dc.creator.ID |
SILVA, F.M.N. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/5927253994526787 |
pt_BR |
dc.contributor.advisor1 |
CARVALHO, Maria Wilma Nunes. |
|
dc.contributor.advisor1ID |
CARVALHO, M. W. N. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/0908368865763328 |
pt_BR |
dc.contributor.referee1 |
CABRAL, Rucilana Patrícia Bezerra. |
|
dc.contributor.referee2 |
SILVA, Maristela Alves da. |
|
dc.contributor.referee3 |
PEREIRA, Kleberson Ricardo de Oliveira. |
|
dc.description.resumo |
A industria petrolífera busca cada vez mais materiais que convertam
hidrocarbonetos pesados em leves os quais apresentam um maior valor agregado.
O crescente rigor das legislações ambientais, a pressão social por combustíveis com
melhor desempenho e a necessidade da utilização do óleo cru cada vez mais
pesado e com alto teor de nitrogenados, tem gerado uma grande demanda para o
desenvolvimento de catalisadores de hidrorrefino. Um exemplo de catalisadores
promissores são os materiais ácidos mesoporosos devido a sua vasta aplicação
como suportes para catalisadores sólidos em processos químicos industriais,
despertando um maior interesse em muitos pesquisadores, impulsionando cada vez
mais a pesquisa nesta área. A peneira molecular mesoporosa, AI-MCM-41 e um
suporte para catalisador interessante por apresentar alta estabilidade térmica e
hidrotérmica, alta área superficial, elevados diâmetros de poros o que fornece
possibilidades para o preparo de catalisadores que possuam elevada capacidade de
dispersão de metais NiMo em AI-MCM-41. Outro suporte mesoporoso interessante a
catalise e a sílica mesoporosa SBA-15 que vem sendo amplamente estudada,
principalmente em função de suas características: estável termicamente, química e
mecanicamente, alem de sua capacidade de adsorver cations metálicos, permitindo
sua utilização como suporte de metais para catalisadores. Desta forma, o objetivo
deste trabalho foi sintetizar e caracterizar o suporte MCM-41 com adição de alumínio
(AI-MCM-41) e os catalisadores NiMo suportados. O suporte AI-MCM-41 foi
sintetizado com razão Si/AI = 31,9 através do método hidrotérmico a 150°C por 12
horas e caracterizados por DRX, EDX, FTIR, MEV, TG. Neste trabalho foi utilizada
uma amostra de SBA-15, como suporte para catalisadores NiMo, previamente
sintetizada e cedida ao LabCAB por pesquisadores da PUC-RJ. Os catalisadores
foram sintetizados pelo método de impregnação via úmida e dispersão física em
concentrações de 4 e 8% em massa de Mo03 e 2% em massa de NiO e foram
caracterizados por DRX, EDX, FTIR e MEV. Os resultados obtidos a partir das
caracterizações indicaram que a fase hexagonal da AI-MCM-41 foi obtida, apos
calcinação do material houve um aumento característico na ordenação hexagonal
desse material. Ocorreu uma redução na ordenação da fase hexagonal apos a
impregnação dos óxidos Mo03 e NiO, mantendo-se ainda sua fase hexagonal de
peneira molecular mesoporosa. A dispersão via úmida sobre AI-MCM-41 mostrou-se
mais eficiente quando se dispersa um teor menor de Mo03 e a dispersão física
quando aumentou-se o teor do Mo03 . A partir da analise termogravimétrica foi
possível averiguar uma boa estabilidade térmica para ambos os suportes AI-MCM-41
e SBA-15. Com as analises de DRX para o suporte SBA-15, constatou-se uma boa
organização hexagonal mesoporosa, seguida da redução hexagonal apos a
impregnação dos óxidos Mo03 e NiO. Para os dois tipos de impregnação dos óxidos
sobre SBA-15 verificou-se a presença das fases cristalinas de molibdênio e níquel. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Química. |
|
dc.title |
Impregnação dos óxidos MoO3/NiO por dispersão física e via úmida sobre Al-MCM-41 e SBA-15. |
pt_BR |
dc.date.issued |
2013-06 |
|
dc.description.abstract |
The oil industry increasingly seeks materials that convert heavy hydrocarbons to light
which have a higher added value. The strict environmental laws, the social pressure
for fuel with better performance and the need for use of crude oil more and more
heavy and with high nitrogen content, have generated a great demand for the
development of hydrorefining catalysts. An example of promising catalysts is acidic
mesoporous material because of its wide application as support for solid catalysts in
industrial chemical process, raising a greater interest in many researchers driving
research in this area. The mesoporous molecular sieve, AI-MCM-41 is an interesting
catalyst support due to high thermal and hydrothermal stability, high surface area,
high pore diameters which provide possibilities for the preparation of catalysts that
have high dispersion metal NiMo on AI-MCM-41. Another interesting mesoporous
support in catalysis is the mesoporous silica SBA-15, it has been widely studied,
mainly due to its characteristics: thermal, chemical and mechanics stable, in addition
to its ability to adsorb metal cations, allowing its use as support for metal catalysts.
