dc.description.resumo |
Neste trabalho foi estudado a influencia do oxido de titânio nas propriedades microestruturais e elétricas do sistema varistor (ZnO.Bi2O3.MnO2.C03O4) sinterizado a 1150°C, 1200°C e 1250°C durante 1 h. A caracterização elétrica foi feita através de medidas de densidade de corrente em função do campo elétrico
aplicado. Por outro lado, as caracterizações microestrutural e de fases cerâmicas foram obtidas através de microscopia eletrônica de varredura e difração de raios-X. O sistema varistor com 1,0% em mol de T i 0 2 e sinterizado a 1150°C apresentou melhores propriedades elétricas. A melhoria das propriedades elétricas está relacionada com as mudanças microestruturais ocorridas com a adição do TiO2 . Para os sistemas sinterizados a 1200 e 1250°C foi observado uma queda nas características elétricas. A presença de poros e tamanhos de grão heterogêneos, provavelmente afetaram as propriedades varistoras. Foi observado a formação da fase Zn2Ti04 quando ao sistema sinterizado a 1200°C e 1250°C foram adicionados 0,7 e 1,0 mol% de Ti02 . Esta fase pode ter comprometido as características elétricas e microestruturais das amostras, sendo evidenciada pela função condutora. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Química |
|
dc.title |
Estudo do efeito do óxido de titânio nas propriedades microestruturais e elétricas de varistores à base de ZnO. |
pt_BR |
dc.date.issued |
1993-02 |
|
dc.description.abstract |
In this work the titanium oxide influence on the electrical properties of
varistor system (ZnO.Bi2O3.MnO2.C03O4) was studied. This system was sinterized at 1150°C, 1200°C and 1250°C during 1 hour. The electrical characterization was made by measurements of current density versus applied electrical field. On the other hand, the microstructural and ceramic phases characterizations were made by scanning eletronic microscopy and X-ray pattern observations. The varistor system containing 1,0% mol of T i 0 2 and sinterized
at 1150°C showed the best electrical properties. The enhancement electrical properties is due to microstructural change caused by T i 0 2 addition. It was observed a decreased electrical properties in the systems sinterized at 1200°C and 1250°C. Microvoides and heterogeneous grains dimensions probably has negative influence on the varistor properties. The Zn2Ti04 phase formation was observed
when to the system sinterized at 1200°C and 1250°C were additioned 0,7 e 1,0% mol of T i 0 2 . This phase that is conductor, may be affect negatively the electrical and microstructural characteristics of the samples. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10145 |
|
dc.date.accessioned |
2019-12-12T12:01:20Z |
|
dc.date.available |
2019-12-12 |
|
dc.date.available |
2019-12-12T12:01:20Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Materiais Não-metálicos |
|
dc.subject |
Metalografia |
|
dc.subject |
Óxido de Titânio |
|
dc.subject |
Varistores |
|
dc.subject |
Non-metallic Materials |
|
dc.subject |
Metallography |
|
dc.subject |
Titanium Oxide |
|
dc.subject |
Varistors |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SANTANA, Lisiane Navarro de Lima. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Study of the effect of titanium oxide on the microstructural and electrical properties of ZnO based varistors. |
pt_BR |
dc.identifier.citation |
SANTANA, Lisiane Navarro de Lima. Estudo do efeito do óxido de titânio nas propriedades microestruturais e elétricas de varistores à base de ZnO. 1993. 92f. (Dissertação) Mestrado em Engenharia Química, Curso de Mestrado em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba - Campus II Campina Grande - Paraíba - Brasil, 1993. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10145 |
pt_BR |