dc.creator.ID |
MOREIRA, A. M. A. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/3827178942982194 |
pt_BR |
dc.contributor.advisor1 |
CATÃO, Carmem Dolores de Sá. |
|
dc.contributor.advisor1ID |
CATÃO, C. D. S. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/7173639352326441 |
pt_BR |
dc.contributor.referee1 |
GUEDES, Maria Carolina Bandeira Macena. |
|
dc.contributor.referee1ID |
GUEDES, M. C. B. M. |
pt_BR |
dc.contributor.referee2 |
RODRIGUES, Rachel de Queiroz Ferreira. |
|
dc.contributor.referee2ID |
RODRIGUES, R. Q. F. |
pt_BR |
dc.description.resumo |
As ligas de NiTi são amplamente utilizadas em dispositivos da área odontológica, como na
Implantodontia, devido as suas propriedades de biocompatibilidade, memória de forma e
superelasticidade. Assim, o presente estudo teve como objetivo avaliar a bioatividade e as
características morfológicas de liga de NiTi (45,3% de Ni e 54,7% de Ti), tratadas a laser com
e sem recobrimento de apatita. Dessa forma, as ligas de NiTi foram obtidas pela técnica
Plasma Skull Push Pull, posteriormente as amostras foram tratadas superficialmente a laser
(Yb:YAG) e pelo método biomimético em SBF-0 e SBF-6 (Simulated Body Fluid), ambas a
1,5 M. A análise de bioatividade foi realizada por meio da pesagem, espectroscopia por
energia dispersiva de raios X (EDS) e microscopia eletrônica de varredura (MEV). As
espectroscopias revelaram aumento na concentração de oxigênio e carbono após a ablação,
favorecendo a difusão de átomos de oxigênio e formação de óxidos de titânio. Após a
deposição da apatita pelo método biomimético em SBF-0 e 6, o recobrimento apresentou uma
razão molar de Ca/P de aproximadamente 1,0, caracterizando a formação de apatitas de baixa
cristalinidade. Pôde-se constatar que a associação da irradiação a laser e deposição química
de apatitas pelo método biomimético em SBF-6, embora tenha demonstrado um melhor
desempenho quanto à bioatividade e topografia das ligas, o ganho de massa não foi
estatisticamente significativo ao nível de 5%. Tais propriedades podem contribuir para maior
interação do biomaterial com o meio biológico e possível redução no tempo de
osseointegração. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Saúde e Tecnologia Rural - CSTR |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Odontologia |
pt_BR |
dc.title |
Avaliação da bioatividade de ligas de NiTi tratadas a laser para aplicação em implantes dentários. |
pt_BR |
dc.date.issued |
2014-08-13 |
|
dc.description.abstract |
NiTi alloys are widely used in devices for dentistry, as in dental implants, due to their
biocompatible, shape memory and superelasticity. Thus, the present study aimed to evaluate
the bioactivity and the morphological characteristics of NiTi alloy (45.3% Ni and 54.7% Ti),
treated with laser and uncoated apatite. Thus, the NiTi alloys were obtained by the technique
Plasma Skull Push Pull, the samples were subsequently treated superficially laser (Yb: YAG)
and the biomimetic method in SBF-0 and SBF-6 (Simulated Body Fluid), both 1,5 M. The
bioactivity analysis was performed by weighing spectroscopy, energy dispersive X-ray (EDS)
and scanning electron microscopy (SEM). The spectroscopy revealed increased concentration
of oxygen and carbon after ablation, favoring the diffusion of oxygen atoms and formation of
titanium oxides. After the biomimetic apatite deposition method on SBF-0 and 6, the coating
had a molar ratio of Ca/P ratio of 1,0, characterizing the formation of low crystalline apatite.
It could be observed that the combination of laser irradiation and chemical deposition of
apatite by biomimetic method in SBF-6, but has shown a better performance in terms of
bioactivity and topography of the alloy, the mass gain was not statistically significant at 5 %.
These properties may contribute to greater interaction of the biomaterial with the biological
environment and possible reduction in the time of osseointegration. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/24815 |
|
dc.date.accessioned |
2022-04-25T17:44:58Z |
|
dc.date.available |
2022-04-25 |
|
dc.date.available |
2022-04-25T17:44:58Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Ligas de NiTi |
pt_BR |
dc.subject |
Implantes dentários |
pt_BR |
dc.subject |
Apatitas |
pt_BR |
dc.subject |
Osseointegração |
pt_BR |
dc.subject |
Implantodontia |
pt_BR |
dc.subject |
Plasma Skull Push Pull |
pt_BR |
dc.subject |
NiTi alloys |
pt_BR |
dc.subject |
Dental implants |
pt_BR |
dc.subject |
Apatites |
pt_BR |
dc.subject |
Osseointegration |
pt_BR |
dc.subject |
Implantology |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
MOREIRA, Anny Mirene Alves. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Bioactivity evaluation of laser-treated NiTi alloys for application in dental implants. |
pt_BR |
dc.identifier.citation |
MOREIRA, Anny Mirene Alves. Avaliação da bioatividade de ligas de NiTi tratadas a laser para aplicação em implantes dentários. 2014. 62f. Trabalho de Conclusão de Curso (Artigo), Curso de Bacharelado em Odontologia, Centro de Saúde e Tecnologia Rural, Universidade Federal de Campina Grande - Patos - Paraíba - Brasil, 2014. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/24815 |
pt_BR |