dc.contributor.advisor1IDMÉLO, T. J. A.pt_BR
dc.contributor.advisor1IDMELO, TOMÁS JEFERSON ALVES DE.pt_BR
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/8562091525519918pt_BR
dc.contributor.referee1ARAÚJO, Edcleide Maria.-
dc.contributor.referee1IDAraújo, E. M.;;pt_BR
dc.contributor.referee1IDE. M. Araújopt_BR
dc.contributor.referee1IDEdcleide M. Araújo.pt_BR
dc.contributor.referee1Latteshttp://lattes.cnpq.br/1097999681102529pt_BR
dc.contributor.referee2WELLEN, Renate Thiago Cândido.-
dc.contributor.referee2IDWELLEN, R. M. R.pt_BR
dc.contributor.referee2IDWELLEN, RENATE M.R.pt_BR
dc.contributor.referee2Latteshttp://lattes.cnpq.br/5406259642631461pt_BR
dc.contributor.referee3CUNHA, Carlos Thiago Cândido.-
dc.contributor.referee3IDCUNHA, C. T. C.pt_BR
dc.contributor.referee3IDCUNHA, C. T.pt_BR
dc.contributor.referee3Latteshttp://lattes.cnpq.br/0288408380576553pt_BR
dc.description.resumoNeste trabalho estudou-se o efeito da concentração de EVA e do teor de VA de EVA nas propriedades mecânicas, morfológicas e reológicas de blendas de polietileno de alta densidade de fonte renovável e copolímero de etileno- acetato de vinila (BioPE/EVA). As blendas foram caracterizadas por Difração de Raios-X (XRD), Calorimetria Diferencial de Varredura, Microscopia Eletrônica de Varredura (MEV) e medidas reológicas sob fluxo de cisalhamento oscilatório. O grau de cristalinidade do BioPE diminuiu com o aumento da concentração de EVA e não foi afetado pelo aumento no conteúdo de VA. Os resultados do DMTA mostraram uma diminuição no módulo de armazenamento (E ') com o aumento no conteúdo de EVA e que as blendas de BioPE/EVA19 apresentaram valores mais altos de E' do que as blendas de BioPE/EVA28. A resistência ao impacto aumentou substancialmente com a adição de concentração de EVA acima de 5% e foi maior para as misturas contendo o maior teor de VA. As blendas contendo maior conteúdo de VA exibiram maior tamanho de domínios da fase dispersa de EVA, do que com o aumentou da concentração de EVA. A viscosidade complexa aumentou com o aumento do conteúdo de EVA, sendo maior para as blendas de BioPE / EVA contendo maior teor de VA. O módulo de armazenamento aumentou, em baixas freqüências, com o aumento no conteúdo de EVA e pode ser atribuído ao aumento no tamanho dos domínios da fase dispersa de EVA.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro de Ciências e Tecnologia - CCTpt_BR
dc.publisher.programPÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAISpt_BR
dc.publisher.initialsUFCGpt_BR
dc.subject.cnpqEngenharia de Materiaispt_BR
dc.titleEfeito do copolímero de EVA contendo diferentes teores de VA nas propriedades de blendas de biopolietileno/EVA.pt_BR
dc.date.issued2019-05-23-
dc.description.abstractThe effect of EVA concentration and of VA content of EVA on the mechanical, morphological and rheological properties of bio-based high density polyethylene/ethylene vinyl acetate (BioPE/EVA) blends was investigated. The blends were characterized by X-Ray Diffraction (XRD), Differential Scanning Calorimetry, Scanning Electron Microscopy (SEM), and rheological measurements under oscillatory shear flow. The degree of crystallinity of BioPE decreased with the increase in the EVA concentration and was unaffected with the increase in the VA content. DMTA results showed a decrease in the storage modulus (E’) with the increase in EVA content and that the BioPE/EVA19 blends showed higher E’ values than BioPE/EVA28 blend. The impact strength substantially increased with the addition of EVA concentration above 5% and was higher for the blends containing the highest VA content. The blends containing a higher content of VA exhibited the higher EVA dispersed phase domains size, which increased with the increase in EVA concentration. The complex viscosity increased with the increase in the EVA content, being higher for the BioPE/EVA blends containing higher VA content. The storage modulus increased, at low frequencies, with the increase in the EVA content and can be ascribed to the increase in the EVA dispersed phase domains size.pt_BR
dc.identifier.urihttp://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35747-
dc.date.accessioned2024-05-22T11:36:28Z-
dc.date.available2024-05-22-
dc.date.available2024-05-22T11:36:28Z-
dc.typeTesept_BR
dc.subjectBlendaspt_BR
dc.subjectBioPEpt_BR
dc.subjectEVApt_BR
dc.subjectPolímerospt_BR
dc.subjectBlendspt_BR
dc.subjectPolymerspt_BR
dc.subjectMezclaspt_BR
dc.rightsAcesso Abertopt_BR
dc.creatorFARIAS, Giselly Marilaide Galdino.-
dc.publisherUniversidade Federal de Campina Grandept_BR
dc.languageporpt_BR
dc.title.alternativeEffect of EVA copolymer containing different VA contents on properties of biopolyethylene/EVA blends.pt_BR
dc.title.alternativeEfecto del copolímero EVA que contiene diferentes contenidos de VA en Propiedades de las mezclas de biopolietileno/EVA.pt_BR
dc.identifier.citationFARIAS, Giselly Marilaide Galdino.Efeito do copolímero de EVA contendo diferentes teores de VA nas propriedades de blendas de iopolietileno/EVA. 2019. 111 fl. Tese (Doutorado em Ciência e Engenharia de Materiais) – Programa de Pós- Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2019. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/35747pt_BR
dc.description.resumenEn este trabajo, el efecto de la concentración de EVA y el contenido de VA de EVA sobre las propiedades mecánicas, morfológicas y reológicas de mezclas de aceites. polietileno de alta densidad de fuente renovable y copolímero de etileno acetato de vinilo (BioPE/EVA). Las mezclas se caracterizaron por difracción. Rayos X (DRX), Calorimetría Diferencial de Barrido, Microscopía Electrónica de escaneo (SEM) y mediciones reológicas bajo flujo cortante. oscilatorio. El grado de cristalinidad de BioPE disminuyó al aumentar concentración de EVA y no se vio afectada por el aumento en el contenido de VA. Tú Los resultados de DMTA mostraron una disminución en el módulo de almacenamiento. (E ') con el aumento del contenido de EVA y que las mezclas BioPE/EVA19 presentó valores de E' más altos que las mezclas BioPE/EVA28. A La resistencia al impacto aumentó sustancialmente con la adición de concentración de EVA superior al 5% y fue mayor para las mezclas que contienen el mayor contenido de VA. Las mezclas que contenían mayor contenido de VA exhibieron mayor tamaño de los dominios de fase dispersa de EVA, que con el aumento Concentración de EVA. La viscosidad compleja aumentó al aumentar Contenido de EVA, siendo mayor para las mezclas de BioPE/EVA que contienen mayor contenido de VA. Módulo de almacenamiento aumentado, en nivel bajo. frecuencias, con el aumento del contenido de EVA y se puede atribuir a la aumento en el tamaño de los dominios de fase dispersa de EVA.pt_BR
Appears in Collections:Doutorado em Ciência e Engenharia de Materiais.

Files in This Item:
File Description SizeFormat 
GISELLY MARILAIDE GALDINO FARIAS - TESE PPG-CEMat 2019.pdfGiselly Marilaide Galdino Farias - Tese PPG-CEMat 20192.43 MBAdobe PDFView/Open
Show simple item record


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.