Avaliação da permeação do hidrogênio através da liga Zn-Ni eletrodepositada sobre o aço SAE 1020.

Página inicial
→
Campus Campina Grande | Centro de Ciências e Tecnologia - CCT
→
PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA
→
Doutorado em Engenharia Química.
→
Ver item

dc.creator.Lattes	http://lattes.cnpq.br/2033392540252868	pt_BR
dc.contributor.advisor1	VILAR, Eudésio Oliveira.
dc.contributor.advisor1Lattes	http://lattes.cnpq.br/6363257813968241	pt_BR
dc.contributor.referee1	ALVES, Jose Jailson Nicacio.
dc.contributor.referee1Lattes	http://lattes.cnpq.br/7986759552135066	pt_BR
dc.contributor.referee2	SILVA, José Nilton.
dc.contributor.referee2Lattes	http://lattes.cnpq.br/7853090239572747	pt_BR
dc.contributor.referee3	ARAÚJO, Bruno Allison
dc.contributor.referee3Lattes	http://lattes.cnpq.br/0265579541739809	pt_BR
dc.contributor.referee4	LIMA, Juliana de Figueiredo
dc.contributor.referee4Lattes	http://lattes.cnpq.br/6140386020886145	pt_BR
dc.description.resumo	A fragilização por hidrogênio, de um metal ou liga, é um problema industrial que pode levar a danos estruturais, quando em condições ótimas acontecerá. Com base nesta premissa o presente estudo teve como objetivo estudar o efeito mitigador da permeação do hidrogênio, pela liga Zn-Ni eletrodepositada sobre Aço SAE 1020. Esta liga, com baixo teor de carbono, é um dos aços mais comumente utilizados na indústria de processo, com excelente relação custo benefício comparado com outros aços destinados ao mesmo propósito. Foram escolhidas duas metodologias para galvanizar este aço com a liga Zn- Ni; uma a base de cloretos e outra a base de sulfatos, com intuito de comparar seus efeitos à permeação de hidrogênio. Inicialmente, foi realizada uma caracterização da corrosão eletroquímica destes e sua análise morfológica, onde ficou constatado que estes revestimentos protegem o metal de base tanto à corrosão quanto a difusão de hidrogênio, porém o processo de eletrodeposição do Zn-Ni a base de sulfatos obteve uma maior concentração de níquel e melhor resistência a corrosão de acordo com os dados obtidos e permeação. Os revestimentos de Zn-Ni diminuíram a susceptibilidade do SAE 1020 à permeação por hidrogênio; onde o revestimento a base de sulfatos obteve razão de alongamento de 95%.	pt_BR
dc.publisher.country	Brasil	pt_BR
dc.publisher.department	Centro de Ciências e Tecnologia - CCT	pt_BR
dc.publisher.program	PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA	pt_BR
dc.publisher.initials	UFCG	pt_BR
dc.subject.cnpq	Engenharia Química	pt_BR
dc.title	Avaliação da permeação do hidrogênio através da liga Zn-Ni eletrodepositada sobre o aço SAE 1020.	pt_BR
dc.date.issued	2021-09-23
dc.description.abstract	The embrittlement by hydrogen, of a metal or an alloy, is an industrial problem that can lead to structural damage, when in optimal conditions it will happen. Based on this premise, the present study aimed to study the mitigating effect of hydrogen permeation, by the Zn-Ni alloy electrodeposited on SAE 1020 Steel. This alloy, with low carbon content, is one of the most commonly used steels in the process industry , with an excellent cost-benefit ratio compared to other steels intended for the same purpose. Two methodologies were chosen to galvanize this steel with the Zn-Ni alloy; one based on chlorides and the other based on sulfates, in order to compare their effects to hydrogen permeation. Initially, a characterization of the electrochemical corrosion of these and its morphological analysis was performed, where it was found that these coatings protect the base metal both to corrosion and hydrogen diffusion, but the Zn-Ni electrodeposition process based on sulfates obtained a higher nickel concentration and better corrosion resistance according to the obtained data and permeation. Zn-Ni coatings decreased the susceptibility of SAE 1020 to hydrogen permeation; where the coating based on sulfates obtained an elongation ratio of 95%.	pt_BR
dc.identifier.uri	http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/22655
dc.date.accessioned	2021-12-20T15:32:47Z
dc.date.available	2021-12-20
dc.date.available	2021-12-20T15:32:47Z
dc.type	Tese	pt_BR
dc.subject	Fragilização por hidrogênio	pt_BR
dc.subject	Permeação por hidrogênio	pt_BR
dc.subject	Aço SAE 1020	pt_BR
dc.subject	Eletrodeposição de Zn-Ni	pt_BR
dc.subject	Corrosão	pt_BR
dc.subject	Hydrogen embrittlement	pt_BR
dc.subject	hydrogen permeation	pt_BR
dc.subject	SAE 1020 steel	pt_BR
dc.subject	Zn-Ni electrodeposition	pt_BR
dc.subject	Corrosion	pt_BR
dc.rights	Acesso Aberto	pt_BR
dc.creator	CARVALHO, João Paulo Dantas de.
dc.publisher	Universidade Federal de Campina Grande	pt_BR
dc.language	por	pt_BR
dc.title.alternative	Evaluation of hydrogen permeation through the Zn-Ni alloy electrodeposited on SAE 1020 steel.
dc.description.sponsorship	Capes	pt_BR
dc.identifier.citation	CARVALHO, João Paulo Dantas de. Avaliação da permeação do hidrogênio através da liga Zn-Ni eletrodepositada sobre o aço SAE 1020. 121f. Tese (Doutorado em Engenharia Química) - Programa de Pós- Graduação em Engenharia Química, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2021. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/22655	pt_BR