dc.description.resumo |
Em decorrência da diversidade de ligas disponíveis, com seus diversos métodos
de fabricação, é importante ao ortodontista conhecer suas propriedades e as variáveis
relacionadas, para planejar o tratamento e otimizar os resultados clínicos, assim como
preservar a histofisiologia do periodonto do paciente. Dessa forma, o objetivo deste estudo foi
avaliar e comparar in vitro as propriedades termomecânicas de fios ortodônticos
superelásticos pré-contornados de níquel-titânio de duas marcas comerciais. Métodos: Foram
utilizadas as marcas comerciais Morelli® (Grupo 1) e Orthometric® (Grupo 2), das quais
obteve-se 5 amostras por grupo, onde foram submetidas aos ensaios de DMA (Análise
Dinâmico-Mecânica) e DSC (Calorimetria Diferencial de Varredura). Os ensaios de DMA
foram realizados no modo de flexão em três pontos, e os parâmetros utilizados foram: taxa de
aquecimento de 5°C/min, na faixa de 30°C a 100°C, frequência de 1 Hz e amplitude de 5 μm.
Para o DSC, os parâmetros foram: taxa de aquecimento/resfriamento de 5°C/min, na faixa de
-60 °C a 120 °C, sob atmosfera dinâmica de ar e de nitrogênio (para resfriamento), com vazão
de gás da ordem de 100 ml/min-1, sob pressão atmosférica. Após a realização dos ensaios, os
dados obtidos foram tratados e analisados utilizando-se o software OriginPro 8.5®, obtendose,
a partir do DMA, gráficos com as curvas de módulo de elasticidade e capacidade de
amortecimento (tan δ) em função da temperatura e, a partir do DSC, gráficos mostrando as
temperaturas de transformação de fase cristalina da liga. Para a análise das médias dos
módulos de elasticidade das amostras, foi empregado o teste estatístico Teste-t de Student,
com nível de significância de 5%. Resultados: O Teste-t de Student demonstrou que a
diferença das médias dos módulos de elasticidade das amostras foi estatisticamente
significante (p < 0,05). A rigidez de ambos os grupos aumentou em função do aumento da
temperatura. À 37°C, temperatura normal intrabucal, o Grupo 1 evidenciou média de rigidez
superior comparado ao Grupo 2, e ambos apresentaram-se na fase austenítica. Conclusões:
Com os dados da pesquisa, pode-se concluir que mesmo as ligas com mesma característica de
superelasticidade e ,possivelmente, semelhante composição química, houve diferença entre os
módulos de elasticidade entre as marcas comerciais, sob as mesmas condições de estudo, onde
o Grupo 1 apresentou maior rigidez quando comparado ao Grupo 2, característica essa que
pode favorecer a um melhor desempenho clínico do primeiro grupo. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Saúde e Tecnologia Rural - CSTR |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Odontologia |
pt_BR |
dc.title |
Avaliação de propriedades termomecânicas de fios de níquel-titânio aplicados na ortodontia. |
pt_BR |
dc.date.issued |
2014 |
|
dc.description.abstract |
As a result of the diversity of available leagues, with his several manufacture
methods, it is important to an ortodontista to know his properties and the connected variables,
to plan the treatment and to optimize the clinical results, as well as to preserve the
histofisiologia of the periodonto of the patient. In this form, the objective of this study valued
and he compared in vitro the properties termomecânicas of threads ortodônticos superelastic
daily pay gone of nickel-titanium of two commercial marks. Methods: The commercial
marks Morelli® (Group 1) and Orthometric® (Group 2) were used, of which 5 samples were
obtained by group, where they were subjected to the tests of DMA (Dynamical Mechanical
Analysis) and DSC (Differencial Scanning Calorimetry). The tests of DMA were carried out
in the flexing way in three points, and the used parameters were: tax of heating of 5°C/min, in
the belt of 30°C to 100°C, 1 Hz frequency and amplitude of 5 μm. For the DSC, the
parameters were: tax of heating/cooling of 5°C/min, in the belt of 60 °C to 120 °C, under
dynamic atmosphere of air and of nitrogen (for cooling), with flow of gas of the order of 100
ml/min-1, under atmospheric pressure. After the realization of the tests, the obtained data
were treated and analysed when is used the software OriginPro 8.5®, when printers are
obtained, from the DMA, with the curves of module of elasticity and capacity of deadening
(tan δ) in function of the temperature and, from the DSC, printers showing the temperatures of
transformation of crystal clear phase of the league. For the analysis of the averages of the
modules of elasticity of the samples, the statistical test was employed Test-t de Student, with
level of signification of 5 %. Results: The Test-t de Student demonstrated that the difference
of the averages of the modules of elasticity of the samples was statistically significant (p <
0,05). The rigidity of both groups increased in function of the increase of the temperature. To
37°C, intrabuccal normal temperature, the Group 1 showed average of superior rigidity up
when 2 was compared to the Group, and both showed up in the austenitic phase.
Conclusions: With the data of the inquiry, it is possible to end what even the leagues with the
same characteristic of superelasticity and, possibly, similar chemical composition, existed
difference between the elasticity modules between the commercial marks, under the same
study conditions, where the Group 1 presented bigger rigidity when the Group 2, this
characteristic that it can favor to a better clinical performance of the first group was compared
to the group. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/24823 |
|
dc.date.accessioned |
2022-04-25T18:42:15Z |
|
dc.date.available |
2022-04-25 |
|
dc.date.available |
2022-04-25T18:42:15Z |
|
dc.type |
Trabalho de Conclusão de Curso |
pt_BR |
dc.subject |
Ortodontia |
pt_BR |
dc.subject |
Pesquisa em Odontologia |
pt_BR |
dc.subject |
Fios ortodônticos |
pt_BR |
dc.subject |
Módulo de elasticidade |
pt_BR |
dc.subject |
Ligas ortodônticas |
pt_BR |
dc.subject |
Propriedades termomecânicas - fios ortodônticos |
pt_BR |
dc.subject |
Orthodontics |
pt_BR |
dc.subject |
Research in Dentistry |
pt_BR |
dc.subject |
Orthodontic wires |
pt_BR |
dc.subject |
Modulus of elasticity |
pt_BR |
dc.subject |
Orthodontic alloys |
pt_BR |
dc.subject |
Thermomechanical properties - orthodontic wires |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
OLIVEIRA, Bruno Firmino de. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Evaluation of thermomechanical properties of nickel-titanium wires applied in orthodontics. |
pt_BR |
dc.identifier.citation |
OLIVEIRA, Bruno Firmino de. Avaliação de propriedades termomecânicas de fios de níquel-titânio aplicados na ortodontia. 2014. 48f. Trabalho de Conclusão de Curso (Artigo), Curso de Bacharelado em Odontologia, Centro de Saúde e Tecnologia Rural, Universidade Federal de Campina Grande - Patos - Paraíba - Brasil, 2014. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/24823 |
pt_BR |