Efeito da direção e da espessura na taxa de propagação de trinca por fadiga de alto ciclo nos aços da classe API 5L-X70 e ASTM A516-GR65.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA
→
Mestrado em Engenharia Mecânica.
→
Ver item

dc.creator.ID	FARIAS, M. A.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/7975544078173876	pt_BR
dc.contributor.advisor1	SANTOS, Marco Antônio dos.
dc.contributor.advisor1ID	SANTOS, M. A.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/4825985900425353	pt_BR
dc.contributor.referee1	STROHAECKER, Telmo Roberto.
dc.contributor.referee2	MACIEL, Theóphilo Moura.
dc.description.resumo	Neste trabalho foi estudada a influência da espessura e da direção de orientação da trinca ( "TL" e "SL" ), no comportamento a fadiga dos aços das classes API 5L-X70 e ASTM A516-GR65. Os ensaios foram realizados a temperatura ambiente em corpos de prova do tipo Tração Compacta ("Compact Tension"). A propagação da trinca de fadiga foi acompanhada pelo método visual com um microscópio de deslocamento ("Travel Microscope"). Para os dois aços estudados, quando a trinca se propaga na direção longitudinal em um piano paralelo ao de laminação da chapa ("SL"), a espessura do corpo de prova tende a afetar a taxa de propagação da trinca de fadiga. O comportamento a fadiga do dois aços foi comparado e as diferenças discutidas.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Mecânica
dc.title	Efeito da direção e da espessura na taxa de propagação de trinca por fadiga de alto ciclo nos aços da classe API 5L-X70 e ASTM A516-GR65.	pt_BR
dc.date.issued	1994-09-15
dc.description.abstract	In This work the effect of thickness and crack orientation ("TL" and "SL") on fatigue behaviour of steels class API 5L-X70 and ASTM A516-GR65 was investigated. The tests were conducted at ambient temperature and compact tension tests specimens was used. Fatigue crack propagation was attended with a travell microscope. When the crack propagate in the longitudinal direction in a parallel plane to lamination plane of the plate ("SL"), the test specimen thickness tend to effect the fatigue crack propagation. Fatigue behaviour of the steels was confronted and the differences discussed.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11413
dc.date.accessioned	2020-01-31T15:16:50Z
dc.date.available	2020-01-31
dc.date.available	2020-01-31T15:16:50Z
dc.type	Dissertação	pt_BR
dc.subject	Defeito-trinca-fadiga
dc.subject	Defecto-crack-fatiga
dc.subject	Defect-crack-fatigue
dc.subject	Aço API5L-X70
dc.subject	API5L-X70 steel
dc.subject	Acero API5L-X70
dc.subject	Aço ASTM A516-GR65
dc.subject	Acero ASTM A516-GR65
dc.subject	ASTM A516-GR65 steel
dc.subject	Propagação de trinca
dc.subject	Crack propagation
dc.subject	Propagación de grietas
dc.rights	Acesso Aberto	pt_BR
dc.creator	FARIAS, Marconi Andrade.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Effect of direction and thickness on the crack propagation rate by high cycle fatigue in API 5L-X70 and ASTM A516-GR65 class steels.	pt_BR
dc.identifier.citation	FARIAS, Marconi Andrade. Efeito da direção e da espessura na taxa de propagação de trinca por fadiga de alto ciclo nos aços da classe API 5L-X70 e ASTM A516-GR65. 201f. (Dissertação de Mestrado em Engenharia Mecânica), Curso de Pós-Graduação em Engenharia Mecânica, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil, 1994. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11413	pt_BR