dc.creator.ID |
OLIVEIRA, J. A. M. |
pt_BR |
dc.creator.ID |
OLIVEIRA, JOSÉ ANDERSON MACHADO |
pt_BR |
dc.creator.ID |
OLIVEIRA, JOSÉ ANDERSON MACHADO DE |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/0336606752365569 |
pt_BR |
dc.contributor.advisor1 |
SILVA, Paulo Sérgio Gomes da. |
|
dc.contributor.advisor1ID |
Silva P S G |
pt_BR |
dc.contributor.advisor1ID |
SILVA, PAULO S. G. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/9463069127508798 |
pt_BR |
dc.contributor.referee1 |
FREITAS, Juliano Carlo Rufino de. |
|
dc.contributor.referee2 |
SANTANA, Renato Alexandre Costa de. |
|
dc.description.resumo |
A eletrodeposição de ligas metálicas e um processo mais sofisticado do que a de
metais puros, pois, requer um maior refinamento dos parâmetros operacionais para
sua obtenção. Na codeposição de ligas unem-se as características dos constituintes
metálicos para obter depósitos de melhor qualidade. As excelentes propriedades
físicas e químicas do tungstênio agregadas às do níquel contribuem para o aumento
na nobreza das ligas Ni-W. As soluções utilizadas para a obtenção dos depósitos
foram preparadas com água destilada e deionizada, utilizando-se reagentes de alta
pureza analítica. Como agentes complexantes utilizaram—se o tartarato e o oxalato
de sódio associados. Avaliaram-se os parâmetros operacionais e de composição
para o enriquecimento de tungstênio na liga Ni-W. O pH da solução foi ajustado para
três valores estudados neste trabalho: 7, 5 e 3. Adicionou-se ácido sulfúrico para
promover a solubilização dos reagentes e para avaliar a influência do pH na
composição química da liga. Observou-se que a proporção entre os metais Ni e W
variam de acordo com a diminuição no valor do pH da solução eletrolítica. Sendo o
pH a única variável no processo de eletrodeposição, nota-se que a diminuição do
mesmo favorece o aumento na proporção percentual em massa de tungstênio no
depósito obtido. A liga tratada termicamente na temperatura de 600 aC apresentou
uma inversão na proporção percentual em massa entre Ni e W, tal fato pode ser
explicado pela possível migração do níquel para o substrato de cobre nesta
temperatura. Notou-se um aumento considerável na dureza da liga quando
submetida ao tratamento de 600 aC. Os resultados obtidos das curvas de
polarização, obtidas em meio de NaCl 0,1 M, demonstram as características de
resistência a corrosão das ligas estudadas. Observa—se uma elevação do potencial
de corrosão com o decréscimo do pH, e consequentemente um aumento da
resistência de polarização. Este comportamento está associado ao maior teor de W
na liga obtida no menor valor de pH estudado. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Educação e Saúde - CES |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Espectroscopia |
pt_BR |
dc.title |
Estudo dos parâmetros operacionais e de composição para o enriquecimento de tungstênio na liga Ni-W. |
pt_BR |
dc.date.issued |
2014-07-22 |
|
dc.description.abstract |
The electroplating of metal alloys is a more sophisticated process than that of
pure metals, therefore, requires a further refinement of the operational parameters to
obtaining it. In the codeposition of alloys, the characteristics of the constituents are united
to obtain better quality deposits. The excellent properties
physical and chemical properties of tungsten added to nickel contribute to the increase
in the nobility of Ni-W alloys. The solutions used to obtain deposits
were prepared with distilled and deionized water, using high-quality reagents
analytical purity. As complexing agents, tartrate and oxalate were used
associated sodium The operational and composition parameters were evaluated
for the enrichment of tungsten in the Ni-W alloy. The pH of the solution was adjusted to
three values studied in this work: 7, 5 and 3. Sulfuric acid was added to
promote the solubilization of reagents and to evaluate the influence of pH on
chemical composition of the alloy. It was observed that the proportion between the metals Ni and W
vary according to the decrease in the pH value of the electrolyte solution. Being the
pH the only variable in the electrodeposition process, it is noted that the decrease in
even favors the increase in the mass percentage proportion of tungsten in the
obtained deposit. The heat-treated alloy at a temperature of 600 BC
