Please use this identifier to cite or link to this item:
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7898
Title: | Nanocompósitos PP/argila. Influência do tipo e do teor de silicato em camadas. |
Other Titles: | PP / clay nanocomposites. Influence of type and silicate content in layers. |
???metadata.dc.creator???: | ARAÚJO, Sueila Silva. |
???metadata.dc.contributor.advisor1???: | SILVA, Suédina Maria de Lima. |
???metadata.dc.contributor.advisor2???: | RAPOSO, Claudia Maria de Oliveira. |
???metadata.dc.contributor.referee1???: | CANEDO, Eduardo Luis. |
???metadata.dc.contributor.referee2???: | MALTA, Oscar Manoel Loureiro. |
Keywords: | Nanocompósitos;Polipropileno;Bentonita;Argilas;Argila Organofílica;Argila Bentonítica;Raios x (DRX);Nanocomposites;Polypropylene;Bentonite;Clays;Organophilic Clay;Bentonitic Clay;X-Rays (XRD) |
Issue Date: | 28-Feb-2008 |
Publisher: | Universidade Federal de Campina Grande |
Citation: | ARAÚJO, Sueila Silva. Nanocompósitos PP/argila. Influência do tipo e do teor de silicato em camadas. 2008. 110f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2008. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7898 |
???metadata.dc.description.resumo???: | Neste estudo, nanocompósitos polipropileno/argila foram preparados pelo método de intercalação por fusão. Na primeira etapa da pesquisa, uma argila bentonítica, fornecida pela Bentonit União Nordeste, Campina Grande, PB, foi submetida a um tratamento químico de purificação visando a remoção de matéria orgânica. As bentonitas, não purificada e purificada foram modificadas com o sal orgânico brometo de cetil trimetil amônio. Como parâmetro de comparação utilizou-se uma argila organofílica comercial Closite 20A, fornecida pela Southern Clay Products, Gonzales, Texas (EUA). As bentonitas foram caracterizadas por espectroscopia no infravermelho (FTIR) e difração de raios-X (DRX). Os resultados mostraram que o tratamento de purificação e organofilização foram bem sucedidos. Os nanocompositos, PP/argila, contendo 1, 3 e 5 % em massa de argila organofílica, foram preparados em extrusora dupla rosca contra-rotativa acoplada ao reômetro de torque Haake e corpos de prova, empregados na caracterização mecânica e termomecânica dos nanocompósitos, foram moldados por injeção. A morfologia dos nanocompositos foi avaliada por DRX. Medidas de resistência ao impacto, dureza e temperatura de reflexão térmica também foram realizadas. Os resultados mostraram que o tipo e teor de argila influenciaram consideravelmente na morfologia e propriedades dos nanocompósitos. De forma geral, as melhores propriedades estudadas foram exibidas pelos nanocompósitos contendo 1% em massa de argila organofílica. Os nanocompósitos preparados com argila organofílica purificada, sintetizada neste estudo, mostraram propriedades semelhantes as dos nanocompósitos preparados com argila organofílica comercial. |
Abstract: | Polypropylene (PP) and clay nanocomposites were prepared by the melt intercalation process. Bentonite clay, provided by Bentonit Uniao Nordeste, of Campina Grande, Paraiba (Brazil), was subject to a chemical purification treatment in order to remove organic matter impurities. Raw and purified clays were then modified with the organic salt cetyl trimethyl ammonium bromide. Clays samples were characterized by infrared spectroscopy and x-ray diffraction. Results showed that the purification and organofilization treatments were successful. As a comparative, tests were also performed with a commercial organoclay (Closite 20A) provided by Southern Clay Products, Gonzales, Texas (USA). PP/bentonite nanocomposites with 1, 3 and 5 % organoclay loading (by weight) were prepared in a counter-rotating twin-screw extruder coupled to a Haake rheometer. Test specimens were injection-molded for mechanical and thermal characterization. The composites morphology was evaluated by x-ray diffraction. Hardness, impact, and heat deflection tests were also performed. Then results showed that the type and amount of clay greatly affect the morphology and mechanical properties of the composite. In general, better results were obtained with 1% organofilic clay. Nanocomposites prepared with the bentonite purified and organofilized in this study showed properties similar to those prepared with the commercial organoclay tested. |
Keywords: | Nanocompósitos Polipropileno Bentonita Argilas Argila Organofílica Argila Bentonítica Raios x (DRX) Nanocomposites Polypropylene Bentonite Clays Organophilic Clay Bentonitic Clay X-Rays (XRD) |
URI: | http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/7898 |
Appears in Collections: | Mestrado em Ciência e Engenharia de Materiais. |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
SUEILA SILVA ARAÚJO - DISSERTAÇÃO PPG-CEMat 2008.pdf | Sueila Silva Araújo - Dissertação PPG-CEMat 2008. | 7.79 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.