dc.description.resumo |
A preocupação da sociedade com o meio ambiente vem aumentando
progressivamente ao longo dos anos. A população tem se voltado para os
conceitos de sustentabilidade e desta forma vários segmentos ligados a ciência e
tecnologia vem buscando alternativas para controlar ou minimizar danos
causados pelo consumo indiscriminado de matéria prima e energia, alem do alto
volume de resíduos gerados. Nesta perspectiva, o objetivo deste trabalho de
pesquisa e otimizar a utilização do resíduo de vidro piano em substituição parcial
ao feldspato em massas cerâmicas para grés sanitários, visando obter produtos
que apresentem propriedades físicos-mecânicos similares as tradicionais, como
também diminuir a quantidade deste tipo de resíduo acumulado no meio
ambiente. As matérias primas foram caracterizadas através dos ensaios de
espectroscopia de energia dispersiva de raio-X; analise granulométrica; difração
de raios-X; termogravimétria e analise térmica diferencial. Foram formuladas
através dos programas Statistic 7.0 e Reformix massas cerâmicas sem e com
resíduos de vidro piano nos percentuais de 4%, 5% e 6%, para posteriormente
serem avaliadas suas propriedades reológicas. Os corpos cerâmicos foram
inicialmente secados em estufa a 110°C, para serem queimados nas
temperaturas de 1.220 °C; 1.230 °C; 1.240 °C e 1.250 °C. Realizou-se também os
seguintes ensaios físico-mecânicos: absorção de água; porosidade aparente;
massa especifica aparente, retração linear de secagem e queima; perda ao fogo,
ensaio de flexão em três pontos, e microscopia eletrônica de varredura. Os
resultados evidenciaram a importância da utilização de um programa de
otimização de produto e que a utilização de resíduo vítreo em massa para grés
sanitário pode ser utilizado substituindo parcialmente o feldspato nas proporções
próximas a 5%, pois estes apresentam valores de propriedades físico-mecânicas
dentro do permitido pelas industrias de grés porcelanato e normas da ABNT. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Ciência e Engenharia de Materiais. |
|
dc.title |
Otimização no processo de incorporação de resíduo vítreo em massas cerâmicas para grés sanitário. |
pt_BR |
dc.date.issued |
2012-08-31 |
|
dc.description.abstract |
The society's concern for the environment has been increasing steadily over the
years. The population has focused on the concepts of sustainabiiity and thus
various segments related to science and technology is looking for alternatives to
control or minimize damage caused by indiscriminate consumption of raw
materials and energy, and the high volume of waste generated. In this perspective,
the goal of this research is to optimize the use of waste flat glass in substitution for
feldspar on ceramic sanitary earthenware, to obtain products having physicalmechanical
properties similar to traditional, as well as decrease the amount of this
type of waste accumulated in the environment. The raw materials were
characterized by testing for energy dispersive spectroscopy x-ray; sieve analysis,
x-ray diffraction, differential thermal analysis and thermogravimetry. They were
then put through the programs and 7.0 statistic reformix ceramic masses with and
without waste of flat glass in the percentage of 4%, 5% and 6%, then its
rheological properties were evaluated. The ceramic samples were initially dried at
110 ° c, to be burned at temperatures of 1.220 °C, 1.230 °C, 1.240 °C and 1.250
°C. Were performed following physico-mechanical water absorption, apparent
porosity, apparent specific gravity, linear shrinkage in drying and firing, loss on
ignition, bending test at three points, and scanning electron microscopy. The
results showed the importance of using an optimization program product and the
use of glassy residue mass for sanitary earthenware can be used by replacing
partially the feldspar in proportions close to 5%, since these present values of
physico-mechanical properties in permitted by industries porcelain stoneware and
ABNT. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11444 |
|
dc.date.accessioned |
2020-02-03T13:43:57Z |
|
dc.date.available |
2020-02-03 |
|
dc.date.available |
2020-02-03T13:43:57Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Resíduo de Vidro - Otimização de Uso. |
|
dc.subject |
Massas Cerâmicas. |
|
dc.subject |
Propriedades Reológicas. |
|
dc.subject |
Grés Sanitário. |
|
dc.subject |
Grés Porcelanato - Indústrias. |
|
dc.subject |
Resíduo Vítreo. |
|
dc.subject |
Sustentabilidade. |
|
dc.subject |
Glass Waste - Optimization of Use. |
|
dc.subject |
Ceramic Pasta. |
|
dc.subject |
Rheological Properties. |
|
dc.subject |
Sanitary Stoneware. |
|
dc.subject |
Grés Porcelanato - Industries. |
|
dc.subject |
Glassy residue. |
|
dc.subject |
Sustainability. |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
PORTO, Valdênia de Sousa. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Optimization in the process of incorporation of vitreous residue in ceramic masses for sanitary stoneware. |
pt_BR |
dc.identifier.citation |
PORTO, Valdênia de Sousa. Otimização no processo de incorporação de resíduo vítreo em massas cerâmicas para grés sanitário. 2012. 105f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2012. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11444 |
pt_BR |