dc.description.resumo |
A utilização dos diversos biomateriais existentes tem sido uma prática frequentemente
estudada e utilizada na ortopedia veterinária, devido à necessidade de adequação mecânica de
implantes e enxertos ao meio biológico onde será implantado. Os implantes à base de silicato
de cálcio são possíveis substitutos do tecido ósseo, assim como todo composto que possui
silicato em sua estrutura, apresentando favorável biocompatibilidade, desencadeando uma
resposta osteogênica através da estimulação e ativação das células osteoblásticas.
Recentemente tem sido proposta uma nova biocerâmica inspirada no Bioeutectic. Ela é
produzida mediante a sinterização de uma mistura de pós de α-Ca3(PO4)2 e α-CaSiO3 com a
composição do ponto eutéctico do sistema (40 %m α-Ca3(PO4)2 60 %m α-CaSiO3) a 1350 oC.
Objetivou-se com este estudo analisar a funcionalidade histológica e morfológica da
biocerâmica composta por silicato de cálcio na reparação óssea, comparado a reparação
fisiológica sem auxílio de implantes de qualquer outra natureza, em tíbias de coelhos. Foram
utilizados 10 coelhos adultos, machos, da raça Nova Zelândia, hígidos, pesando em média 3,5
kg. Nas regiões metafisárias proximal e distal de ambas as tíbias, criou-se em cada uma delas
um defeito circular em plano ósseo medindo 2,4 mm de diâmetro. Em um dos membros
implantou-se o silicato de cálcio em ambos os defeitos criados. Os resultados obtidos
demonstraram uma menor formação óssea das regiões onde o silicato de cálcio foi
implantado, em relação à resposta da reparação fisiológica. Conclui-se que o implante de
silicato de cálcio se mostrou bioativo, osteocondutor, e não citotóxico, porém retardou a
cicatrização óssea. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Saúde e Tecnologia Rural - CSTR |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Medicina Veterinária |
pt_BR |
dc.title |
Avaliação histológica da reparação óssea utilizando implantes de silicato de cálcio em tíbia de coelhos. |
pt_BR |
dc.date.issued |
2016-12 |
|
dc.description.abstract |
Histological Evaluation of Bone Repair Using Calcium Silicate Implants in Rabbit Tibia. The use of the various existing biomaterials has been a practice frequently studied and
used in veterinary orthopedics, due to the necessity of the mechanical adequacy of implants
and grafts to the biological environment where it will be implanted. Calcium silicate implants
are possible substitutes for bone tissue, as well as any compound that has silicate in its
structure, presenting favorable biocompatibility, triggering an osteogenic response through the
stimulation and activation of the osteoblastic cells. Recently, a new bioceramic inspired by
Bioeutectic has been proposed. It’s produced by sintering a mixture of α-Ca 3 (PO 4) 2 and α-
CaSiO 3 powders with the eutectic dot composition of the system (40% m α-Ca 3 (PO 4) 2
60% m α-CaSiO 3) at 1350 ° C. The purpose of this study was analyze the histological and
morphological functionality of the bioceramics which are composed of calcium silicate in the
bone repair, compared to the physiological repair without the aid of implants of any other
nature, in rabbit’s tibia. Ten healthy male New Zealand rabbits weighing on average 3.5 kg
were used. In the proximal and distal metaphyseal regions of both tibias, a circular defect in
the bone plane measuring 2.4 mm in diameter was created. In one of the limbs calcium
silicate was implanted in both created defects. The obtained results demonstrated a smaller
bone formation of the regions where the calcium silicate was implanted, in relation to the
response of the physiological repair. It was concluded that the calcium silicate implant was
bioactive, osteoconductive, and non-cytotoxic, but delayed bone healing. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/24124 |
|
dc.date.accessioned |
2022-03-25T13:05:51Z |
|
dc.date.available |
2022-03-25 |
|
dc.date.available |
2022-03-25T13:05:51Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Avaliação histológica |
pt_BR |
dc.subject |
Reparação óssea |
pt_BR |
dc.subject |
Implantes de silicato de cálcio |
pt_BR |
dc.subject |
Biomateriais |
pt_BR |
dc.subject |
Coelhos - tíbia |
pt_BR |
dc.subject |
Tíbia de coelhos |
pt_BR |
dc.subject |
Sistema ósseo |
pt_BR |
dc.subject |
Biocerâmicas |
pt_BR |
dc.subject |
Histological evaluation |
pt_BR |
dc.subject |
Bone repair |
pt_BR |
dc.subject |
Calcium silicate implants |
pt_BR |
dc.subject |
Biomaterials |
pt_BR |
dc.subject |
Rabbits - tibia |
pt_BR |
dc.subject |
Rabbit tibia |
pt_BR |
dc.subject |
Bone system |
pt_BR |
dc.subject |
Bioceramics |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
ALEXANDRE, Peterson Renê da Silva. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Histological evaluation of bone repair using calcium silicate implants in rabbit tibia. |
pt_BR |
dc.identifier.citation |
ALEXANDRE, Peterson Renê da Silva. Avaliação histológica da reparação óssea utilizando implantes de silicato de cálcio em tíbia de coelhos. 2016. 39f. Trabalho de Conclusão de Curso (Monografia), Curso de Bacharelado em Medicina Veterinária, Centro de Saúde e Tecnologia Rural, Universidade Federal de Campina Grande - Patos - Paraíba - Brasil, 2016. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/24124 |
pt_BR |