dc.creator.ID |
PATRICIO, S. M. R. |
pt_BR |
dc.creator.Lattes |
http://lattes.cnpq.br/9872880548902941 |
pt_BR |
dc.contributor.advisor1 |
RODRIGUES, John Kennedy Guedes. |
|
dc.contributor.advisor1ID |
RODRIGUES, J. K. G. |
pt_BR |
dc.contributor.advisor1Lattes |
http://lattes.cnpq.br/7834302744515283 |
pt_BR |
dc.contributor.advisor-co1 |
MENDONÇA, Ana Maria Gonçalves Duarte. |
|
dc.contributor.advisor-co1ID |
MENDONÇA, A. M. G. D. |
pt_BR |
dc.contributor.referee1 |
PATRÍCIO, Jonny Dantas. |
|
dc.contributor.referee1ID |
PATRICIO, J. D. |
pt_BR |
dc.contributor.referee1Lattes |
http://lattes.cnpq.br/4467510175248835 |
pt_BR |
dc.contributor.referee2 |
SOUZA, Loredanna Melyssa Costa de. |
|
dc.contributor.referee2ID |
SOUZA, L. M. C. |
pt_BR |
dc.contributor.referee2Lattes |
http://lattes.cnpq.br/7849794050135972 |
pt_BR |
dc.description.resumo |
O polietileno tereftalato (PET), devido a versatilidade e baixo custo de produção, se
tornou um dos materiais plásticos mais utilizados mundialmente. Todavia, configura
um problema ambiental, em decorrência da permanência prolongada no ambiente e
da destinação inadequada, o que contribui para o acúmulo de grandes volumes na
natureza e nos aterros sanitários. Ao encontro desta questão a indústria da construção
civil possui grande potencial para incorporação de resíduos advindos de outros
sistemas produtivos. Assim, este trabalho tem por objetivo avaliar as propriedades
físicas, químicas, mineralógicas e mecânicas, e, a durabilidade de argamassas de
assentamento e revestimento, produzidas com substituição parcial do agregado miúdo
por PET triturado. Para tanto, formulou-se dois traços com proporções de
aglomerantes e agregado miúdo distintos, nos quais foram utilizados o cimento
Portland CP ll Z-32, cal, areia e PET triturado, em substituição parcial de 5%, 10%,
15%, 20% e 25%. A caracterização física foi realizada por meio de ensaios para
determinar a massa específica e unitária e a granulometria por peneiramento e a lazer
dos elementos constituintes. Para a caracterização química, empregou-se as técnicas
de espectrometria de fluorescência de raios-X, análise termogravimétrica (TGA),
térmica diferencial (DTA) e difração de raios-X (DRX). As propriedades físicas e
mecânicas foram determinadas a partir da densidade de massa e teor de ar
incorporado, no estado fresco. No estado endurecido, aferiu-se a densidade,
resistência à compressão simples (RCS), resistência à tração na flexão, absorção de
água por capilaridade e a resistência de aderência à tração (RAT). No estudo de
durabilidade utilizou-se a resistência ao ataque por sulfatos. O aumento de teor de
PET em substituição parcial ao agregado miúdo reduziu a relação água/aglomerante
em até 15%. Com isso, há ganhos na trabalhabilidade das argamassas em
decorrência da maior disponibilidade de água livre. Constatou-se que o aumento de
teor de PET reduziu a relação água/aglomerante em até 15%. Houve ganhos na
trabalhabilidade das argamassas, dada a maior disponibilidade de água livre. No
estado fresco, a densidade de massa reduz linearmente, a medida em que se aumenta
o percentual de PET, com diferenças de até 11,48%. O teor de ar incorporado sofre
elevações, contudo, tende a decrescer quando o percentual de substituição parcial
ultrapassa 15%. No estado em endurecido, também ocorre a diminuição de densidade
em função do aumento do teor de PET, chegando a 15,81%. Quanto à RCS e a
resistência à tração na flexão, para o traço 1:2:9, houve um aumento tanto com a
incorporação de PET quanto com a idade de cura, para as argamassas com teores de
10%, 15%, 20% e 25% de PET, a partir dos 14 dias. Para o traço 1:1:6, aos 28 dias
cura, percebe-se que a argamassa sem adição de PET demonstrou melhor
desempenho para esses parâmetros mecânicos. Todavia, aos 56 dias de cura, todas
as argamassas com aditivo de PET mostraram maior resistência. A inserção de
PET reduziu a absorção de água por capilaridade, contudo, ocorreu a redução da
RAT. Em relação ao ataque por sulfatos, são consideradas reativas, em virtude de
sofrerem expansões dimensionais quando imersos em solução de sulfato de sódio. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Ciências e Tecnologia - CCT |
pt_BR |
dc.publisher.program |
PÓS-GRADUAÇÃO EM ENGENHARIA DE PROCESSOS |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Materiais e Componentes de Construção |
pt_BR |
dc.title |
Incorporação de PET triturado em substituição parcial ao agregado miúdo para utilização em argamassas. |
pt_BR |
dc.date.issued |
