dc.description.resumo |
O termo biomaterial foi definido na Conferência do Institute Nacional de
Desenvolvimento de Consenso em Saúde, em 1982, como sendo "Qualquer
substância (outra que não droga) ou combinação de substâncias, sintética ou
natural em origem, que possa ser usada por um período de tempo, completa ou
parcialmente como parte de um sistema que trate, aumente ou substitua
qualquer tecido, órgão ou função do corpo". Os de origem metálica são
bastante utilizados no campo biomédico devido a facilidade de processamento
e por apresentarem algumas propriedades mecânicas semelhantes as dos
materiais biológicos, tendo como exemplo o titânio. O titânio é um dos poucos
materiais que naturalmente tem a capacidades para ser implantado no corpo
humano, pois apresenta alta forca, baixo peso, excelente resistência a corrosão
e biocompatibilidade. Nos últimos anos, foi possível observar um notável
crescimento do numero de cirurgias com aplicação dos grampos cirúrgicos em
substituição das suturas padrões. Dessa forma, este trabalho tem como
objetivo caracterizar grampos cirúrgicos de titânio com intuito de certificar se as
informações dadas pelos fornecedores condizem com a realidade. Os
difratogramas dos grampos GPX e GPY obtidos na analise de DRX são típicos
do titânio. Na MO e MEV foi possível observar frisos na superfície interna dos
grampos GPX e GPY, frisos esses que são inexistentes nos grampos GPZ.
Ainda no MEV pode-se verificar fraturas na região de todos os grampos
estudados. A analise de EDS comprovou a pureza dos grampos GPX e GPY, e
apresentando materiais não informados pelo fornecedor. Pela analise de DSC
comprovou-se a não existência de materiais com ponto de fusão menor que
500 °C. Concluiu-se que os grampos GPX e GPY apresentam composição e
morfologia idênticas as informadas pelo fornecedor e que os grampos GPZ
apresentam elementos na sua composição que não são informados pelo
fornecedor. Observou-se que todos os grampos possuem fraturas em sua
estrutura, o que faz necessário estudar materiais que associados ao titânio
aumentem sua resistência a flexão, impedindo que o material sofra ruptura no
pós-operatório. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Ciência e Engenharia de Materiais. |
|
dc.title |
Análise, caracterização e perspectiva de desenvolvimento de grampos cirúrgicos. |
pt_BR |
dc.advisor1 |
Grampos Cirúrgicos. |
|
dc.date.issued |
2013-10-18 |
|
dc.description.abstract |
The term biomaterial was defined at the Conference of the National Institute of
Health Consensus Development in 1982, as" any substance (other than drugs)
or combination of substances, synthetic or natural in origin, which can be used
for a period of time, completely or partially as part of a system that treats,
increase or replace any tissue, organ or function of the body."The metal source
are widely used in the biomedical field due to ease of processing and
presenting some mechanical properties similar to biological materials, having
for example titanium. Titanium is one of the few materials that naturally have the
ability to be implanted in the human body, because of its high strength, low
weight, excellent corrosion resistance and biocompatibility. In recent years, we
observed a notable increase in the number of surgeries with application of
surgical staples instead of sutures standards. Thus, this work aims to
characterize titanium surgical staples aiming to ensure that the information
provided by suppliers in line with reality. The XRD patterns of the staples GPX
and GPY obtained from XRD analysis are typical of titanium. In OM and SEM
was observed friezes on the inner surface of the clamps GPX and GPY, friezes
that are nonexistent in these clips GPZ. Also in the SEM can be observed
fractures in the region of all staples studied. EDS analysis confirmed the purity
of the staples GPX and GPY, and presenting material not informed by the
supplier. For DSC analysis proved the absence of materials having a melting
point lower than 500 ° C. It was concluded that the clamps GPX and GPY
identical in composition and morphology reported by the supplier and that the
pins in their GPZ elements present composition are not reported by the
supplier. It was observed that all of the clips have breaks in their structure,
which makes it necessary to study materials associated with titanium to
increase its bending resistance, preventing the material undergoes rupture in
the postoperative period. |
pt_BR |
dc.date.accessioned |
2020-01-07T14:19:14Z |
|
dc.date.available |
2020-01-07 |
|
dc.date.available |
2020-01-07T14:19:14Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Biomaterias. |
|
dc.subject |
Titânio. |
|
dc.subject |
Grampos. |
|
dc.subject |
Grampo Metálico de Titânio. |
|
dc.subject |
Corpo - Resistência de Metais - Cirurgias. |
|
dc.subject |
Corrosão - Resistência. |
|
dc.subject |
Biomaterials. |
|
dc.subject |
Titanium. |
|
dc.subject |
Bobby pins. |
|
dc.subject |
Titanium Metal Clamp. |
|
dc.subject |
Body - Resistance of Metals - Surgeries. |
|
dc.subject |
Corrosion - Resistance. |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
BORGES FILHO, Odir Pereira. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Analysis, characterization and development perspective of surgical staples. |
pt_BR |
dc.identifier.citation |
BORGES FILHO, Odir Pereira. Análise, caracterização e perspectiva de desenvolvimento de grampos cirúrgicos. 2013. 45f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10754 |