dc.creator.Lattes |
http://lattes.cnpq.br/0625690569373047 |
pt_BR |
dc.contributor.advisor1 |
FOOK, Marcus Vinicius Lia. |
|
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/4149843752530120 |
pt_BR |
dc.contributor.referee1 |
NEVES, Gelmires de Araujo. |
|
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/3167458244674160 |
pt_BR |
dc.contributor.referee2 |
WELLEN, Renate Maria Ramos. |
|
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/5406259642631461 |
pt_BR |
dc.contributor.referee3 |
PINTO, Maria Roberta de Oliveira. |
|
dc.contributor.referee3Lattes |
http://lattes.cnpq.br/9225790526299506 |
pt_BR |
dc.contributor.referee4 |
AMOAH, Solomon Kweku Sagoe. |
|
dc.contributor.referee4Lattes |
http://lattes.cnpq.br/6445921030833387 |
pt_BR |
dc.description.resumo |
O Traumatismo Crânio-Encefálico (TCE) é uma situação comum nos hospitais de
trauma, e tem se tornado responsável pelas elevadas taxas de morbidade e
mortalidade em todo o mundo, constituindo-se assim em um problema de saúde
pública com grande impacto socioeconômico, devido às consequências. O TCE
pode se apresentar de diversas formas, entretanto, necessitam de reconhecimento
precoce tanto no atendimento primário como no exame clínico e neurológico para
iniciar os procedimentos avançados de apoio à vida e diminuir a incidência de lesões
neuronais secundárias ao trauma. Quando a vítima de TCE é acometida por lesões
na calota craniana em que há necessidade de enxertos, há uma dificuldade em
relação à reposição do osso e disponibilidade de materiais adequados com um custo
acessível. Com a evolução dos biomateriais, os aloplásticos vêm sendo utilizados
com maior frequência nos TCE, dentre eles o Poli éter-éter-cetona (PEEK) que é um
polímero biocompatível de alto desempenho quando comparado aos polímeros
tradicionais. Sendo assim, este trabalho tem como objetivo desenvolver e avaliar
estruturas compostas de PEEK para a realização de Cranioplastia. As amostras
foram obtidas através da técnica de compressão, modulando a porosidade das fases
utilizando Cloreto de Sódio (NaCl), as mesmas foram posteriormente lixiviadas para
formação dos poros. A matéria prima foi caracterizada por Espectroscopia no
Infravermelho com Transformada de Fourier (FTIR), Calorimetria Exploratória
Diferencial (DSC) e Termogravimetria (TG). Para as amostras que simulam a calota
craniana foram caracterizadas por Microscopia Ótica (MO), Microscopia de Força
Atômica (AFM) Molhabilidade por medida do ângulo de contato, Resistência a
Compressão e Citotoxicidade. No resultado de FTIR observou-se bandas típicas de
absorção do PEEK. Através da análise de DSC foi possível observar comportamento
de um material semicristalino, quanto aos valores obtidos no ensaio de TG, o PEEK
apresenta apenas um pico de perda de massa, que corresponde à degradação,
sendo observada uma perda de massa de 46,91% a qual se inicia em 532ºC e vai
até 700° C. Ao analisar a morfologia da superfície das amostras, observou-se uma
superfície aparentemente rugosa sem poros, foi visto também que a superfície que
fica em contato com pastilha de sal apresenta uma certa orientação preferencial,
possivelmente acentuada pelo processo de acabamento. Na AFM percebe-se que
todas as amostras possuem uma superfície rugosa, com orientação preferencial nas
cadeias (sulcos paralelos), que corrobora as imagens obtidas na microscopia ótica.
