Avaliação da susceptibilidade a trincas a frio induzidas por hidrogênio em juntas soldadas dos aços API 5L X-80 por meio do teste de implante.

Accueil de DSpace
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS
→
Mestrado em Ciência e Engenharia de Materiais.
→
Voir le document

dc.creator.ID	MARQUES, L. N.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/3754473953019217	pt_BR
dc.contributor.advisor1	MACIEL, Theophilo Moura.
dc.contributor.advisor1ID	MACIEL, T. M.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/9476858938351846	pt_BR
dc.contributor.referee1	SANTOS, Marco Antonio dos.
dc.contributor.referee2	ALMEIDA, Daisy Martins de.
dc.contributor.referee3	CASTRO, Walman Benicio de.
dc.description.resumo	Neste trabalho foi avaliada a influencia dos parâmetros, processos e procedimentos de soldagem sobre a susceptibilidade a trincas a frio induzidas pelo hidrogênio (TIH) em juntas soldadas do ago API 5L X80. Para isto foram realizados ensaios de implante em soldagens executadas pelos processos SMAW e FCAW com diferentes parâmetros e procedimentos de soldagem. Os consumíveis utilizados foram o arame autoprotegido AWS E 91T8-K8 com 1,60 mm de diâmetro e com proteção gasosa (75% Ar -25%CO-,) AWS E 91T1-G com diâmetro de 1,20 mm. E os eletrodos AWS E 8010 e AWS E 8018-G, com diâmetro de 4,00 mm. Apos as soldagens os corpos de prova foram cortados transversalmente e as trincas e microtrincas, quando existentes, foram identificadas, para cada condição de soldagem sendo os resultados associados a microestrutura e ao valor de microdureza na região onde ocorreu trincamento. A microestrutura predominante foi composta por Bainita e Ferrita Primaria e todas as trincas encontradas foram de característica intergranular, entretanto não representaram um numero significativo, os como os valores de microdureza, foram todos abaixo de 238,1 HV, tanto no metal de solda como na ZTA e possível dizer que o ago estudado apresenta boa soldabilidade e não e susceptível ao TIH para as condições analisadas.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Ciência e Engenharia de Materiais.
dc.title	Avaliação da susceptibilidade a trincas a frio induzidas por hidrogênio em juntas soldadas dos aços API 5L X-80 por meio do teste de implante.	pt_BR
dc.date.issued	2013-02-27
dc.description.abstract	In this study, the influence of the parameters, process and welding procedures on susceptibility to hydrogen induced cold cracking in API 5L X80 steel welded joints . Were evaluated for this Implant Test using SMAW and FCAW process with different parameters and welding procedures. Were used AWS E 91T8-K8 with 1,60 mm diameter self protected and AWS E 91T1-G with 1,20 mm diameter gas protected . And AWS E 8010 e AWS E 8018-G, with diameter 4,00 mm. After welding the specimens were cut and cracks and microcracks were identified for each welding condition and the results associated with the microstructure and microhardness value in the region where cracking occurred. It was verified that all cracks occurred were predominantly composed of Bainite and Primary Ferrite All cracks were intergranular but do not represented a significant size, as all the microhardness values were less than 238,1 HV it is possible to say that the steel studied has a good weldability and it is not likely to be susceptible to hydrogen induced cold cracking for the analyzed conditions	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11430
dc.date.accessioned	2020-02-03T11:50:33Z
dc.date.available	2020-02-03
dc.date.available	2020-02-03T11:50:33Z
dc.type	Dissertação	pt_BR
dc.subject	Soldagem
dc.subject	Aço API 5L X80
dc.subject	Trincamento Induzido por Hidrogênio
dc.subject	Teste de Implante
dc.subject	Processos SMAW e FCAW
dc.subject	Trincas
dc.subject	Welding
dc.subject	API 5L X80 Steel
dc.subject	Hydrogen-Induced Cracking
dc.subject	Implant Test
dc.subject	SMAW and FCAW Processes
dc.subject	Cracks
dc.rights	Acesso Aberto	pt_BR
dc.creator	MARQUES, Lívia Neves.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Evaluation of susceptibility to cold cracks induced by hydrogen in welded joints of API 5L X-80 steels using the implant test.	pt_BR
dc.identifier.citation	MARQUES, Lívia Neves. Avaliação da susceptibilidade a trincas a frio induzidas por hidrogênio em juntas soldadas dos aços API 5L X-80 por meio do teste de implante. 2013. 97 f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2013. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11430	pt_BR