Title: Uso de extensor de cadeia visando a modificação da estrutura molecular do PET.
Other Titles: Use of chain extender to modify the molecular structure of PET.
???metadata.dc.creator???: DUARTE, Izarelle da Silva.
???metadata.dc.contributor.advisor1???: SILVA, Suédina Maria de Lima.
???metadata.dc.contributor.advisor2???: CANEDO, Eduardo Luis.
???metadata.dc.contributor.referee1???: ANDRADE, Daniela de Lourdes Anjos Coutinho Simões.
???metadata.dc.contributor.referee2???: CAVALCANTI, Wilma Sales.
Keywords: Polímeros;PET;Extensor de Cadeia;Massa Molar;Viscosidade Intrínseca;Reciclagem de PET;Processos de Degradação do PET;Polymers;Chain Extender;Molar Mass;Intrinsic Viscosity;PET Recycling;PET Degradation Processes
Issue Date: 28-Jun-2013
Publisher: Universidade Federal de Campina Grande
Citation: DUARTE, Izarelle da Silva. Uso de extensor de cadeia visando a modificação da estrutura molecular do PET. 2013.74f. (Dissertação) Mestrado em Ciência e Engenharia de Materiais, Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7327
???metadata.dc.description.resumo???: Neste estudo, os polímeros poli(tereftalato de etileno) virgem (PET-V) e pós-consumo (PET-PC) foram aditivados com um oligômero multifuncional estirenico-acrílico-epóxi (Joncryl - POLYAD PR 002), comercializado como extensor de cadeia para polímeros de condensação como o PET, visando compensar a redução da massa molar destes polímeros durante o processamento. O PET-V e PET-PC nao aditivados e aditivados com o extensor de cadeia foram processados em misturador interno Haake, com rotores tipo roller. A influencia da velocidade dos rotores, do teor de extensor de cadeia e do reprocessamento do PET aditivado na viscosidade e massa molar dos referidos polímeros foi avaliada com base nas medidas de torque e de viscosidade intrínseca. A aditivação do PET-V e do PET-PC resultou no aumento da viscosidade e da massa molar destes polímeros, sendo os maiores valores obtidos quando os mesmos foram processados a 60 rpm e na presença de 1,5 % do extensor de cadeia. O reprocessamento do PET-V aditivado com 1,5% do extensor de cadeia resultou na diminuição do torque e da viscosidade do material. Entretanto, os valores de massa molar foram superiores ao do PET-V processado sem aditivo, sugerindo que o aditivo não gerou subprodutos que poderiam catalisar a degradação do polímero no reprocessamento. Alem disso, quando a mesma quantidade do aditivo (1,5%) foi adicionada ao material reprocessado, a viscosidade e a massa molar do polímero voltaram a aumentar, atingindo patamares próximos ao do polímero aditivado e processado uma unica vez. Isto indica que o extensor de cadeia foi eficiente em compensar a redução da massa molar do PET durante o processamento e o reprocessamento. Os valores de massa molar estimados a partir dos dados de processamento foram confirmados experimentalmente, indicando que a análise da curva torque-tempo no misturador interno e uma ferramenta rápida e precisa para avaliar a eficiência da extensão de cadeia do PET processado e reprocessado.
Abstract: This work is concerned with the effect of a multifunctional styrenicacrylic- epoxi oligomer (Joncryl - POLYAD PR 002) - marked as a chain extender for condensation polymers - on the molar mass of poly(ethylene terephthalate), in virgin (PET-V) and post-consumer recycled (PET-PC) forms. The purpose of incorporation of additive is to compensate the loss of molar mass of these polymers during processing due to degradation. The PET-V and PET-PC, neat and with the chain extender added, were compounded in a Haake Rheomix 3000 internal mixer, fitted with high intensity rotors. The effect of rotor speed, additive concentration, and reprocessing on the viscosity and molar mass of the polymers was estimated from torque measured during processing and from intrinsic viscosity measured after processing. The addition of chain extender resulted in the increase of viscosity and molar mass, the largest values obtained for resins processed at 60 rpm with 1.5% additive. Reprocessing PET-V with 1.5% additive resulted in a drop of torque and viscosity, but the molar mass of the reprocessed material was superior to the PET-V compounded without chain extender, suggesting that the additive did not generate byproducts that may degrade the polymer on further processing. Moreover, when 1.5% chain extender were added to the reprocessed material, viscosity and molar mass increased again, reaching values close to the ones obtained for the polymer reprocessed once with the additive. The result showed that the chain extender tested compensated the loss o molar mass, not only during processing, but on reprocessing too. The molar mass values estimated from the data processing were confirmed experimentally, indicating that the analysis of the torque-time curve in the internal mixer is a fast and accurate tool for evaluating the efficiency of chain extension of PET processed and reprocessed.
Keywords: Polímeros
PET
Extensor de Cadeia
Massa Molar
Viscosidade Intrínseca
Reciclagem de PET
Processos de Degradação do PET
Polymers
Chain Extender
Molar Mass
Intrinsic Viscosity
PET Recycling
PET Degradation Processes
???metadata.dc.subject.cnpq???: Engenharia de Materiais
URI: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7327
Appears in Collections:Mestrado em Ciência e Engenharia de Materiais.

Files in This Item:
File Description SizeFormat 
IZARELLE DA SILVA DUARTE - DISSERTAÇÃO PPG-CEMat CCT 2013.pdfIzarelle da Silva Duarte - Dissertação PPG-CEMat CCT 2013.7.47 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.