GOMES, A. A. R.; http://lattes.cnpq.br/2533860814976031; GOMES, Allysson Antônio Ribeiro.
Resumo:
Silicone breast implants are medical devices used to increase, reconstruct or correct mammary congenital deformities. Typically, they are filled with silicone gel and / or saline solutions. Currently, there is often used breast implants with the outer surface of the textured membrane to present maximum security and reduce post-operative complications such as capsular contracture. Thus, this study aimed to evaluate the physical, chemical and biological properties of textured silicone gel breast implants. Four breast implants were analyzed, two different manufacturers. The characterization tests were performed on the inner side of the membrane which is in contact with the gel, and the external side, in contact with the biological environment, through the following techniques: optical microscopy - MO, Scanning Electron Microscopy - SEM, Spectroscopy Energy Dispersive X-ray - EDS, Straightness, Dimensional Testing - Thickness, Mechanical Testing - Traction, Cytotoxicity and cohesiveness gel. The results of the morphological evaluation test (OM and SEM) it was observed that the surface of the membrane in contact with the gel appears with smooth and uniform texture, however, the external side of the membrane was observed pores with very different sizes and shapes . Regarding the mechanical tests, all samples met the regulatory requirements, but one of the samples showed a value close to approval limit. It was observed that the texturing of suferfícies influences the mechanical performances of the membranes. The cohesiveness filling gel test, cytotoxicity and chemical contaminants were similar in all samples and comply with certification regulations.