dc.description.resumo |
O ramo das cerâmicas magnéticas, em especia! as ferritas de Mn-Zn, vem
crescendo comercialmente por apresentarem propriedades como alta
saturação magnética e possibilidade de aplicação em altas frequências com
baixas perdas magnéticas. Porem, estas cerâmicas apresentam propriedades
magnéticas que são sensíveis a sua estrutura e morfologia, e que dependem
fundamentalmente das condições de processamento. Assim, o objetivo deste
trabalho foi estudar a influencia dos combustíveis glicina e ureia, e da diluição
na síntese de ferritas Mn0,65Zn0,35Fe2O4 nas proporções 1:0 (sem diluição),
1:3,5, 1:7, 1:10 e 1:14 de reagentes total (RT):100 mL de água destilada. Os
resultados mostram que as amostras sintetizadas com glicina, o aumento da
diluição favoreceu a obtenção de amostras monofásicas e com maior tamanho
de partícula e/ou aglomerados e isso contribuiu para o aumento das
propriedades magnéticas. Para as amostras sintetizadas com ureia, em todas
as diluições avaliadas houve a formação da fase ferrita Mn-Zn com tragos de
hematita. O aumento da diluição não alterou de forma significativa a estrutura,
morfologia e comportamento magnético das amostras. Para as amostras
sintetizadas com glicina o melhor resultado magnético foi observado para a
amostra diluída na proporção 1:14 que apresentou magnetização de saturação
64 emu/g e campo coercitivo 0,183 KOe. Para a amostra ureia o melhor
resultado magnético foi obtido pela amostra sem diluição proporção 1:0 que
apresentou magnetização de saturação 51 emu/g e campo coercitivo 0,134
KOe. De uma forma geral, analisando o tipo de combustível, os melhores
resultados foram obtidos para as amostras sintetizadas com glicina. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Ciência e Engenharia de Materiais. |
|
dc.title |
Avaliação dos combustíveis uréia e glicia na síntese por reação de combustão de ferrita Mn0, 65Zn0, 35Fe, O4. |
pt_BR |
dc.date.issued |
2011-05-16 |
|
dc.description.abstract |
In the field of magnetic ceramics, in particular the Mn-Zn ferrites have grown
commercially due to their properties such as high magnetic saturation and the
possibility of application at high frequencies with low magnetic losses. However,
these ceramics exhibit magnetic properties that are sensitive to their structure
and morphology, and depend mainly on the processing conditions. Thus, the
aim was to study the influence of glycine and urea fuels, and the dilution in the
synthesis of ferrites Mn0 . 6 5Zn0 3 5Fe204 in the proportions 1:0 (undiluted), 1:3,5,
1:7, 1: 1:14 and 10 total reagent (RT): 100 mL of distilled water. The results
show that the samples synthesized with glycine, the increase in dilution favored
the production of single-phase samples and greater particle size and / or
clusters, and this contributed to the increase of the magnetic properties. For
samples synthesized with urea, for all dilutions was evaluated the formation of
Mn-Zn ferrite phase with traces of hematite. Increasing the dilution did not
significantly alter the structure, morphology and magnetic behavior of the
samples. For samples synthesized with glycine the best result was observed for
the magnetic sample diluted in the ratio 1:14 showed that saturation
magnetization 64 emu/g and coercive field 0.183 KOe. For the urea sample the
best result was obtained by magnetic sample without dilution ratio 1.0 showed
that saturation magnetization coercive field 51 emu/g e 0.134 KOe. In general,
analyzing the type of fuel, the best results were obtained for samples
synthesized with glycine. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10751 |
|
dc.date.accessioned |
2020-01-07T13:53:27Z |
|
dc.date.available |
2020-01-07 |
|
dc.date.available |
2020-01-07T13:53:27Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Combustíveis |
|
dc.subject |
Proporção de Diluição |
|
dc.subject |
Ferritas Mn-Zn |
|
dc.subject |
Reação de Combustão |
|
dc.subject |
Glicina |
|
dc.subject |
Ureia |
|
dc.subject |
Fuels |
|
dc.subject |
Dilution Ratio |
|
dc.subject |
Ferrites Mn-Zn |
|
dc.subject |
Glycine |
|
dc.subject |
Urea |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SANTOS, Rafaela Luiz Pereira. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Evaluation of urea and glycium fuels in the synthesis by ferrite combustion reaction Mn0,65Zn0,35Fe, O4. |
pt_BR |
dc.identifier.citation |
SANTOS, Rafaela Luiz Pereira. Avaliação dos combustíveis uréia e glicia na síntese por reação de combustão de ferrita Mn0, 65Zn0, 35Fe, O4. 2011. 124 f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2011. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10751 |
pt_BR |