Estudo dos processos de solidificação rápida melt-spinning e inrowasp na amorfização de ligas à base de ferro.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA
→
Mestrado em Engenharia Mecânica.
→
Ver item

dc.creator.ID	NÓBREGA NETO, S. C.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/6390203344658131	pt_BR
dc.contributor.advisor1	LIMA, Severino Jackson Guedes de.
dc.contributor.advisor1ID	LIMA, S. J. G.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/1045652409149134	pt_BR
dc.contributor.referee1	MACIEL, Theophilo Moura.
dc.contributor.referee2	KLEIN, Aloisio Nelmo.
dc.contributor.referee3	MELO, Tadeu Antonio de A.
dc.description.resumo	Os processos de Solidificação rápida Melt-Spinning e Inrowasp (In Rotating Water Spinning Process) foram utilizados para a obtenção de ligas com estruturas amorfas nas formas de fitas e fios, nas composições Fe7sSiio(Bi.xCx)i5 em porcentagem atômica, com x variando de 0 a 0,8, numa razão de 0,2. As fitas obtidas como produto resultante do processo Melt-Spinning, foram submetidas a ensaios de caracterização estrutural atraves da Difração de Raios-X e a ensaios de Análise Térmica Diferencial (DTA) para estudo da sua estabilidade térmica. Os fios obtidos do processo Inrowasp, foram ensaiados através de teste de dobramento a 180°, que serviu como um teste tipo "passa-não-passa" e, desta forma, avaliou-se a ductilidade do fio. Através do processo Melt-Spinning, obteve-se fitas dúcteis em 38,89 % de um total de 36 experimentos, enquanto que o processo Inrowasp apresentou fios dúcteis em apenas 11,76 % para um total de 85 experimentos.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Mecânica
dc.title	Estudo dos processos de solidificação rápida melt-spinning e inrowasp na amorfização de ligas à base de ferro.	pt_BR
dc.date.issued	1995-09
dc.description.abstract	The process of rapid solidification Melt-Spinning and Inrowasp (In Rotating Water Spinning Process) were used in obtaining alloys with amorphous structures in ribbon and wire shapes in the follow compositions on atomic content Fe75Siio(Bi.xCx)i5 with the x varying from 0 to 0,8, by a rate of 0,2. The ribbons obtaneid as a resulting product from the Melt-Spinning process, were structurely characterized by X-Ray Difraction and Diferencial Thermal Analysis (DTA) in order to study the thermal stability. The wires obtaneid from Inrowasp process, were tested by the 180° bending test, which was used as a selective type test, characterizing the wire ductility. Using the Melt-Spinning process, it was possible to obtain 38,89% of ductile ribbons within a total number of 36 tests, while the inrowasp process revealed ductile wires only in 11,76% within a total number of 85 tests.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10174
dc.date.accessioned	2019-12-13T11:05:58Z
dc.date.available	2019-12-13
dc.date.available	2019-12-13T11:05:58Z
dc.type	Dissertação	pt_BR
dc.subject	Solidificação - Processos
dc.subject	Melt-Spinning - Solidificação Rápida
dc.subject	Processo Inrowasp
dc.subject	Fitas Dúcteis
dc.subject	Difração de Raios-X
dc.subject	Análise Térmica Diferencial (DTA)
dc.subject	Estabilidade Térmica
dc.subject	Ligas à Base de Ferro
dc.subject	Solidification - Processes
dc.subject	Melt-Spinning - Fast Solidification
dc.subject	Inrowasp Process
dc.subject	Ductile Tapes
dc.subject	X-ray Diffraction
dc.subject	Differential Thermal Analysis (DTA)
dc.subject	Thermal Stability
dc.subject	Iron-based Alloys
dc.rights	Acesso Aberto	pt_BR
dc.creator	NÓBREGA NETO, Severino Cesarino da.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Study of melt-spinning and inrowasp rapid solidification processes in the amorphization of iron-based alloys.	pt_BR
dc.identifier.citation	NÓBREGA NETO, Severino Cesarino da. Estudo dos processos de solidificação rápida melt-spinning e inrowasp na amorfização de ligas à base de ferro. 1995. 105f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 1995. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10174	pt_BR