Estudo do comportamento da eletrodeposição da liga ni-p-w utilizando glicina como complexante.

Página inicial
→
Campus Cuité | Centro de Educação e Saúde - CES
→
PÓS-GRADUAÇÃO EM CIÊNCIAS NATURAIS E BIOTECNOLOGIA
→
Mestrado em Ciências Naturais e Biotecnologia - Dissertações 001
→
Ver item

dc.contributor.advisor1	PRASAD, Shiva.
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/8867755176012809	pt_BR
dc.contributor.advisor2	SANTANA, Renato Alexandre Costa de.
dc.contributor.advisor2Lattes	http://lattes.cnpq.br/1438381290031148	pt_BR
dc.contributor.referee1	CAMPOS, Ana Regina Nascimento.
dc.contributor.referee1Lattes	http://lattes.cnpq.br/9510211229362397	pt_BR
dc.contributor.referee2	ALVES, José Jailson Nicacio.
dc.contributor.referee2Lattes	http://lattes.cnpq.br/7986759552135066	pt_BR
dc.description.resumo	A eletrodeposição de um simples metal ou de suas ligas é atualmente de grande importância nas diversas áreas de engenharia e tecnologia. Dessa forma, as técnicas eletroquímicas para obtenção de revestimentos pelo processo de eletrodeposição são amplamente estudadas. Pelo processo de eletrodeposição podem ser obtidos filmes finos de óxidos metálicos com propriedades bem específicas para determinado uso. Através da utilização de métodos eletroquímicos é possível avaliar o comportamento relacionado a corrosão de um metal ou sua liga. Neste trabalho investigou-se os parâmetros operacionais para eletrodeposição da liga Ni-PW utilizando-se glicina como agente complexante. Para este estudo realizou-se um planejamento experimental 23, com composto central. As variáveis estudadas foram densidade de corrente, pH do banho eletrolítico e temperatura do banho. A liga Ni-P-W foi depositada sobre substrato de cobre de área superficial total de 8 cm2. A composição da liga foi obtida por meio da utilização de energia dispersiva de raios-X. A morfologia foi obtida por meio de microscopia eletronica de varredura. Foi feito medidas de difratometria de raios-X e de microdureza Vickers. No estudo de corrosão foram utilizadas as medidas de polarização potenciodinâmico linear realizados em NaCl 3,5%. As análise de composição química mostraram que as ligas obtidas apresentaram elevadas porcentagens de Ni e P e traços de W. As análises de morfologia das ligas obtidas mostram revestimentos com superfície homogênea e morfologia nodular bem definida para depósitos com maior porcentagem de P. Ligas com uma menor porcentagem de P apresentaram nódulos de tamanhos variados, e uma elevada quantidade de trincas. Os depósitos obtidos apresentaram comportamento amorfo. Os ensaios de corrosão mostraram que os revestimento obtido com densidade de corrente de 70 mA/cm2, pH 6,5 e temperatura de 63,5 oC apresentou os melhores resultados para resistência a polarização e corrente de corrosão.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Educação e Saúde - CES	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM CIÊNCIAS NATURAIS E BIOTECNOLOGIA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia e tecnologia	pt_BR
dc.title	Estudo do comportamento da eletrodeposição da liga ni-p-w utilizando glicina como complexante.	pt_BR
dc.date.issued	2015-04-16
dc.description.abstract	The electrodeposition of a simple metal or alloy is currently of great importance in many areas of engineering and technology. Thus, electrochemical techniques to obtain coatings by electrodeposition process are widely studied. By electrodeposition process there can be obtained thin films of metal oxides with very specific properties for specific use. Through the use of electrochemical methods it is possible to evaluate the corrosion related behavior of a metal or its alloy. In this study we investigated the operating parameters of Ni-P-W alloy plating using glycine as a complexing agent. For this study was made an experimental design 23 with central composite variables studied were current density, the electrolytic bath pH and bath temperature. The Ni-P-W alloy was deposited on copper substrate of total surface area 8 cm2. The composition of the alloy was obtained by using energy dispersive X-ray (EDX). The morphology of the