dc.creator.Lattes |
http://lattes.cnpq.br/4237136708419469 |
pt_BR |
dc.contributor.advisor1 |
FOOK, Marcus Vinícius Lia. |
|
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/4149843752530120 |
pt_BR |
dc.contributor.advisor-co1 |
BARBOSA, Rossemberg Cardoso. |
|
dc.contributor.advisor-co1Lattes |
http://lattes.cnpq.br/3078704003282914 |
pt_BR |
dc.contributor.referee1 |
SILVA, Suédina Maria de Lima. |
|
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/6437959556217825 |
pt_BR |
dc.contributor.referee2 |
PINTO, Maria Roberta de Oliveira. |
|
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/9225790526299506 |
pt_BR |
dc.description.resumo |
Este trabalho teve como objetivo desenvolver telas a partir da tecelagem de fios mono
e multifilamentares de quitosana obtidos por fiação úmida para possíveis aplicações
biomédicas. Além disso, etapas do processo de fiação úmida foram otimizadas para
obter fibras com propriedades mecânicas adequadas ao processo de tecelagem. Para
o processo de fiação úmida foram utilizadas solução de quitosana a 4% (m/V) e banho
de coagulação contendo 70% de hidróxido de sódio (0,5M)/30% de metanol. A cinética
de coagulação da fibra foi avaliada por Microscopia Ótica (MO); a metodologia de
secagem foi avaliada por Análise Termogravimétria (TGA), Difratometria de Raios-X
(DRX) e ensaio mecânico sob tração. O tempo ideal de coagulação foi determinado e
a metodologia de secagem mostrou-se eficiente. A partir dos resultados de tração e
DRX, optou-se pela condição de secagem dos fios sob tensão. Os fios mono e
multifilamentares obtidos foram caracterizados por ensaio mecânico sob tração e
Microscopia Eletrônica de Varredura (MEV). A configuração do fio afetou suas
propriedades mecânicas, além disso, verificou-se a partir dos ensaios morfológicos
que os fios conservam as características dos filamentos individuais, apresentando a
microestrutura típica de fibras obtidas por fiação úmida. As telas obtidas foram
avaliadas por MO, ensaio mecânico sob tração, grau de intumescimento,
biodegradação enzimática in vitro e citotoxicidade in vitro. A partir dos ensaios de
tração e MO optou-se pelo revestimento com uma solução de quitosana a 1,5% (m/V).
As telas obtidas a partir dos fios trifilamentares resistiram à cargas mais elevadas. A
resistência a tração das amostras no estado úmido mostrou-se semelhante à derme
humana. A configuração do fio utilizado na tecelagem influenciou diretamente a
quantidade de água absorvida e a cinética de degradação enzimática das telas. Os
resultados do ensaio de citotoxicidade in vitro, mostraram que as amostras
apresentaram ausência de citotoxicidade, sendo classificadas como satisfatórias.
Assim, obteve-se telas de quitosana com boas propriedades mecânicas,
biodegradáveis e biocompatíveis, com potencial para aplicações biomédicas, como
curativos bioativos, enxertos para engenharia de tecidos, reforço para tecidos moles
ou ainda como sistema de liberação controlada de fármacos. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia de Materiais |
pt_BR |
dc.title |
Processamento de fios de quitosana em telas para aplicações biomédicas. |
pt_BR |
dc.date.issued |
2019-08-26 |
|
dc.description.abstract |
The objective of this work was to develop meshes from the weaving of monofilament
and multifilaments chitosan threads obtained by wet spinning for possible biomedical
applications. In addition, wet spinning process steps have been optimized to obtain
fibers with mechanical properties suitable for the weaving process. For the wet
spinning process 4% chitosan solution (w / v) and coagulation bath containing 70%
(0.5M) sodium hydroxide/30% methanol were used. Fiber coagulation kinetics was
evaluated by Optical Microscopy (OM); The drying methodology was evaluated by
Thermogravimetric Analysis (TGA), X-ray Diffractometry (XRD) and tensile test. The
ideal coagulation time was determined and the drying methodology was efficient. From
the results of tensile and XRD, it was chosen for the condition of drying of the wires
under tension. The monofilament and multifilaments wires obtained were characterized
by tensile test and Scanning Electron Microscopy (SEM). The configuration of the yarn
affected its mechanical properties. Moreover, it was verified from the morphological
tests that the yarns preserve the characteristics of the individual filaments present the
typical microstructure of fibers obtained by wet spinning. The woven meshes obtained
were evaluated by OM, tensile test, swelling degree, in vitro enzymatic biodegradation
and in vitro cytotoxicity. From the tensile and OM tests it was decided to coat with a
1,5% chitosan solution (w / v). The woven mesh obtained from the tri-filament yarns
withstood higher loads. The tensile strength of the samples in the wet state was similar
to the human dermis. The configuration of the yarn used in weaving directly influenced
the amount of water absorbed and the enzymatic degradation kinetics of the fabrics.
The results of the in vitro cytotoxicity test showed that the samples showed no
cytotoxicity and were classified as satisfactory. Thus, chitosan woven mesh with good
mechanical, biodegradable and biocompatible properties were obtained, with potential
for biomedical applications, such as bioactive dressings, tissue engineering grafts, soft
tissue reinforcement or even as a controlled drug release system. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/23520 |
|
dc.date.accessioned |
2022-02-14T17:05:31Z |
|
dc.date.available |
2022-02-14 |
|
dc.date.available |
2022-02-14T17:05:31Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Quitosana |
pt_BR |
dc.subject |
Fiação úmida |
pt_BR |
dc.subject |
Fios |
pt_BR |
dc.subject |
Tecelagem |
pt_BR |
dc.subject |
Telas |
pt_BR |
dc.subject |
Biotêxteis |
pt_BR |
dc.subject |
Chitosan |
pt_BR |
dc.subject |
Wet spinning |
pt_BR |
dc.subject |
Wires |
pt_BR |
dc.subject |
Weaving |
pt_BR |
dc.subject |
Woven mesh |
pt_BR |
dc.subject |
Biotextiles |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SILVA, Henrique Nunes da. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Processing chitosan threads into screens for biomedical applications. |
|
dc.description.sponsorship |
Capes |
pt_BR |
dc.identifier.citation |
SILVA, Henrique Nunes da. Processamento de fios de quitosana em telas para aplicações biomédicas. 103 f. Dissertação (Mestrado em Ciência e Engenharia de Materiais) - Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande, Paraíba, Brasil, 2019. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/23520 |
pt_BR |