dc.description.resumo |
O objetivo do presente estudo foi comparar o processo de regeneração óssea em coelhos
através da utilização do cimento ósseo á base de fosfato de cálcio isolado e associado à
membrana de colágeno. Essa dissertação foi dividida em dois capítulos: o primeiro, uma
avaliação clínica e termográfica do processo inflamatório nos membros onde se realizou a
ostectomia, e o segundo, uma comparação da regeneração óssea através da análise
radiográfica, por microscopia de luz (ML) e Microscopia Eletrônica de Varredura (MEV).
Foram utilizados 12 coelhos adultos, de ambos os sexos e pesando em média 2,49± 0,29 kg
(média ± desvio padrão). Os animais foram distribuídos aleatoriamente em dois grupos
experimentais, grupo cimento ósseo (GCO) e grupo cimento ósseo acrescido da membrana de
colágeno (GCOM). Os biomateriais foram introduzidos em defeitos criados cirurgicamente na
diáfise proximal e distal de cada tíbia, de modo que o cimento ósseo foi introduzido no
membro direito e no membro esquerdo, além do cimento ósseo foi adicionada a membrana de
colágeno. Logo após o procedimento cirúrgico e aos e 30 e 60 dias de pós- operatório foram
realizadas radiografias nas projeções crânio-caudal e médio-lateral. No capítulo I, foram
avaliadas a temperatura retal (TR) e temperatura superficial (TS) da região das ostectomias
nos momentos D0(antes do procedimento cirúrgico) e do D1 ao D7 e D14 de pós-operatório.
A TR se manteve dentro dos valores de referência para a espécie. Com relação a TS não se
observou diferença estatística entre os grupos.Essa diferença foi constatada em ambos os
grupos com relação à localização dos implantes e em relação ao momento D14. Observou-se
em ambos os grupos reação inflamatória na maioria dos animais a partir do D8 e que no
GCOM essa inflamação foi mais acentuada. Conclui-se que avaliação clínica e termográfica
foram ferramentas auxiliares para análise do processo inflamatório nos membros onde se
realizou a ostectomia. No capítulo II esses animais foram subdivididos ao acaso em dois
momentos experimentais, sendo 06 animais eutanasiados aos 30 dias após a cirurgia, e 06 aos
60 dias. Tanto na radiografia e ML quanto na MEV na avaliação descritiva e comparativa, não
se observou diferença com relação à regeneração óssea entre os grupos, o que se verificou foi
que aos 60 dias de pós-operatório a reparação óssea foi mais acentuada e intensificou a
neoformação óssea se comparada aos 30 dias. Segundo os resultados obtidos, todas as
amostras foram gradativamente absorvidas durante os períodos avaliados, sendo substituídas
por tecido ósseo neoformado, no entanto a atividade osteopromotora da membrana de
colágeno não foi evidenciada. |
pt_BR |
dc.publisher.country |
Brasil |
pt_BR |
dc.publisher.department |
Centro de Saúde e Tecnologia Rural - CSTR |
pt_BR |
dc.publisher.program |
PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA E SAÚDE ANIMAL |
pt_BR |
dc.publisher.initials |
UFCG |
pt_BR |
dc.subject.cnpq |
Medicina Veterinária |
pt_BR |
dc.title |
Avaliação da interação biológica de substituto ósseo à base de fosfato de cálcio em falhas ósseas induzidas em tíbias de coelhos. |
pt_BR |
dc.date.issued |
2018-02-28 |
|
dc.description.abstract |
The objective of the present study was to compare the bone regeneration process in rabbits
through the use of calcium phosphate based bone cement isolated and associated with the
collagen membrane. This dissertation was divided into two chapters: the first, a clinical and
thermographic evaluation of the inflammatory process in the limbs where the ostectomy was
performed, and the second, a comparison of the bone regeneration through the radiographic
analysis, by light microscopy (LM) and Microscopy Scanning Electronics (SEM). Twelve
adult rabbits of both sexes and weighing on average 2.49 ± 0.29 kg (mean ± standard