Ni-PW electroplated alloy was obtained by Scanning Electronic Microscopy (SEM). Measurements of X-ray diffraction and Vickers microhardness were made. The linear potentiodynamic polarization (LPP) corrosion measurements were carried out in NaCl 3.5% in the study of corrosion. Chemical composition analysis showed that the obtained alloys showed high percentages of Ni and P and low of W. The analysis of the obtained alloys shows coatings with homogeneous surface and well defined nodular morphology for deposits with the highest percentage of P. Alloys with a lower percentage of P showed varying sizes of nodules, and a high percentage of cracks. The deposits obtained showed amorphous behavior. The corrosion tests showed that the coating obtained with current density 70 m/cm2, pH 6.5 and temperature of 63.5 °C showed the best results for the polarization resistance and corrosion current.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/1273
dc.date.accessioned	2018-07-27T13:48:39Z
dc.date.available	2018-07-27
dc.date.available	2018-07-27T13:48:39Z
dc.type	Dissertação	pt_BR
dc.subject	Eletrodeposição	pt_BR
dc.subject	Ligas metálicas	pt_BR
dc.subject	Ni-P-W	pt_BR
dc.subject	Glicina	pt_BR
dc.subject	Electrodeposición
dc.subject	Aleaciones metálicas
dc.subject	Ni-p-w
dc.subject	Glicina
dc.rights	Acesso Aberto	pt_BR
dc.creator	LINS, Mislene Pereira.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Study of the behavior of Ni-P-W alloy electrolytes using glycine as a complemente.	pt_BR
dc.title.alternative	Estudio del comportamiento de la electrodeposición de la aleación ni-p-w utilizando glicina como agente complejante.
dc.description.sponsorship	CNPq	pt_BR
dc.identifier.citation	LINS, Mislene Pereira. .Estudo do comportamento da eletrodeposição da liga ni-p-w utilizando glicina como complexante 2015. 71f. Dissertação (Mestrado em Ciências Naturais e Biotecnologia) – Programa de Pós-Graduação em Ciências Naturais e Biotecnologia PPGCNBiotec, Centro de Educação e Saúde, Universidade Federal Campina Grande - Cuité - Paraíba - Brasil, 2015.	pt_BR
dc.description.resumen	La electrodeposición de un solo metal o sus aleaciones es de gran importancia en la actualidad en diversas áreas de la ingeniería y la tecnología. Así, las técnicas electroquímicas para la obtención de recubrimientos por el proceso de electrodeposición son ampliamente estudiadas. Mediante el proceso de electrodeposición se pueden obtener películas delgadas de óxidos metálicos con propiedades muy específicas para un uso determinado. Mediante el uso de métodos electroquímicos es posible evaluar el comportamiento relacionado con la corrosión de un metal o su aleación. En este trabajo investigamos los parámetros operativos para la electrodeposición de aleación Ni-PW utilizando glicina como agente complejante. Para este estudio se realizó un diseño experimental 23, con un compuesto central. Las variables estudiadas fueron densidad de corriente, pH del baño electrolítico y temperatura del baño. La aleación Ni-P-W se depositó sobre un sustrato de cobre con una superficie total de 8 cm2. La composición de la aleación se obtuvo utilizando rayos X de energía dispersiva. La morfología se obtuvo mediante microscopía electrónica de barrido. Se realizaron mediciones de difractometría de rayos X y microdureza Vickers. En el estudio de corrosión se utilizaron medidas de polarización potenciodinámica lineal realizadas en NaCl al 3,5%. El análisis de composición química mostró que las aleaciones obtenidas presentaban altos porcentajes de Ni y P y trazas de W. Los análisis morfológicos de las aleaciones obtenidas muestran recubrimientos con superficie homogénea y morfología nodular bien definida para depósitos con mayor porcentaje de P. Aleaciones con un menor porcentaje de P mostró nódulos de diferentes tamaños y una gran cantidad de grietas. Los depósitos obtenidos mostraron un comportamiento amorfo. Las pruebas de corrosión mostraron que el recubrimiento obtenido con densidad de corriente de 70 mA/cm2, pH 6,5 y temperatura de 63,5 oC presentó los mejores resultados para la resistencia a la corriente de polarización y corrosión.