No resultado da Molhabilidade, viu-se que as amostras apresentaram ângulo de
contato em torno de 50 a 60° indicando perfil característico de material hidrofílico. Na
resistência a compressão verificou-se que a deformação máxima das amostras foi
de aproximadamente 20% e a deformação mínima em quase 13,78%. O ensaio de
Citotoxicidade indicou a biocompatibilidade do material. Conclui-se que os
resultados apontam para efetividade da metodologia utilizada, mimetizando de forma
promissora a estrutura básica da calota craniana, sendo possível inferir que as
amostras apresentam potencial para serem utilizadas em cranioplastia. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.department |
Transformada de Fourier |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Materiais |
pt_BR |
dc.title |
Desenvolvimento de estruturas compostas de PEEK para cranioplastia. |
pt_BR |
dc.date.issued |
2018-11-16 |
|
dc.description.abstract |
Cranio-encephalic trauma (TBI) is a common situation in trauma hospitals and has
become responsible for the high rates of morbidity and mortality worldwide, thus
constituting a public health problem with great socioeconomic impact due to its
consequences. The ECT can present in several ways, however, they need early
recognition in both primary care and clinical and neurological examination to initiate
advanced procedures to support life and reduce the incidence of neuronal lesions
secondary to trauma. When the victim of TBI is affected by injuries to the skullcap
where there is a need for grafting, there is a difficulty regarding bone replacement
and the availability of suitable materials at an affordable cost. With the evolution of
biomaterials, alloplastics have been used more frequently in TCE, among them
Polyether ether-ketone (PEEK), which is a biocompatible polymer of high
performance when compared to traditional polymers. Therefore, this work aims to
develop and evaluate composite structures of PEEK for the accomplishment of
Cranioplasty. The samples were obtained through the compression technique,
modulating the porosity of the phases using sodium chloride (NaCl), which were later
leached to form the pores. The raw material was characterized by Infrared
Spectroscopy with Fourier Transform (FTIR), Differential Exploration Calorimetry
(DSC) and Thermogravimetry (TG). For the samples that simulated the skull cap
were characterized by Optical Microscopy (MO), Atomic Force Microscopy (AFM)
Wettability by contact angle measurement, Compression Resistance and
Cytotoxicity. In the FTIR result, typical bands of PEEK absorption were observed. By
the DSC analysis it was possible to observe the behavior of a semicrystalline
material, in relation to the values obtained in the TG test, PEEK presents only a mass
loss peak corresponding to degradation, with a loss of mass of 46.91% which starts
at 532 ° C and goes up to 700 ° C. When analyzing the surface morphology of the
samples, an apparently rugose surface without pores was observed, it was also seen
that the surface that comes in contact with the salt tablet has a certain orientation
preferable, possibly accentuated by the finishing process. In the AFM, all the
samples have a rough surface, with a preferred orientation in the chains (parallel
grooves), which corroborates the images obtained by optical microscopy. In the
result of the wettability, the samples showed a contact angle around 50 to 60 °
indicating a characteristic profile of hydrophilic material. In the compressive strength
it was verified that the maximum deformation of the samples was approximately 20%
and the minimum deformation was almost 13.78%. The cytotoxicity assay indicated
the biocompatibility of the material. It is concluded that the results point to the
effectiveness of the methodology used, promisingly mimicking the basic structure of
the skull cap, and it is possible to infer that the samples have potential to be used in
cranioplasty. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/23472 |
|
dc.date.accessioned |
2022-02-10T18:57:38Z |
|
dc.date.available |
2022-02-10 |
|
dc.date.available |
2022-02-10T18:57:38Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Biomateriais |
pt_BR |
dc.subject |
Polímeros de cetona |
pt_BR |
dc.subject |
Traumatismo crânio- encefálico |
pt_BR |
dc.subject |
Biomaterials |
pt_BR |
dc.subject |
Ketone polymers |
pt_BR |
dc.subject |
Cranio-encephalic trauma |
pt_BR |
dc.subject |
Traumatismo crânio-encefálico |
pt_BR |
dc.subject |
Espectroscopia no infravermelho |
pt_BR |
dc.subject |
Calorimetria exploratória diferencial |
pt_BR |
dc.subject |
Microscopia de força atômica |
pt_BR |
dc.subject |
Microscopia ótica |
pt_BR |
dc.subject |
Calorimetria exploratória diferencial |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
BRITTO FILHO, Claudio Orestes. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Development of PEEK composite structures for cranioplasty. |
|
dc.identifier.citation |
BRITTO FILHO, Claudio Orestes. Desenvolvimento de estruturas compostas de PEEK para cranioplastia. 71 f. Tese (Doutorado em Ciência e Engenharia de Materiais) - Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2018. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/23472 |
pt_BR |