2021-12-27 |
|
dc.description.abstract |
Polyethylene terephthalate (PET), due to its versatility and low production cost, has
become one of the most widely used plastic materials worldwide. However, it is an
environmental problem, due to the prolonged stay in the environment and inadequate
disposal, which contributes to the accumulation of large volumes in nature and in
landfills. In response to this issue, the civil construction industry has great potential for
incorporating waste from other production systems. Thus, this work aims to evaluate
the physical, chemical, mineralogical and mechanical properties, and the durability of
laying and coating mortars, produced with partial replacement of fine aggregate by
crushed PET. For this purpose, two mixes were formulated with different proportions
of binders and fine aggregate, in which Portland cement CP ll Z-32, lime, sand and
crushed PET were used, in partial replacement of 5%, 10%, 15%, 20% and 25%. The
physical characterization was carried out through tests to determine the specific and
unitary mass and the sieving and leisure granulometry of the constituent elements. For
the chemical characterization, the techniques of X-ray fluorescence spectrometry,
thermogravimetric analysis (TGA), differential thermal (DTA) and X-ray diffraction
(XRD) were used. The physical and mechanical properties were determined from the
mass density and incorporated air content, in the fresh state. In the hardened state,
density, simple compressive strength (SCS), flexural tensile strength, capillary water
absorption and tensile bond strength (TBS) were measured. In the durability study, the
resistance to attack by sulfates was used. The increase in PET content in partial
replacement of fine aggregate reduced the water/binder ratio by up to 15%. As a result,
there are gains in the workability of mortars as a result of the greater availability of free
water. It was found that the increase in PET content reduced the water/binder ratio by
up to 15%. There were gains in the workability of the mortars, given the greater
availability of free water. In the fresh state, the mass density decreases linearly as the
percentage of PET increases, with differences of up to 11.48%. The content of
incorporated air increases, however, it tends to decrease when the percentage of
partial replacement exceeds 15%. In the hardened state, there is also a decrease in
density due to the increase in the PET content, reaching 15.81%. As for the SCS and
the flexural tensile strength, for the 1:2:9 mix, there was an increase both with the
incorporation of PET and with the curing age, for the mortars with contents of 10%,
15%, 20% and 25% PET, after 14 days. For the 1:1:6 mix, after 28 days of cure, it is
noticed that the mortar without the addition of PET showed better performance for
these mechanical parameters. However, at 56 days of cure, all mortars with PET
additive showed greater strength. The insertion of PET reduced capillary water
absorption, however, there was a reduction in the TBS. Regarding the attack by
sulfates, they are considered reactive, as they undergo dimensional expansion when
immersed in sodium sulfate solution. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/25580 |
|
dc.date.accessioned |
2022-06-09T12:07:29Z |
|
dc.date.available |
2022-06-09 |
|
dc.date.available |
2022-06-09T12:07:29Z |
|
dc.type |
Tese |
pt_BR |
dc.subject |
Argamassas - PET triturado |
pt_BR |
dc.subject |
PET triturado -materiais alternativos |
pt_BR |
dc.subject |
Comportamento mecânico |
pt_BR |
dc.subject |
Polietileno tereftalano ( PET) |
pt_BR |
dc.subject |
Durabilidade |
pt_BR |
dc.subject |
Mortars - crushed PET |
pt_BR |
dc.subject |
Mechanical behavior |
pt_BR |
dc.subject |
Durability |
pt_BR |
dc.subject |
Crushed PET - alternative materials |
pt_BR |
dc.subject |
Polyethylene terephthalane (PET) |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
PATRICIO, Solange Maria da Rocha. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Incorporation of crushed PET as a partial replacement for fine aggregate for use in mortars. |
pt_BR |
dc.identifier.citation |
PATRÍCIO, Solange Maria da Rocha. Incorporação de PET triturado em substituição parcial ao agregado miúdo para utilização em argamassas. 2021. 137 f. Tese (Doutorado em Engenharia de Processos) – Programa de Pós - graduação em Engenharia de Processos, Centro de Ciências e Tecnologia, Campina Grande, Paraíba, Brasil, 2021. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/25580 |
pt_BR |