VELOSO, I. T. B. M.; http://lattes.cnpq.br/6335832410995233; VELOSO, Isis Tatiane de Barros Macêdo.
Resumo:
Glass recycling is an alternative to the impact caused by its disposal in environment, contributing to preservation of natural resources, reduction in gas emissions and decrease in volume of landfills and dumps. Glass can be recycled endlessly without any loss of mass or its properties. In addition, stands out for its beauty, for being one of few materials capable of reflecting light, the implementation of which may result in high aesthetic appeal products. This research aims to develop glass pastilles for coatings by recycling process of sodium-calcium glass residues, from heat treatment studies of melting and annealing. Initially, glasses were separated by color, manually grinded, distinguished into different granulometries and conditioned in cellular concrete molds. Then were subjected to different heat treatments, which resulted in melting and annealing, the latter process to minimize the internal tensions that weaken glass. Thus, it sought to analyze the influence of grain size and thermal treatments of visual aspects of the pieces; studies of materials of molds and their interaction with glass, demoldability and finish of the tablets; equipment used for comminution of the glass. As a result, it defined the heat treatment four (TT4) for colorless glass and heat treatment five (TT5) for tinted (blue, amber, light green, dark green) in seeking to obtain pieces of wrinkled texture, glassy and glossy surface. About heat treatment, the analysis performed by optical microscopy showed elimination of internal stresses which weaken the glass, and impact test showed a greater shock resistance for samples annealed, confirming thus its effectiveness. As for viability of production, results showed that pastilles are likely to be made by CAVI group, artisanal scale, using technologies and resources accessible to the group, in a perspective of social technology.