an inversion in the mass percentage ratio between Ni and W, this fact can be
explained by the possible migration of nickel to the copper substrate in this
temperature. A considerable increase in alloy hardness was noted when
subjected to the treatment of 600 BC. The results obtained from the
polarization, obtained in 0.1 M NaCl medium, demonstrate the characteristics of
corrosion resistance of the studied alloys. An increase in the potential is observed
corrosion with decreasing pH, and consequently an increase in
polarization resistance. This behavior is associated with a higher content of W
in the alloy obtained in the lowest studied pH value. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/18984 |
|
dc.date.accessioned |
2021-05-24T12:21:58Z |
|
dc.date.available |
2021-05-24 |
|
dc.date.available |
2021-05-24T12:21:58Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Eletrodeposição |
pt_BR |
dc.subject |
Liga Ni-W |
pt_BR |
dc.subject |
Voltametria cíclica |
pt_BR |
dc.subject |
Eletroquímica |
pt_BR |
dc.subject |
Corrosão |
pt_BR |
dc.subject |
Electroplating |
pt_BR |
dc.subject |
Ni-W alloy |
pt_BR |
dc.subject |
Cyclic voltammetry |
pt_BR |
dc.subject |
Electrochemistry |
pt_BR |
dc.subject |
Corrosion |
pt_BR |
dc.subject |
Aleación de Ni-W |
pt_BR |
dc.subject |
Voltametría cíclica |
pt_BR |
dc.subject |
Galvanoplastia |
pt_BR |
dc.subject |
Electroquímica |
pt_BR |
dc.subject |
Corrosión |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
OLIVEIRA, José Anderson Machado. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Study of the operational and composition parameters for tungsten enrichment in Ni-W alloy. |
pt_BR |
dc.title.alternative |
Estudio de parámetros operativos y de composición para el enriquecimiento de tungsteno en aleación Ni-W. |
pt_BR |
dc.identifier.citation |
OLIVEIRA, José Anderson Machado. Estudo dos parâmetros operacionais e de composição para o enriquecimento de tungstênio na liga Ni-W. 2014. 47 fl. (Trabalho de Conclusão de Curso – Monografia), Curso de Licenciatura em química, Centro de Educação e Saúde, Universidade Federal de Campina Grande, Cuité – Paraíba – Brasil, 2014. |
pt_BR |
dc.description.resumen |
La galvanoplastia de aleaciones metálicas es un proceso más sofisticado que el de
metales puros, por lo tanto, requiere un mayor refinamiento de los parámetros operativos para
su obtención. En la codeposición de aleaciones, las características de los constituyentes están unidas
para obtener depósitos de mejor calidad. Las excelentes propiedades
Las propiedades físicas y químicas del tungsteno agregado al níquel contribuyen al aumento
en la nobleza de las aleaciones Ni-W. Las soluciones utilizadas para obtener depósitos
se prepararon con agua destilada y desionizada, utilizando reactivos de alta calidad
pureza analítica. Como agentes complejantes se utilizaron tartrato y oxalato.
sodio asociado Se evaluaron los parámetros operativos y de composición
para el enriquecimiento de tungsteno en la aleación Ni-W. El pH de la solución se ajustó a
tres valores estudiados en este trabajo: 7, 5 y 3. Se añadió ácido sulfúrico a
promover la solubilización de los reactivos y evaluar la influencia del pH en
composición química de la aleación. Se observó que la proporción entre los metales Ni y W
varían según la disminución del valor de pH de la solución de electrolito. Siendo el
pH la única variable en el proceso de electrodeposición, se observa que la disminución en
incluso favorece el aumento de la proporción porcentual de masa de tungsteno en el
deposito obtenido. La aleación tratada térmicamente a una temperatura de 600 AC.
una inversión en la relación porcentual de masa entre Ni y W, este hecho puede ser
explicado por la posible migración de níquel al sustrato de cobre en este
temperatura. Se notó un aumento considerable en la dureza de la aleación cuando
sometido al tratamiento del 600 a. C. Los resultados obtenidos de la
polarización, obtenida en medio NaCl 0,1 M, demuestran las características de
resistencia a la corrosión de las aleaciones estudiadas. Se observa un aumento en el potencial
corrosión con la disminución del pH y, en consecuencia, un aumento en la
Resistencia a la polarización. Este comportamiento está asociado a un mayor contenido de W
en la aleación obtenida en el valor de pH más bajo estudiado. |