Cinética de corrosão e caracterização microestrutural de materiais à base de ligas de NiTi para aplicação em stents cardiovasculares.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA
→
Mestrado em Engenharia Química
→
Ver item

dc.creator.ID	OLIVEIRA, C. E. S.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/3749089263890866	pt_BR
dc.contributor.advisor1	VILAR, Eudésio Oliveira.
dc.contributor.advisor1ID	VILAR, E. O.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/6363257813968241	pt_BR
dc.contributor.referee1	ALVES, José Jailson Nicácio.
dc.contributor.referee2	ARAÚJO, Carlos José de.
dc.contributor.referee3	BRASILEIRO, Ilza Maria do Nascimento.
dc.description.resumo	A utilização de ligas de NiTi tratadas superficialmente, permite combinar as características da liga metálica em estudo com as características do revestimento a ser formado na superfície do material base. Neste trabalho foram estudadas a cinética de corrosão e as características encontradas em cada liga de NiTi com composição diferenciada para uma melhor abordagem do problema, analisando não apenas as superfícies tratadas superficialmente, como também aquelas que não sofreram nenhuma modificação. Com isso, o comportamento eletroquímico das ligas metálicas de NiTi foi verificado em um meio que se assemelha bastante as condições corpóreas. A partir de ensaios eletroquímicos, foi possível a comparação dos resultados obtidos entre as ligas metálicas em estudo. Alem dos métodos eletroquímicos empregados no estudo da resistência a corrosão das ligas metálicas de NiTi, também foram utilizadas métodos de analises na quantificação das modificações superficiais oriundas dos tratamentos empregados. Foi observado ao longo deste trabalho a resistência que os materiais a base de nitinol possuem, quando submetidos a teste em solução de Hank's que se assemelha bastante ao sangue, como também utilizando uma temperatura em torno de 37 °C que e normalmente a temperatura encontrada no corpo humano e constata-se uma boa durabilidade do material. Os testes utilizados na analise das modificações ocorridas na superfície das amostras revelaram as mudanças causadas quando a superfície passa por irradiações por feixe de laser de acordo com cada composição da liga e os possíveis danos que isso pode acarretar no processo de degradação do material.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Química.
dc.title	Cinética de corrosão e caracterização microestrutural de materiais à base de ligas de NiTi para aplicação em stents cardiovasculares.	pt_BR
dc.date.issued	2012-08-23
dc.description.abstract	The use of NiTi alloys surface treated, allows to combine the characteristics of the alloy in a study of the characteristics of the coating to be formed on the surface of the base material. In this study the kinetics of corrosion and features found in each NiTi alloy with different composition to better approach the problem by analyzing not only superficially treated surfaces, as well as those who experienced no change. Therefore, the electrochemical behavior of NiTi alloys was verified in a way that closely resembles the bodily conditions. From electrochemical tests, it was possible to compare the results between the alloys under study. Besides the methods employed to study the electrochemical corrosion resistance of alloys of NiTi, were also used assay methods in quantification of surface modifications coming from the treatments. It was observed throughout this work the resistance that the material to base nitinol have, when subjected to test in a solution of Hank's that closely resembles the blood, as well as using a temperature around 37 ° C which is normally the temperature found in human body and it is observed a good durability of the material. The tests used in the analysis of the changes occurring on the surface of the samples revealed changes caused when the surface undergoes irradiation by laser beam according to each alloy composition and the possible damage that may result in degradation of the material.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10247
dc.date.accessioned	2019-12-17T12:21:12Z
dc.date.available	2019-12-17
dc.date.available	2019-12-17T12:21:12Z
dc.type	Dissertação	pt_BR
dc.subject	Liga NiTi
dc.subject	Liga Memória de Forma
dc.subject	Cinética Eletroquímica
dc.subject	Biomateriais
dc.subject	Cinética de Corrosão
dc.subject	Stents Cardiovasculares
dc.subject	Emprego de Laser
dc.subject	Corrosão - Materiais Metálicos
dc.subject	NiTi Alloy
dc.subject	Connects Shape Memory
dc.subject	Electrochemical Kinetics
dc.subject	Biomaterials
dc.subject	Corrosion Kinetics
dc.subject	Cardiovascular Stents
dc.subject	Use of Laser.
dc.subject	Corrosion - Metallic Materials
dc.rights	Acesso Aberto	pt_BR
dc.creator	OLIVEIRA, Cláudio Emanuel Silva.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Corrosion kinetics and microstructural characterization of NiTi alloy-based materials for application in cardiovascular stents.	pt_BR
dc.identifier.citation	OLIVEIRA, Cláudio Emanuel Silva. Cinética de corrosão e caracterização microestrutural de materiais a base de ligas de NiTi para aplicação em stents cardiovasculares. 2012. 123f. (Dissertação de Mestrado em Engenharia Química), Programa de Pós-graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2012. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10247	pt_BR