Please use this identifier to cite or link to this item:
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7324
Full metadata record
DC Field | Value | Language |
---|---|---|
dc.creator.ID | CARRASCO, J. A. P. | pt_BR |
dc.creator.Lattes | http://lattes.cnpq.br/9085140310628380 | pt_BR |
dc.contributor.advisor1 | SILVA, Antonio Almeida. | - |
dc.contributor.advisor1ID | SILVA, A. A. | pt_BR |
dc.contributor.advisor1Lattes | http://lattes.cnpq.br/8361717016612632 | pt_BR |
dc.contributor.advisor2 | SANTOS, Neilor Cesar dos. | - |
dc.contributor.advisor2ID | SANTOS, N. C. | - |
dc.contributor.advisor2Lattes | http://lattes.cnpq.br/4049499502347220 | - |
dc.contributor.referee1 | SANTOS, Marco Antonio dos. | - |
dc.contributor.referee2 | BARBOSA, José Maria Andrade. | - |
dc.description.resumo | Foi implementado um modelo computacional consistente, baseado na Mecânica da Fratura Linear Elástica e na Mecânica do Dano Continuo, para simular o problema da propagação de uma trinca submetida a um esforço mecânico e ao efeito da degradação provocada pela difusão do hidrogênio na estrutura cristalina de um ago de alta resistência. Na implementação dos modelos para o calculo do fator de intensidade de tensões no material hidrogenado e na simulação do crescimento e propagação de trincas, foram utilizados o Método dos Elementos Finitos e o Método de Runge-Kutta de quarta ordem, respectivamente. Os resultados obtidos nas simulações confirmaram a influencia da presença do hidrogênio na variação do fator de intensidade de tensões quando e considerado o seu efeito sobre os módulos elásticos do material. Do mesmo modo, a partir da aplicação do modelo de dano, foi observada a influencia da presença do hidrogênio na diminuição do tempo de início e propagação de trincas. | pt_BR |
dc.publisher.country | Brasil | pt_BR |
dc.publisher.department | Centro de Ciências e Tecnologia - CCT | pt_BR |
dc.publisher.program | PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS | pt_BR |
dc.publisher.initials | UFCG | pt_BR |
dc.subject.cnpq | Engenharia de Materiais | - |
dc.title | Aplicação de modelos de fratura elástica e de dano para a simulação numérica da influência do hidrogênio na propagação de trincas em aços de alta resistência. | pt_BR |
dc.date.issued | 2008-02-29 | - |
dc.description.abstract | A consistent computational model based on Elastic Linear Fracture Mechanics and Continuous Damage Mechanics was implemented to simulate the problem of crack propagation under mechanical stress and the effect of degradation caused by hydrogen diffusion in the crystal structure of a ago high strength. In the implementation of the models for the calculation of the stress intensity factor in the hydrogenated material and in the simulation of crack growth and propagation, the Finite Element Method and the Runge-Kutta Method were used. fourth order respectively. The results obtained in the simulations confirmed the influence of the presence of hydrogen on the stress intensity factor variation when considering its effect on the elastic modulus of the material. Likewise, from the application of the damage model, it was observed the influence of the presence of hydrogen in the reduction of crack initiation and propagation time. | pt_BR |
dc.identifier.uri | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7324 | - |
dc.date.accessioned | 2019-09-25T19:11:10Z | - |
dc.date.available | 2019-09-25 | - |
dc.date.available | 2019-09-25T19:11:10Z | - |
dc.type | Dissertação | pt_BR |
dc.subject | Mecânica - Fratura. | - |
dc.subject | Fragilização. | - |
dc.subject | Método dos Elementos Finitos. | - |
dc.subject | Método de Runge-Kutta de Quarta Ordem. | - |
dc.subject | Mecânica da Fratura Linear Elástica. | - |
dc.subject | Mecânica do Dano Contínuo. | - |
dc.subject | Mechanics - Fracture. | - |
dc.subject | Fragility. | - |
dc.subject | Finite Element Method. | - |
dc.subject | Fourth Order Runge-Kutta Method. | - |
dc.subject | Mechanics of Elastic Linear Fracture. | - |
dc.subject | Mechanics of Continuous Damage. | - |
dc.rights | Acesso Aberto | pt_BR |
dc.creator | CARRASCO, Jorge Antonio Palma. | - |
dc.publisher | Universidade Federal de Campina Grande | pt_BR |
dc.language | por | pt_BR |
dc.title.alternative | Application of elastic fracture and damage models for the numerical simulation of the influence of hydrogen on crack propagation in high strength steels. | pt_BR |
dc.identifier.citation | CARRASCO, Jorge Antonio Palma. Aplicação de modelos de fratura elástica e de dano para a simulação numérica da influência do hidrogênio na propagação de trincas em aços de alta resistência. 2008. 134f. (Dissertação) Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Campina Grande - Paraíba - Brasil, 2008. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7324 | pt_BR |
Appears in Collections: | Mestrado em Ciência e Engenharia de Materiais. |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
JORGE ANTONIO PALMA CARRASCO - DISSERTAÇÃO PPG-CEMat 2008.pdf | Jorge Antonio Palma Carrasco - Dissertação PPG-CEMat 2008 | 13.09 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.