dc.description.resumo |
Neste trabalho, foram estudados nanocompósitos de polipropileno/argila
bentonítica organofílica e polipropileno/compatibilizante/argila bentonítica
organofílica. Os nanocompósitos foram preparados com o polipropileno como
matriz e argila bentonítica organofílica como fase dispersa. Foi utilizada a argila
Brasgel, e diferentes concentrações (0,5; 1; 3; 5 e 10) per para a preparação
dos sistemas. Inicialmente, a argila foi organofilizada com o tensoativo iônico
Praepagen WB® e, em seguida, caracterizada pelas técnicas de DRX e FTIR.
Posteriormente, a argila foi incorporada a matriz polimérica a fim de se obter
um nanocompósito com e sem compatibilizantes. Foram utilizados dois tipos de
compatibilizantes, o PPgMA e o EG. Para cada tipo de compatibilizante, as
concentrações de argila utilizadas foram de 0,5 e 1 per. A organofilização da
argila foi indicada pela técnica de FTIR e comprovada pela técnica de DRX. A
formação do nanocompósito e de suas características foram verificadas através
das técnicas de DRX e das propriedades reológicas. Por meio dos resultados
de DRX foi observado que o comportamento dos nanocompósitos foi o mesmo
apresentados nos difratogramas de DRX da argila OMMT, sendo que os picos
apresentaram maior intensidade com o aumento do teor de argila. Já para os
nanocompósitos com o PPgMA foi observado picos semelhantes ao da argila
OMMT, e para o EG não houve aparecimento de picos característicos da argila
OMMT. Reologicamente foi observada que a viscosidade aumentou com o teor
de argila e com o tipo de compatibilizante. Essa variação foi percebida em
baixas frequências, tanto no regime permanente, quanta no regime oscilatório.
O modulo de armazenamento a baixas frequências foi maior quando
comparado ao PP puro para todas as composições estudadas. Sendo que o
EG proporcionou mudanças mais significativas quando comparado com o
PPgMA. Tendo como base os resultados obtidos, pode-se concluir que houve a
formação de três tipos de estruturas: microcompósito; intercalada; e esfoliada
e/ou intercalada com alto grau de dispersão. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Ciência e Engenharia de Materiais. |
|
dc.title |
Estudo reológico em regimes permanente e oscilatório de nanocompósitos com matriz de polipropileno. |
pt_BR |
dc.date.issued |
2012-08 |
|
dc.description.abstract |
In this work polypropylene (PP)/organophilic bentonitic clay (OMMT) and
PP/compatibilizer/OMMT nanocomposites were studied. The nanocomposites
were prepared using polypropylene as matrix and organophilic bentonite clay as
the dispersed phase (0.5, 1, 3, 5 and 10) phr of Brasgel clay was used for
preparing the systems. Initially, the clay was organophilizated with the ionic
surfactant Praepagen WB® and then characterized by XRD and FTIR
techniques. Subsequently, the clay was incorporated into the polymer matrix in
order to obtain a nanocomposite with and without compatibilizers. PPgMA and
EG were used as compatibilizers. For each type of compatibilizer, the clay
concentrations used were 0.5 and 1 phr. The organophilization of clay was
confirmed by FTIR and XRD techniques. The formation of the nanocomposites
and their characteristics were checked by XRD technique and Theological
properties. Through the XRD results it was observed that the behavior of the
nanocomposite was the same as the OMMT clay. The clay peaks intensity
increased with the increase in the clay content. As for the nanocomposites with
PPgMA the peaks were similar to that of OMMT clay. For the EG no OMMT
characteristic peak was observed. Rheologically it was observed that the
viscosity increased with the clay content and with the compatibilizer type. This
variation was seen at low frequencies, both in the steady state, as in the
oscillatory regime. The storage modulus at low frequencies was higher
compared to pure PP for all compositions investigated. The EG provided more
significant changes compared with the PPgMA. Based on these results, we
concluded that there was formation of three types of structures: microcomposite;
intercalated, and exfoliated and / or intercalated with high degree of
dispersion. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10756 |
|
dc.date.accessioned |
2020-01-07T14:28:03Z |
|
dc.date.available |
2020-01-07 |
|
dc.date.available |
2020-01-07T14:28:03Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Reologia. |
|
dc.subject |
Nanocompósitos. |
|
dc.subject |
Argila Organofílica. |
|
dc.subject |
Polipropileno. |
|
dc.subject |
Reologia de Polímeros. |
|
dc.subject |
Propriedades Reológicas. |
|
dc.subject |
Rheology. |
|
dc.subject |
Nanocomposites. |
|
dc.subject |
Organophilic clay. |
|
dc.subject |
Polypropylene. |
|
dc.subject |
Polymer Rheology. |
|
dc.subject |
Rheological Properties. |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
XAVIER, Pablícia Fernanda Sousa Pires. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Permanent and oscillatory rheological study of polypropylene matrix nanocomposites. |
pt_BR |
dc.identifier.citation |
XAVIER, Pablícia Fernanda Sousa Pires. Estudo reológico em regimes permanente e oscilatório de nanocompósitos com matriz de polipropileno. 2012. 116f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2012. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10756 |
pt_BR |