dc.description.resumo |
O presente trabalho apresenta um estudo da solidificação de ligas do sistema
Pb-Sb super-resfriadas pela técnica de Fusão em Presença de Fluxo. Nesta técnica o metal e
fundido e solidificado envolto em um fluxo viscoso, o qual alem de evitar o contato do
metal liquido com a parede do cadinho e com a atmosfera, atua como agente de limpeza,
absorvendo óxidos superficiais e/ou impurezas que possam vir a atuar como agentes
nucleantes. Os resultados de níveis de super-resfriamentos das amostras solidificadas com
fluxo foram maiores que as ligas solidificadas sem fluxo. O fluxo provavelmente atuou
como agente de limpeza das amostras aumentando o super-resfriamento. Níveis diferentes
de super-resfriamento mostraram influenciar a microestrutura das ligas de composição hipoeutética.
As dendritas se tornaram mais finas e em maior quantidade, como também o
eutético ficou mais fino. Teoria do aumento da taxa de nucleação da fase primaria com o
aumento do super-resfriamento e influencia do crescimento não-estável da fase primaria,
foram as duas teoria adotadas neste trabalho para explicar o refino microestrutural das
dendritas primárias e do eutético, respectivamente. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Ciência e Engenharia de Materiais. |
|
dc.title |
Solidificação de ligas hipo-eutéticas Pb-Sb super-resfriadas pela técnica de fluxo. |
pt_BR |
dc.date.issued |
2006-05-03 |
|
dc.description.abstract |
This work aimed at the study of the solidification of undercooled Pb-Sb
alloys by the fluxing technique. Flux technique has been used to reduce nucleation sites and
produce increased undercooling in metals and alloys. In this work, hypoeutectic alloys were
solidified by fluxing technique. The samples undercooled by flux obtained undercooling
level bigger than the samples undercooled without flux. The flux can have trapped
impurities during solidification, increasing undercooling. The microstructures were
investigated as a function of the undercooling level. For this alloys, a morphological change
occurs with increasing undercooling and was accompanied by a refinement of the primary
dendrites Pb phase and eutectic. The crystal growth velocity usually increases when
undercooling increases, provoked changes morphology in primary phase and eutectic. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/12192 |
|
dc.date.accessioned |
2020-02-26T18:04:58Z |
|
dc.date.available |
2020-02-26 |
|
dc.date.available |
2020-02-26T18:04:58Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Solidificação. |
|
dc.subject |
Super-resfriamento. |
|
dc.subject |
Técnica de Fluxo. |
|
dc.subject |
Ligas Hipo-eutéticas Pb-Sb. |
|
dc.subject |
Taxa de Nucleação. |
|
dc.subject |
Sistema Binário Chumbo - Antimonio (Pb-Sb). |
|
dc.subject |
Análise Microestrutural. |
|
dc.subject |
Solidification. |
|
dc.subject |
Super-cooling. |
|
dc.subject |
Flow Technique. |
|
dc.subject |
Hypo-eutectic alloys Pb-Sb. |
|
dc.subject |
Nucleation Rate. |
|
dc.subject |
Lead Binary System - Antimonio (Pb-Sb). |
|
dc.subject |
Microstructural Analysis. |
|
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
MACÊDO NETO, José Costa de. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Solidification of hypoeutectic Pb-Sb alloys supercooled by the flow technique. |
pt_BR |
dc.identifier.citation |
MACÊDO NETO, José Costa de. Solidificação de ligas hipoeutéticas Pb-Sb super-resfriadas pela técnica de fluxo. 91f. (Dissertação de Mestrado em Ciência e Engenharia de Materiais), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2006. |
pt_BR |