dc.creator.ID |
PAZ, R. A. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/2848266629474356 |
pt_BR |
dc.contributor.advisor1 |
ARAÚJO, Edcleide Maria. |
|
dc.contributor.advisor1ID |
ARAÚJO, E. M. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/1097999681102529 |
pt_BR |
dc.contributor.advisor2 |
MÉLO, Tomás Jeferson Alves de. |
|
dc.contributor.advisor2ID |
MÉLO, T. J. A. |
|
dc.contributor.advisor2Lattes |
http://lattes.cnpq.br/8562091525519918 |
|
dc.contributor.referee1 |
RABELLO, Marcelo Silveira. |
|
dc.contributor.referee2 |
MALTA, Oscar Manoel Loureiro. |
|
dc.description.resumo |
O efeito do peso molecular da poliamida 6 (PA6) no desenvolvimento de
nanocompósitos polímero/silicatos em camadas preparados pelo método de
intercalação por fusão, foi estudado neste trabalho. A argila foi tratada com o
sal quaternário de amônio (Genamin) visando-se a obtenção da argila
organofilica (OMMT). Ela foi caracterizada por fluorescência de raios-X (FRX),
espectroscopia no infravermelho por transformada de Fourier (FTIR),
termogravimetria (TG) e difração de raios-X (DRX). Os resultados dessas
analises mostraram a incorporação do sal entre as camadas da argila,
tornando-a organofilica. Para a obtenção dos nanocompósitos poliamida
6/argila, foram preparados concentrados de PA6: argila (1:1) para favorecer a
mistura na extrusora de rosca dupla contra-rotacional. Os concentrados obtidos
foram adicionados a matriz polimérica, em quantidades necessárias para a
obtenção de teores nominais de 3% em massa de argila em extrusora e,
posteriormente, foram injetados em Injetora Fluidmec. A caracterização desses
materiais foi realizada atraves de reometria de torque, indice de fluidez,
espectroscopia no infravermelho por transformada de Fourier (FTIR), difração
de raios -X (DRX), calorimetria exploratória diferencial (DSC), microscopia
eletrônica de transmissão (MET), caracterização mecânica (tração e impacto),
temperatura de deflexão térmica (HDT) e analise térmica dinâmico-mecânica
(DMTA). Os resultados de reometria de torque e índice de fluidez mostraram
que a presença da argila organofilica na PA6 aumentou o torque quando
comparado a argila sem tratamento e, que quanta maior a taxa de
cisalhamento, menor a viscosidade do material, caracterizando o
comportamento pseudoplastico. Os difratogramas de raios-X dos filmes da
poliamida 6/argila organofilica mostraram que todos os sistemas apresentaram
predominância de estrutura esfoliada, o que foi confirmado por MET. Já os
resultados de DR-X e MET das amostras obtidas por injeção mostraram
estrutura parcialmente esfoliada. O grau de cristalinidade do nanocompósito,
obtido por DSC, as propriedades mecânicas sob tração e a HDT foram
melhoradas quando comparadas as propriedades da poliamida 6. Em geral, os
nanocompósitos com poliamida 6 de peso molecular mais alto exibiram resultados mais significativos destas propriedades. Os nanocompósitos
apresentaram redução na resistência ao impacto, ou seja, perda de ductilidade.
A analise por DMTA mostrou que a incorporação da argila organofilica, nas
matrizes poliméricas de poliamida 6, aumentou a rigidez do sistema (E') e
diminuiu o tan 5, para todas as temperaturas, confirmando o efeito reforçante
da argila no polímero. Portanto, pode-se mencionar que os sistemas com
poliamida 6 de alto peso molecular apresentaram propriedades melhores em
relação aqueles com pesos moleculares menores. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Ciência e Engenharia de Materiais. |
|
dc.title |
Efeito do peso molecular da poliamida 6 no desenvolvimento da nanocompósitos. |
pt_BR |
dc.date.issued |
2008-02 |
|
dc.description.abstract |
The effect of polyamide 6 (PA6) molecular weight on the development of
polymer/layered silicates nanocomposites prepared by the melt intercalation
technique was studied in this work. The clay was treated with a quaternary
ammonium salt (Genamin) to obtain the organoclay (OMMT). It was
characterized by X-ray fluorescence (XRF), Fourier Transform infrared
spectroscopy (FTIR), thermogravimetry (TG) and X-ray diffraction (XRD). The
results of these analyses showed the incorporation of the salt in the clay
structure, confirming the organophilization. In order to obtain the polyamide
6/organoclay nanocomposites masters of PA6: organoclay (1:1) were prepared
to facilitate the mixture in the counter-rotational twin screw extruder. The
obtained masters were incorporated in the polymer matrix at a content of 3 wt.%
of clay and then, the pellets were injected using a Fluidmec injection molding
machine. The materials were characterized by torque rheometry, melt flow
index, Fourier Transform infrared spectroscopy (FTIR), X-ray diffraction (XRD),
differential scanning calorimetry (DSC), transmission electron microscopy
(TEM), mechanical properties (tensile and Izod impact strength), heat deflection
temperature (HDT) and dynamical-mechanical thermal analysis (DMTA). The
results of torque rheometry and melt flow index showed that the presence of
organoclay in the polyamide 6 increased the torque in relation to the untreated
clay and, the bigger the shear rate the smaller the viscosity of the material,
confirming the pseudoplastic behavior of the system. The patterns of XRD of
the films of PA6/organoclay showed that all systems presented predominance
exfoliated structure which was confirmed by TEM. However, the results of XRD
and TEM of the specimens obtained by injection molding showed exfoliated
and/or partially exfoliated structure. The crystallinity degree of nanocomposite
obtained by DSC, its mechanical properties of tensile and HDT were enhanced
in relation to pure PA6. In general, the polyamide 6 with high molecular weight
nanocomposites presented more significant results of these properties. On the
other hand, its Izod impact strength was reduced. The DMTA analysis showed
that the incorporation of organoclay in the polymer matrices increased the rigidity (E*) of the system and the tanS decreased for all studied temperatures,
confirming the reinforcing effect of the clay in the polymer. Hence, one can say
that the systems with high molecular weight polyamide 6 presented better
properties in relation to the ones with lower molecular weight. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11440 |
|
dc.date.accessioned |
2020-02-03T12:54:04Z |
|
dc.date.available |
2020-02-03 |
|
dc.date.available |
2020-02-03T12:54:04Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Nanocompósitos. |
|
dc.subject |
Poliamida 6 (PA6). |
|
dc.subject |
Argila Bentonita. |
|
dc.subject |
Nanocompositos Polimero/silicatos. |
|
dc.subject |
Reometria de Torque. |
|
dc.subject |
Nanocompósito - Cristalinidade. |
|
dc.subject |
Nanocomposites. |
|
dc.subject |
Polyamide 6 (PA6). |
|
dc.subject |
Bentonite clay. |
|
dc.subject |
Polymer nanocomposites / silicates. |
|
dc.subject |
Torque rheometry. |
|
dc.subject |
Nanocomposite - Crystallinity. |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
PAZ, Renê Anísio da. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Effect of the polyamide 6 molecular weight on the development of nanocomposites. |
pt_BR |
dc.identifier.citation |
PAZ, Renê Anisio da. Efeito do peso molecular da poliamida 6 no desenvolvimento da nanocompósitos. 2008. 96f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2008. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11440 |
pt_BR |