dc.description.resumo |
As espumas de EVA tem sido amplamente usadas, sobretudo em
componentes de calcados, pelas boas propriedades mecânicas aliadas a baixa densidade. Entre as cargas usadas na espuma de EVA, o carbonato de cálcio e o mais empregado, principalmente em função do seu baixo custo e fácil processamento. Entretanto, essa carga também tem influencia nas propriedades físicas das espumas. Os carbonatos de cálcio mais usados são os naturais, seguidos pelos sintéticos, conhecidos como carbonatos precipitados. Estes últimos tem valor elevado e sua escolha ocorre quando se desejam melhores propriedades mecânicas. Neste trabalho, as espumas foram preparadas em prensa quente de laboratório, apos mistura em
misturador intensivo industrial (Banbury) e moinho de rolos. Os compostos foram preparados com dois tipos de carbonato de cálcio precipitado e dois de origem natural, todos cristalinos, com granulometrias entre 1,7 e 8,3 fxm. Os teores de carbonato de cálcio empregados variaram de 5 a 45 per. Foram avaliadas a densidade, dureza e propriedades tênseis das espumas, em condições padronizadas, alem da topografia, através de micrografias obtidas
em microscópio eletrônico de varredura. Os resultados mostraram uma clara correlação da elevação das propriedades analisadas com o aumento do teor dos carbonatos e do tamanho das partículas dos mesmos. Observou-se uma influencia mais acentuada dos carbonatos precipitados que a dos naturais. As micrografias mostraram uma boa dispersão e distribuição das partículas na matriz polimérica e ilustram claramente os diferentes tamanhos de partículas das cargas usados neste trabalho. O estudo mostrou ainda uma grande heterogeneidade das propriedades da espuma, em função da posição na placa moldada e ao longo da espessura. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Materiais |
|
dc.title |
Influência do carbonato de cálcio nas propriedades físicas da espuma de EVA. |
pt_BR |
dc.date.issued |
2007-05 |
|
dc.description.abstract |
EVA foams have been widely used in footwear components owing to
combination of good mechanical properties and low density. The calcium carbonate is the filler more used in EVA foams mainly due to its low price and good processability. However, this filler also has influence in the physical and mechanical properties of the foam. The most frequently used calcium carbonates are the natural ones, followed for the synthetic carbonates, known as precipitated CaC03. These last ones are more expensive and they are used when better mechanical properties are desired. In this work, the foams were prepared in a laboratory hot press after mixing in an industrial intensive mixer
(Banbury) and roll mill. The composites were prepared with two types of natural and two types of precipitated calcium carbonate, both having crystalline structure, with sizes between 1,7 and 8,3 \.im. The amount of calcium carbonate in the foam varied between 5 and 45 phr. The density, the hardness and tensile properties of the various types of foams were evaluated and also the topography, through scanning electron microscopy. The results showed a very good correlation between the increase in properties and concentration and particle size of the filler. The precipitated calcium carbonate had more influence
than of the natural calcium carbonate. The scanning electron micrographs showed a good filler dispersion and distribution in polymer matrix and illustrate clearly the different sizes of filler used in this work. The study also showed that the properties of the foam are highly heterogeneous, as a function of the position in the foam sheet and through the thickness direction. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10750 |
|
dc.date.accessioned |
2020-01-07T13:44:10Z |
|
dc.date.available |
2020-01-07 |
|
dc.date.available |
2020-01-07T13:44:10Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Espuma de EVA |
|
dc.subject |
Carbonato de Cálcio |
|
dc.subject |
Densidade |
|
dc.subject |
Dureza |
|
dc.subject |
Propriedades Mecânicas |
|
dc.subject |
Resina de EVA |
|
dc.subject |
Expansor ou Esponjante |
|
dc.subject |
Reticulante |
|
dc.subject |
Lubrificante |
|
dc.subject |
EVA Foam |
|
dc.subject |
Calcium Carbonate |
|
dc.subject |
Density |
|
dc.subject |
Toughness |
|
dc.subject |
Mechanical Properties |
|
dc.subject |
EVA Resin |
|
dc.subject |
Expander or Sponge |
|
dc.subject |
Crosslinker |
|
dc.subject |
Lubricant |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
CHÁVEZ, Manuel Alpire. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Influence of calcium carbonate on the physical properties of EVA foam. |
pt_BR |
dc.identifier.citation |
ALPIRE CHÁVEZ, Manuel. Influência do carbonato de cálcio nas propriedades físicas da espuma de EVA. 2007. 105f. (Dissertação) Mestrado em Ciência e Engenharia de Materiais, Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Campina Grande- Paraíba - Brasil, 2007. |
pt_BR |