dc.creator.ID |
SOARES, R.L. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/0494374289705105 |
pt_BR |
dc.contributor.advisor1 |
CASTRO, Walman Benício de. |
|
dc.contributor.advisor1ID |
CASTRO, W. B. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/3592569966434979 |
pt_BR |
dc.contributor.advisor2 |
LUCIANO, Benedito Antonio. |
|
dc.contributor.advisor2ID |
LUCIANO, B. A. |
|
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/2390722791029216 |
|
dc.contributor.referee1 |
ARAÚJO, Carlos José de. |
|
dc.contributor.referee2 |
GONZALEZ, Cezar Henrique. |
|
dc.description.resumo |
Nesta dissertação é apresentada a caracterização da liga Ti45Ni48Cu7 com efeito de
memoria de forma a ser empregada numa microválvula destinada ao controle
fluídico mediante o Efeito Joule. Neste intuito, buscou-se obter inicialmente uma
porção fundida de massa com proporções controladas de 45%Ti48%Ni7%Cu em
peso, transformada em fitas solidificadas rapidamente pelo processo melt spinning a
uma velocidade de 38 m/s. As fitas obtidas foram submetidas ao processo térmico
de relaxação com o objetivo de pro mover a eliminação dos defeitos internos. Em
seguida, a obtenção das temperaturas de transformação de fase e o registro das
energias de entalpia das fitas foram feitos experimentalmente mediante Calorimetria
Exploratória Diferencial. Adicionalmente, o teste DMA (Dynamic Mechanical
Analysis) foi feito para registrar o crescimento percentual do modulo de elasticidade
da fita submetida a temperaturas variadas. A submissão da fita a um banho térmico
possibilitou traçar o gráfico Resistência Elétrica versus Temperatura nos padrões
desejados e, assim, chegou-se a escolha da fita a ser empregada na microválvula
teorizada por Bellouard. Para demonstrar experimentalmente que esta fita seria
capaz de funcionar normalmente no produto para o qual foi teoricamente sugerida,
traçou-se o gráfico experimental de Resistividade Elétrica. O projeto tridimensional
da microválvula, a geometria 3D interna e, a partir desta ultima, uma simulação
computacional a base de estrutura estática com a ferramenta CFX do ANSYS®
Workbench V14 foram realizados e apresentados, possibilitando a visualização do
deslocamento do fluido newtoniano no interior da microválvula. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Ciência e Engenharia de Materiais. |
|
dc.title |
Caracterização de uma fita de Ti45Ni48Cu7 com efeito de memória de forma para aplicação em uma microválvula. |
pt_BR |
dc.date.issued |
2013-03 |
|
dc.description.abstract |
In this work is presented the characterization of Ti45Ni48Cu7 alloy with shape memory
effect to be used in a microvalve to fluid control by Joule effect. To this purpose, it
was obtained a portion fused mass with controlled rates of 45%Ti48%Ni7%Cu weight
was transformed into ribbons by melt spinning process at a speed of 38 m/s. The
ribbons obtained were subjected to thermal relaxation process in order to promote
the elimination of internal defects. Then, to obtain the phase transformation
temperatures and the energy enthalpy, the ribbons were submitted to Differential
Scanning Calorimetry (DSC). Following, the dynamic mechanical analysis (DMA) test
was done to record the percentage increase in the modulus of elasticity of the ribbon
submitted to different temperatures. By submission of the ribbon to a thermal bath it
was possible to plot the electrical resistance versus the pattern desired temperature
and thus the ribbon to be used in the microvalve theorized by Bellouard was chosen.
To demonstrate experimentally that this tape would be able to work normally in the
product for which it was theoretically suggested, an experimental electrical resistivity
versus temperature graph was plotted. Additionally, from the three-dimensional
design and the 3D and internal microvalve geometry, a computer simulation based
on static structure CFX tool with the ANSYS® Workbench V14 were performed and
displayed, enabling the visualization of the Newtonian fluid movement within the
microvalve. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11331 |
|
dc.date.accessioned |
2020-01-29T13:49:40Z |
|
dc.date.available |
2020-01-29 |
|
dc.date.available |
2020-01-29T13:49:40Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Fluido |
|
dc.subject |
Microválvula |
|
dc.subject |
Efeito de Memória de Forma - EMF |
|
dc.subject |
Microssistema |
|
dc.subject |
Ti-Ni-Cu - Fita |
|
dc.subject |
Ligas |
|
dc.subject |
Fluid |
|
dc.subject |
Microvalve |
|
dc.subject |
Shape Memory Effect |
|
dc.subject |
Microsystem |
|
dc.subject |
Ti-Ni-Cu - Tape |
|
dc.subject |
Leagues |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SOARES, Roniere Leite. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Characterization of a Ti45Ni48Cu7 tape with shape memory effect for application in a microvalve. |
pt_BR |
dc.identifier.citation |
SOARES, Roniere Leite. Caracterização de uma fita de Ti45Ni48Cu7 com efeito de memória de forma para aplicação em uma microválvula. 2013. 102. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11331 |