dc.creator.ID |
SILVA, Y. M. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/0526124346405305 |
pt_BR |
dc.contributor.advisor1 |
SIMPLÍCIO , Marcos Antônio de Souza. |
|
dc.contributor.advisor1ID |
SIMPLÍCIO, M. A. S. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/5090248192860158 |
pt_BR |
dc.contributor.referee1 |
SILVA, José Bezerra da. |
|
dc.contributor.referee1ID |
SILVA, J. B. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/8531283237997416 |
pt_BR |
dc.contributor.referee2 |
ANJOS, Cássia Mendonça dos. |
|
dc.contributor.referee2ID |
ANJOS, C. M. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/0763317847663674 |
pt_BR |
dc.description.resumo |
O concreto consiste em um dos materiais mais empregados na construção civil. Diversos
avanços vêm sendo realizados a fim de se obter um concreto com melhores características e
um deles consiste no concreto de alto desempenho (CAD). A partir de aditivos e adições este
tipo de concreto atinge excelentes propriedades, em que, uma das formas de obtenção destes
resultados consiste na incorporação de fibras de aço a matriz cimentícia. Entretanto, existem
diversas lacunas a serem preenchidas no que se refere às suas propriedades, como a aderência,
que representa um dos fatores primordiais para um bom funcionamento do concreto e deve ser
cautelosamente analisada. Diante do contexto, este trabalho consiste em propor uma análise
da influência da adição de fibras de aço na aderência aço-concreto através do ensaio push-out
test. Para esta análise foram confeccionados corpos de prova prismáticos com aresta de 20 cm
e comprimento de ancoragem de 2,5Ø, utilizando barras de aço nervuradas nos diâmetros de
10, 12,5 e 16 mm e concreto dosado para um fck correspondente a 60 MPa. Além do efeito
das fibras, foi avaliada a correlação existente entre o diâmetro da barra e a tensão máxima de
aderência. Através dos resultados obtidos, foi possível constatar que a adição de fibras de aço
melhora a aderência, bem como a resistência à compressão do concreto, no qual, o diâmetro
que apresentou melhores resultados foi o de 16 mm. Além disso, foi possível concluir que os
resultados teóricos, fornecidos pela expressão da ABNT NBR 6118/2014 mostraram-se
inferiores aos obtidos experimentalmente. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Tecnologia e Recursos Naturais - CTRN |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Engenharia Civil |
pt_BR |
dc.title |
Estudo da aderência entre barras de aço e concreto de alto desempenho reforçado com fibras metálicas. |
pt_BR |
dc.date.issued |
2017 |
|
dc.description.abstract |
Concrete consists of one of the materials most used in construction. Several advances have
been made in order to obtain a concrete with better characteristics and one of them consists of
high performance concrete (CAD). From additives and additions, this type of concrete
achieves excellent properties, where one of the ways of obtaining these results is the
incorporation of steel fibers into the cementitious matrix. However, there are several gaps to
be filled in regard to their properties, such as bond, which is one of the key factors for a
smooth operation of the concrete and should be carefully considered. Considering the context,
this work consists in proposing an analysis of the influence of the addition of steel fibers in
the steelconcrete bond through the pushout test. For this analysis prismatic test pieces with a
20 cm edge and 2.5Ø anchorage length were made using steel bars in the diameters of 10,
12.5 and 16 mm and concrete compressive strength of 60 MPa. In addition to the effect of the
fibers, the correlation between the diameter of the bar and the maximum bond strength was
evaluated. Through the results obtained, it was possible to verify that the addition of steel
fibers improves the bond strength as well as the compressive strength of the concrete, where
the diameter that presented the best results was 16 mm. In addition, it was possible to
conclude that the theoretical results, provided by the ABNT NBR 6118/2014 expression were
inferior to those obtained experimentally. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/23954 |
|
dc.date.accessioned |
2022-03-21T13:34:04Z |
|
dc.date.available |
2022-03-21 |
|
dc.date.available |
2022-03-21T13:34:04Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Concreto de alto desempenho |
pt_BR |
dc.subject |
Fibras metálicas e concreto |
pt_BR |
dc.subject |
Barras de aço e concreto |
pt_BR |
dc.subject |
Aderência entre barras de aço e concreto |
pt_BR |
dc.subject |
NBR 6118/2014 |
pt_BR |
dc.subject |
Fibras de aço |
pt_BR |
dc.subject |
Matriz cimentícia e fibras de aço |
pt_BR |
dc.subject |
Concreto reforçado com fibras |
pt_BR |
dc.subject |
Compósitos |
pt_BR |
dc.subject |
High performance concrete |
pt_BR |
dc.subject |
Metal fibers and concrete |
pt_BR |
dc.subject |
Steel and concrete bars |
pt_BR |
dc.subject |
Adhesion between steel bars and concrete |
pt_BR |
dc.subject |
Steel fibers |
pt_BR |
dc.subject |
Cement matrix and steel fibers |
pt_BR |
dc.subject |
Fiber reinforced concrete |
pt_BR |
dc.subject |
Composites |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SILVA, Yana de Medeiros. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Study of adhesion between steel bars and high performance concrete reinforced with metallic fibers. |
pt_BR |
dc.identifier.citation |
SILVA, Yana de Medeiros. Estudo da aderência entre barras de aço e concreto de alto desempenho reforçado com fibras metálicas. 2017. 80f. Trabalho de Conclusão de Curso (Monografia), Curso de Bacharelado em Engenharia Civil, Centro de Tecnologia e Recursos Naturais, Universidade Federal de Campina Grande - Campina Grande - Paraíba - Brasil, 2017. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/23954 |
pt_BR |