Obtenção de híbridos de nanoferrita/SiO2/quitosana para uso em biossensores.

Abstract

In this research was obtained a hybrid material nanoferrit es base Ni0,5Zn0,5Fe2O4 and CoFe2O4 modified the surface with silane agent and functionalized chitosan aiming their use as biosensors. To this end, nanoferritas were synthesized by combustion and silanized with 3-aminopropyltrimethoxysilane. The functionalization was carried out by the solvent evaporation method using the biopolymer chitosan. All samples were characterized by X-ray diffraction, infrared spectroscopy by Fourier transform spectroscopy energy dispersive X-ray, thermal analysis, scanning electron microscopy, transmission electron microscopy, sedimentation test and magnetic separation, magnetic measurements and Analysis by in vitro cytotoxicity. The samples showed synthesized as the formation of spinel single phase with nanometer feature under study and after the formation of the hybrid structure of the material has been maintained. In the infrared spectra there were absorption bands characteristic of nanoferritas and bands related to the presence of the silane agent and chitosan. Through micrographs showed the formation of agglomerates frail and after silanization and functionalization was observed with a morphology more rigid aspect of tightly bound agglomerates of nanoparticles. Thermogravimetric analysis showed that the nanoferritas showed low weight loss and that after hybrid formation was increased mass loss thereby proving the presence of the silane agent and chitosan. As for the magnetic behavior, both nanoferritas had high magnetization typical saturation ferrimagnetic materials, this behavior continued after the hybrid formation is suitable for biotechnological applications. Cell viability nanoferritas showed characteristic for cytotoxic and non-cytotoxic ferrite Ni0,5Zn0,5Fe2O4 to CoFe2O4 ferrite, the formation of hybrid favored increased cell viability in both nanoferritas. The obtained hybrid materials are promising for use in nanobiotechnology as biosensors and / or treatment and clinical diagnosis.