dc.creator.ID |
NERI, K. D. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/7605887176195246 |
pt_BR |
dc.contributor.advisor1 |
VILAR, Eudésio Oliveira. |
|
dc.contributor.advisor1 |
MEIRA, Gibson Rocha. |
|
dc.contributor.advisor1ID |
VILAR, E. O. |
pt_BR |
dc.contributor.advisor1ID |
MEIRA, G. R. |
|
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/6363257813968241 |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/4589258287572417 |
|
dc.contributor.referee1 |
CARNEIRO, Arnaldo Manoel Pereira. |
|
dc.contributor.referee2 |
OLIVEIRA, Líbia de Souza Conrado. |
|
dc.description.resumo |
A corrosão do aço de reforço e de grande preocupação na construção civil, pois e a causa mais comum da degradação no concreto armado. Inicialmente o aço embutido e naturalmente protegido da corrosão pela alta alcalinidade da estrutura de concreto. No entanto, esse estado passive pode ser rompido pela destruição da película passiva por íons agressivos (cloretos, sulfatos). No presente trabalho, estudamos o comportamento de três tipos de concreto em
relação ao fator água/cimento (0,4; 0,5; 0,6) submetidos ao ataque químico de uma solução constituída apenas de cloretos (NaCl) 1M e outras duas acrescidas de 0,4% e 2% de H2SO4 respectivamente. Com objetivo de avaliar o teor critico de cloretos no concreto. Para a realização dos ensaios eletroquímicos utilizamos a técnica de resistência de polarização linear (LPR) para medir potencial de corrosão (Ecorr) e densidade da corrente de corrosão (icorr), após sua despassivação os corpos-de-prova foram retirados do ensaio e rompidos para constatação visual da corrosão na armadura e determinações dos teores de OH' e CI totais e livres, NaH, Ca+2, K+ e S04
2. O método de lixiviação foi empregado para determinação do pH. A eficiência da lixiviação foi avaliada medindo-se o valor do pH da amostra despassivada e
aquele obtido por titulação. Utilizamos a titilação potenciométrica para determinar o teor de cloreto retido no concrete. E com os valores de pH e teores de CI' determinamos as relações iônicas [Cl"]/[OH'], referentes aos teores retidos no concreto no processo de indução da corrosão. As concentrações de sulfatos foram determinadas pelo método turbidimétrico e dos álcalis (Na", K*, Ca'2) por fotometria de chama. Na presente pesquisa pode-se observar que a relação água/cimento e agressividade das soluções foram fatores determinantes para a corrosão do aço. Os concretos de maior relação água/cimento (0,6) submetidos a solução de
NaCl + 2% H2SO4 foram os primeiros a despassivarem, obtiveram o menor valor de
resistência a compressão e maior retenção de cloretos. Obtivemos uma diferença media entre os resultados do pH titulado e pHmetro de aproximadamente 3 % com desvio padrão de ±0,06, um teor CI" total (1,07 - 2,5) % da massa de cimento e uma relação media iônica [CI*
]/[OH] (0,1-0,33). |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Química |
|
dc.title |
Avaliação do teor crítico de cloretos em concreto armado em meios com a presença de ácido sulfúrico. |
pt_BR |
dc.date.issued |
2010-09 |
|
dc.description.abstract |
The corrosion of reinforcing steel is of great concern in the construction, because the most
common cause of deterioration in reinforced concrete. Initially, the embedded steel from
corrosion and naturally protected by high alkalinity of the concrete structure. However, this
passive state can be broken by destroying the passive film by aggressive ions (chlorides,
sulfates). In this paper, we study the behavior of three types of concrete over the water /
cement ratio (0.4, 0.5, 0.6) subjected to chemical attack of a solution consisting of only
ehlotide (NaCl) and two 1M increased by 0.4% and 2% H2S04 , respectively. To evaluate the
critical chloride content in concrete. For the tests we used the electrochemical technique of
linear polarization resistance (LPR) to measure the corrosion potential (Ecorr) and corrosion
current density (icorr) after their bodies depassivation proof-of-test and were removed from
the ruptured for visual evidence of corrosion in the steel and determination of the levels of
OH- and CI- total and free, Na + Ca +2, K + and SO4. The leaching method was employed to
determine pH. The leaching efficiency was assessed by measuring the pH of the sample
despassivada and that obtained by titration. We used the potentiometric titillation to determine
the chloride content retained in the concrete. And with the pH and concentration of CI
determined the ionic relations [C1-] / [OH-], referring to the contents retained in the concrete
in the induction process of corrosion. The concentrations of sulfate were determined by
turbidimetric method and the alkali (Na K Ca ~2) by rlame photometry. In this research
can be observed that the water / cement ratio and aggressiveness of the solutions were
determining factors for the corrosion of steel The concrete of higher water / cement ratio
(0.6) subjected to NaCl solution + 2% H2SO4 as the first to despassivarem, had the lowest
value of compressive strength and greater retention of chlorides. We obtained an average
difference between the results of pH titration and pH meter to about 3% with standard
deviation of ± 0.06, a total CI- content (1.07 - 2.5)% by weight of cement and an average ratio
of[Cl-]/[OH-](0.1-0.33). |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10976 |
|
dc.date.accessioned |
2020-01-16T10:29:53Z |
|
dc.date.available |
2020-01-16 |
|
dc.date.available |
2020-01-16T10:29:53Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Teor Crítico de Cloretos |
|
dc.subject |
Concreto Armado |
|
dc.subject |
Ácido Sulfúrico |
|
dc.subject |
Corrosão |
|
dc.subject |
Despassivação |
|
dc.subject |
Polarização Linear |
|
dc.subject |
Critical Chloride Content |
|
dc.subject |
Reinforced Concrete |
|
dc.subject |
Sulfuric Acid |
|
dc.subject |
Corrosion |
|
dc.subject |
Despassivation |
|
dc.subject |
Linear Polarization |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
NERI, Kátya Dias. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Evaluation of the critical chloride content in reinforced concrete in sulfuric acid media. |
pt_BR |
dc.identifier.citation |
NERI, Kátya Dias. Avaliação do teor crítico de cloretos em concreto armado em meios com a presença de ácido sulfúrico. 2010. 91f. (Dissertação de Mestrado em Engenharia Química), Programa de Pós-graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2010. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/10976 |
pt_BR |