Thus, the aim of this work was to synthesize and characterize the support MCM-41
with the addition of aluminum (AI-MCM-41) and NiMo catalysts supported. The
support AI-MCM-41 was synthesized with ratio Si/AI= 31,9 through the hydrothermal
method at 150°C for 12 hours and characterized by XRD, EDX, FTIR, MEV and TG.
In this work was used a sample of SBA-15 as support for NiMo catalysts previously
synthesized and ceded to LabCAB by researchers from PUC-RJ. The catalysts were
synthesized by the wet impregnation method and physical dispersion at
concentrations of 4 and 8 wt% Mo03 and 2 wt% NiO and were characterized by
XRD, EDX, FTIR and MEV. The results obtained from the characterization indicated
that the hexagonal phase of the AI-MCM-41 were obtained, after calcination of the
material there as an increase in the characteristic hexagonal ordering of the material.
There was a reduction in the hexagonal phase ordering after impregnation of the
oxides NiO and Mo03, still remain its hexagonal phase of mesoporous molecular
sieve. The wet dispersion on AI-MCM-41 was more efficient when dispersed a lower
Mo03 content and the physical dispersion when the content of Mo03 was increased.
From the thermal analysis it was possible verify good thermal stability for both of
supports, AI-MCM-41 and SBA-15. With the XRD for SBA-15 support, it was found
good organization hexagonal mesoporous followed by hexagonal reduction after
impregnation of the oxides NiO and Mo03. For both types of impregnation of the
oxides on SBA-15 was found the presence of crystalline phases of molybdenum and
niquel. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10244 |
|
dc.date.accessioned |
2019-12-17T11:56:28Z |
|
dc.date.available |
2019-12-17 |
|
dc.date.available |
2019-12-17T11:56:28Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Óxidos - Impregnação. |
|
dc.subject |
Peneira Molecular Mesoporosa. |
|
dc.subject |
Catalisador. |
|
dc.subject |
Óxido de Molibdênio. |
|
dc.subject |
Fase Hexagonal. |
|
dc.subject |
Impregnação - Método. |
|
dc.subject |
Catalisadores Sólidos. |
|
dc.subject |
Processos Químicos Industriais. |
|
dc.subject |
Oxides - Impregnation. |
|
dc.subject |
Mesoporous Molecular Sieve. |
|
dc.subject |
Catalyst. |
|
dc.subject |
Molybdenum oxide. |
|
dc.subject |
Hexagonal phase. |
|
dc.subject |
Impregnation - Method. |
|
dc.subject |
Solid Catalysts. |
|
dc.subject |
Industrial Chemical Processes. |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SILVA, Fabiana Medeiros do Nascimento. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
MoO3 / NiO oxides impregnation by physical and wet dispersion on Al-MCM-41 and SBA-15. |
pt_BR |
dc.identifier.citation |
SILVA, Fabiana Medeiros do Nascimento. Impregnação dos óxidos MoO3/NiO por dispersão física e via úmida sobre Al-MCM-41 e SBA-15. 2013. 114f. (Dissertação de Mestrado em Engenharia Química), Programa de Pós-graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10244 |
pt_BR |