dc.creator.ID |
QUIRINO, A. P. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/0841234251177566 |
pt_BR |
dc.contributor.advisor1 |
CARVALHO, Laura Hecker de. |
|
dc.contributor.advisor1ID |
CARVALHO, L. H. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/6358009621640820 |
pt_BR |
dc.contributor.advisor2 |
QUIRINO, Alberto Porto. |
|
dc.contributor.advisor2ID |
QUIRINO, A. P. |
|
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/0841234251177566 |
|
dc.contributor.referee1 |
ALMEIDA, José Roberto Moraes. |
|
dc.contributor.referee2 |
TOLEDO FILHO, Romildo Dias. |
|
dc.description.resumo |
Neste trabalho investigou-se os efeitos de diferentes formas de
tratamento superficial em cordoes de sisal, utilizados para o desenvolvimento de
compósitos de reforço continuo em matriz poliéster. Os compósitos foram
submetidos a tratamentos de pós-cura e imersão em água e suas propriedades
mecânicas foram determinadas.
Os tratamentos superficiais nos cordoes, em geral, reduziram a
resistência a tração e elevaram o modulo de elasticidade. Nos compósitos, os
tratamentos elevaram os valores de resistência a tração, indicando melhor adesão
interfacial.
A pós-cura, provocou redução nos valores da resistência a tração e
no modulo de elasticidade dos compósitos com reforço tratado. A imersão dos
compósitos em água a 100 °C por 2h, teve efeito semelhante ao do pós-cura,
porem mais drástico. Os tratados com poliol, apresentaram deformação acentuada
não permitindo a realização de ensaios mecânicos.
O comportamento a flexão dos compósitos submetidos a pós-cura
mostrou queda nos valores da resistência, em torno de 30%, exceção feita aos
tratados com poliol, onde verificou-se um pequeno acréscimo nesta propriedade.
Nos ensaios de impacto, verificou-se que, a pós-cura reduziu a
ductilidade dos compósitos, sendo a queda mais acentuada para aqueles com
reforço tratado com uretano. Um comportamento inverso foi verificado com os
compósitos com reforço tratado com poliol, onde foi observado um acréscimo da
energia absorvida. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Mecânica |
|
dc.title |
Cordões de sisal como reforço em compósitos de matriz poliéster. |
pt_BR |
dc.date.issued |
1997-12 |
|
dc.description.abstract |
In this effects of different surface treatments on sisal twines
employed in the development of unidirectional continuous reinforced polyester
composites were investigated. The composites were subjected to both pos-cure
and hot water immersion conditions and their mechanical properties were
determined.
The surface treatments on the sisal twines in general reduced their
tensile strength and increased their elastic moduli. The surface treatments
increased the composite's tensile strength which is taken as an indication of better
interfacial adhesion.
Pos-cure caused a reduction on tensile strength and modulus of the
surface modified reinforced composites. Hot water immersion (100°C for 2h) had a
similar effect on the composite's properties except that, in this case, the changes
were more drastic. Composites surface modified with poliol deformed greatly and
did not allow tensile testing to be performed.
Flexural strength of pos-cured composites suffered a 30% reduction,
except for those modified with poliol where a slight increase in this property was
observed.
Pos-cure also reduced the composite's impact properties and this
effect was more severe for the composites in which reinforcement was surface
modified with urethane. The inverse behaviour was observed with poliol modified
composites. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10350 |
|
dc.date.accessioned |
2019-12-19T12:45:08Z |
|
dc.date.available |
2019-12-19 |
|
dc.date.available |
2019-12-19T12:45:08Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Cordoes de Sisal |
|
dc.subject |
Compósitos |
|
dc.subject |
Matriz Poliéster |
|
dc.subject |
Resistência à Tração |
|
dc.subject |
Módulo de Elasticidade |
|
dc.subject |
Comportamento à Flexão |
|
dc.subject |
Sisal Strings |
|
dc.subject |
Composites |
|
dc.subject |
Polyester Matrix |
|
dc.subject |
Tensile Strength |
|
dc.subject |
Modulus of Elasticity |
|
dc.subject |
Flexion Behavior |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
QUIRINO, Alberto Porto. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Sisal cords as reinforcement in polyester matrix composites. |
pt_BR |
dc.identifier.citation |
QUIRINO, Alberto Porto. Cordões de sisal como reforço em compósitos de matriz poliéster. 1997. 151f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 1997. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10350 |
pt_BR |