Influência da energia térmica em propriedades mecânicas e físicas de agregados lateríticos utilizados em concreto betuminoso.

Página inicial
→
Campus Campina Grande | Centro de Tecnologia e Recursos Naturais - CTRN
→
PÓS-GRADUAÇÃO EM ENGENHARIA CIVIL E AMBIENTAL
→
Mestrado em Engenharia Civil e Ambiental.
→
Ver item

dc.creator.ID	MOIZINHO, J. C.	pt_BR
dc.creator.Lattes	http://lattes.cnpq.br/1723058582764231	pt_BR
dc.contributor.advisor1	CARVALHO, João Batista Queiroz de.
dc.contributor.advisor1ID	CARVALHO, J. B. Q.	pt_BR
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/1833502684638113	pt_BR
dc.contributor.advisor2	BRASILEIRO, Francisco Edmar.
dc.contributor.advisor2ID	BRASILEIRO, F. E.
dc.contributor.referee1	BRASILEIRO, Francisco Edmar.
dc.contributor.referee2	CHAGAS FILHO, Milton Bezerra das.
dc.description.resumo	Esta dissertação apresenta os resultados de um estudo desenvolvido como objetivo de estudar a influência da temperatura de secagem na resistência de cinco agregados porosos de origem laterítica da região Nordeste do Brasil. Este estudo consistiu da análise de resultados dos ensaios de esmagamento, abrasão "Los Angeles " e 10% de finos. Também foram verificadas as variações ocorridas com respeito a absorção, a massa específica real e aparente e a resistência dos agregados lateríticos estudados, antes e após ser em extraídos de concreto betuminoso usinado à quente em laboratório pelo método Marshall. Os ensaios foram realizados, com agregados lateríticos secos a temperatura ambiente, a 100º Cr 200º C e 350º C e após serem extraídos de concreto betuminoso usinado à quente. Os resultados obtidos permitiram concluir que, todos os agregados pesquisados aumentaram sua resistência quando tratados a diferentes níveis de energia térmica ate uma certa temperatura. A partir dessa temperatura a resistência dos agregados tendem a diminuir. Agregados antes rejeitados por normas tradicionais passam após tratamento térmico a satisfazerem as mesmas. FinaImente, se conclui que os agregados lateríticos extraídos de concreto betuminoso apresentaram redução de absorção, massa específica real, percentagem de vários, assim como uma resistência maior do que a obtida com o agregado no estado natural.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Tecnologia e Recursos Naturais - CTRN	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA CIVIL E AMBIENTAL	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Civil
dc.title	Influência da energia térmica em propriedades mecânicas e físicas de agregados lateríticos utilizados em concreto betuminoso.	pt_BR
dc.date.issued	1994-04
dc.description.abstract	This dissertation presents the results of a study developed with the objective of studying the influence of drying temperature on the resistance of five porous aggregates of lateritic origin in the Northeast region of Brazil. This study consisted of analyzing the results of crushing, abrasion "Los Angeles" and 10% fines tests. The variations that occurred with respect to absorption, the real and apparent specific gravity and the resistance of the studied lateritic aggregates were also verified, before and after being extracted from hot machined bituminous concrete in the laboratory by the Marshall method. The tests were carried out, with lateritic aggregates dried at room temperature, at 100º Cr 200º C and 350º C and after being extracted from hot machined bituminous concrete. The results obtained allowed us to conclude that, all researched aggregates increased their resistance when treated at different levels of thermal energy up to a certain temperature. From that temperature the resistance of the aggregates tends to decrease. Aggregates previously rejected by traditional standards pass after heat treatment to satisfy them. Finally, it is concluded that the lateritic aggregates extracted from bituminous concrete showed a reduction absorption, real specific mass, percentage of several, as well as greater resistance than that obtained with the aggregate in its natural state.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11778
dc.date.accessioned	2020-02-11T14:46:00Z
dc.date.available	2020-02-11
dc.date.available	2020-02-11T14:46:00Z
dc.type	Dissertação	pt_BR
dc.subject	Geotecnia
dc.subject	Agregados Lateríticos
dc.subject	Energia Térmica
dc.subject	Concreto Betuminoso
dc.subject	Secagem
dc.subject	Agregados Porosos - Região Nordeste - Brasil
dc.subject	Propriedades Mecânicas e Físicas - Concreto Betuminoso
dc.subject	Ensaios de Esmagamento
dc.subject	Geotechnics
dc.subject	Lateritic aggregates.
dc.subject	Thermal energy.
dc.subject	Bituminous Concrete
dc.subject	Drying
dc.subject	Porous Aggregates - Northeast Region - Brazil
dc.subject	Mechanical and Physical Properties - Bituminous Concrete
dc.subject	Crushing Tests
dc.rights	Acesso Aberto	pt_BR
dc.creator	MOIZINHO, Joel Carlos.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Influence of thermal energy on mechanical and physical properties of lateritic aggregates used in bituminous concrete.	pt_BR
dc.identifier.citation	MOIZINHO, Joel Carlos. Influência da energia térmica em propriedades mecânicas e físicas de agregados lateríticos utilizados em concreto betuminoso. 1994. 123f. (Dissertação de Mestrado em Engenharia Civil e Ambiental), Curso de Pós-Graduação em Engenharia Civil, Centro de Ciências e Tecnologia, Universidade Federal da Paraíba – Campus II - Campina Grande - PB - Brasil,1994. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/11778	pt_BR