deviation) were used. The animals were randomly assigned to two experimental groups, bone
cement group (GCO) and bone cement group plus collagen membrane (GCOM). The
biomaterials were introduced into surgically created defects in the proximal and distal
diaphysis of each tibia, so that the bone cement was introduced into the right limb and left
limb, in addition to the bone cement was added to the collagen membrane. Shortly after the
surgical procedure and at the 30 and 60 postoperative days, radiographs were performed in the
cranio-caudal and mid-lateral projections. In section I, the rectal temperature (TR) and
superficial temperature (TS) of the ostectomy region at the D0 moments (before the surgical
procedure) and from the D1 to the D7 and postoperative D14 were evaluated. The TR
remained within the reference values for the species. Regarding TS, no statistical difference
was observed between the groups. This difference was observed in both groups in relation to
the location of the implants and in relation to the D14 moment. It was observed in both groups
inflammatory reaction in the majority of the animals from the D8 and that in the GCOM this
inflammation was more accentuated. It was concluded that clinical and thermographic
evaluation were auxiliary tools to analyze the inflammatory process in the limbs where the
ostectomy was performed. In Chapter II, these animals were randomly subdivided into two
experimental moments, with six animals euthanized at 30 days after surgery, and 06 at 60
days. In both radiography and ML and in the SEM in the descriptive and comparative
evaluation, no difference was observed in relation to the bone regeneration between the
groups, which was verified that at 60 postoperative days the bone repair was more
accentuated and intensified the neoformation compared to 30 days. According to the results
obtained, all the samples were gradually absorbed during the evaluated periods, being
replaced by neoformed bone tissue, however the osteopromotor activity of the collagen
membrane was not evidenced. |
pt_BR |
dc.identifier.uri |
http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/25630 |
|
dc.date.accessioned |
2022-06-10T16:53:24Z |
|
dc.date.available |
2022-06-10 |
|
dc.date.available |
2022-06-10T16:53:24Z |
|
dc.type |
Dissertação |
pt_BR |
dc.subject |
Ortopedia Veterinária |
pt_BR |
dc.subject |
Biomateriais |
pt_BR |
dc.subject |
Falhas ósseas |
pt_BR |
dc.subject |
Fosfato de cálcio - falhas ósseas |
pt_BR |
dc.subject |
Falhas ósseas induzidas - coelhos |
pt_BR |
dc.subject |
Substituto ósseo - interação biológica |
pt_BR |
dc.subject |
Regeneração óssea |
pt_BR |
dc.subject |
Termografia |
pt_BR |
dc.subject |
Veterinary Orthopedics |
pt_BR |
dc.subject |
Biomaterials |
pt_BR |
dc.subject |
Bone defects |
pt_BR |
dc.subject |
Calcium Phosphate - Bone Failures |
pt_BR |
dc.subject |
Induced bone defects - rabbits |
pt_BR |
dc.subject |
Bone substitute - biological interaction |
pt_BR |
dc.subject |
Bone regeneration |
pt_BR |
dc.subject |
Bone regeneration |
pt_BR |
dc.rights |
Acesso Aberto |
pt_BR |
dc.creator |
SOUZA, Mônica Adriana de. |
|
dc.publisher |
Universidade Federal de Campina Grande |
pt_BR |
dc.language |
por |
pt_BR |
dc.title.alternative |
Evaluation of the biological interaction of calcium phosphate-based bone substitute on bone defects induced in rabbit tibiae. |
pt_BR |
dc.identifier.citation |
SOUZA, Mônica Adriana Araújo de. Avaliação da interação biológica de substituto ósseo à base de fosfato de cálcio em falhas ósseas induzidas em tíbias de coelhos. 2018. 49f. (Dissertação de Mestrado), Programa de Pós-graduação em Medicina Veterinária, Centro de Saúde e Tecnologia Rural, Universidade Federal de Campina Grande - Patos - Paraíba - Brasil, 2018. Disponível em: http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/25630 |
pt_BR |